Polymer Property : Tensile Strength, Yield = 22600 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Yield 156 MPa
22600 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics EXTEM XH2315 TPI Resin
Extem XH2315 Resin
Tensile Strength, Yield 156 MPa
22600 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics EXTEM XH2315 TPI Resin (Asia Pacific)
Extem XH2315 Resin
Tensile Strength, Yield 156 MPa
22600 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics EXTEM XH2315 TPI Resin (Europe-Africa-Middle East)
Extem XH2315 Resin
Tensile Strength, Yield 156 MPa
22600 psi
ISO 527-2/1A/5
Solvay Specialty Polymers AvaSpire® AV-742 SL30 Polyaryletherketone (PAEK)  (Unverified Data**)
AV-742 SL30 is a wear resistant grade of AvaSpire polyaryletherketone (PAEK) designed to provide low wear rates in both non-lubricated and lubricated environments. In addition to outstanding wear re..
Tensile Strength, Yield 156 MPa
22600 psi
ISO 527
GEHR Plastics PEEK-30GF Polyetheretherketone, 30% Glass Fiber
Polyether etherketone can be used at very high temperatures and it shows a good mechanical strength, toughness, hardness, flexural strength, and torsional strength. PEEK exhibits excellent chemical ..
Tensile Strength, Yield 156 MPa
22600 psi
5 mm/min, Type 1A; ISO 527-2
Solvay Specialty Polymers AvaSpire® AV-742 SL30 Polyaryletherketone (PAEK)
AV-742 SL30 is a wear resistant grade of AvaSpire® polyaryletherketone (PAEK) designed to provide low wear rates in both non-lubricated and lubricated environments. In addition to outstanding wea..
Tensile Strength, Yield 156 MPa
22600 psi
ASTM D638
Techmer ES Luriblend® PA6/6 GF30 TS1 BK 30% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 30% Filler by WeightAdditive: Heat Stabilizer, Silicone Lubricant and PTFE Lubricant(15%)Features: Lubricated, Good Wear R..
Tensile Strength, Yield 156 MPa
22600 psi
ASTM D638
Techmer ES Luriblend® PA6/6 GF30 TS15 30% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 30% Filler by WeightAdditive: Heat Stabilizer, Silicone Lubricant and PTFE Lubricant(15%)Features: Lubricated, Good Wear R..
Tensile Strength, Yield 156 MPa
22600 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP EFB26ER PEI (Europe-Africa-Middle East)
LNP* THERMOCOMP* EFB26ER is a compound based on Polyetherimide containing Glass Fiber, Glass Bead. Added features include: Easy Molding, Mold Release.
Tensile Strength, Yield 156 MPa
22600 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP LF005 PEEK
LNP* THERMOCOMP* LF005 is a compound based on Polyetheretherketone resin containing 25% Glass Fiber.
Tensile Strength, Yield 156 MPa
22600 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP LF005 PEEK (Asia Pacific)
LNP* Thermocomp* LF005 is a compound based on Polyetheretherketone resin containing Glass Fiber.
Tensile Strength, Yield 156 MPa
22600 psi
ISO 527
SABIC Innovative Plastics LNP THERMOCOMP LF008 PEEK
LNP* THERMOCOMP* LF008 is a compound based on Polyetheretherketone resin containing 40% Glass Fiber.
Tensile Strength, Yield 156 MPa
22600 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP QF007 PA 6/10
LNP* THERMOCOMP* QF007 is a compound based on Nylon 6/10 resin containing 35% Glass Fiber.
Tensile Strength, Yield 156 MPa
22600 psi
ISO 527
SABIC Innovative Plastics LNP THERMOCOMP LF008 PEEK (Asia Pacific)
LNP* Thermocomp* LF008 is a compound based on Polyetheretherketone resin containing Glass Fiber.
Tensile Strength, Yield 156 MPa
22600 psi
ISO 527
Eurostar Star L PA6 30V D51 PA6, Glass Filled, Injection Molding
Star L PA6 30V D51 is a PTFE Lubricated, Glass Fiber Reinforced, Polyamide 6 Injection Molding ResinInformation provided by Eurostar.
Tensile Strength, Yield 156 MPa
22600 psi
ISO 527
SABIC Innovative Plastics LNP VERTON NV008E PC/ABS (Asia Pacific)
LNP* Verton* NV008E is a compound based on PC/ABS resin containing Long Glass Fiber. Added features of this material include: Easy Molding.
Tensile Strength, Yield 156 MPa
22600 psi
ISO 527
SABIC Innovative Plastics LNP VERTON NV008E PC+ABS
LNP* VERTON* NV008E is a compound based on PC+ABS resin containing 40% Long Glass Fiber. Added features of this material include: Easy Molding. Structural.