Polymer Property : Tensile Strength, Yield = 2250 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	15.5 MPa	2250 psi	Type IV, 510 mm/min; ASTM D638
PolyOne Geon™ Vinyl Wire & Cable JC435XC Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne
Tensile Strength, Yield	15.5 MPa	2250 psi	Type IV, 510 mm/min; ASTM D638
PolyOne Geon™ Vinyl Wire & Cable WR7400L Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne
Tensile Strength, Yield	15.5 MPa	2250 psi	at 100%; ASTM D412
Multibase Multi-FlexÂ® D 6606 TPE Thermoplastic Elastomer Features: Chemical Resistance, Good Colorability, GoodElasticity, HighElectrically InsulatingFlame RetardantFlexibility, GoodHeat StabilizedOzone ResistantProcessability, GoodUV Resistance, Good R..
Tensile Strength, Yield	15.5 MPa	2250 psi	ASTM D412-97
Saint-Gobain TygonÂ® R-3400 UV Resistant Tubing Formulation TygonÂ® R-3400: Ideal for virtually any permanent or temporary chemical transfer application, TygonÂ® UV Resistant Tubing combines suppleness and flexibility with resistance to a wide range of..
Tensile Strength, Yield	15.5 MPa	2250 psi	ASTM D412
Teknor Apex APEXÂ® 3302-70 Polyvinyl Chloride, Flexible Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTM Uses- Medical Applications, Tubing, Appearance-ClearForms-PelletsProcessing-ExtrusionInformation provided by..
Tensile Strength, Yield	15.5 MPa	2250 psi	ASTM D412
Teknor Apex APEXÂ® 90-A472R-80-NT Polyvinyl Chloride, Flexible Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTMUses-Medical Applications, Caps, Closures, Valves/Valve Parts Appearance-ClearForms-PelletsProcessing Method-..
Tensile Strength, Yield	15.5 MPa	2250 psi	ASTM D-882
Saint-Gobain NortonÂ® PFA Fluoropolymer Film Features/Benefits:Outstanding flex life and stress crack resistancePerformance from -254Â°C (-425Â°F) to 260Â°C (500Â°F)Outstanding anti-stick release propertiesExcellent electrical properti..
Tensile Strength, Yield	15.5 MPa	2250 psi	9.8 in/min; ASTM D638
Teknor Apex Sinvicomp SSG 7006 Polyvinyl Chloride, Flexible Availability: Asia Pacific Features: Good Flexibility Uses: Cable Jacketing; Wire and Cable Applications Wire Types: ST4; ST5; Type 6; YM1; YM2; TM2 Agency Ratings: BS 6746; IEC 60227; VDE 0207 For..
Tensile Strength, Yield	15.5 MPa	2250 psi	2"/min; ASTM D638
A. Schulman POLYAXIS® CP812 Stabilized Compounded Rotational Molding Resin DescriptionPolyaxis CP 812 is a stabilized compounded rotational molding resin with a combination of good flow and stiffness. NOTE: Physical properties are based on rotationally molded samples from ..
Tensile Strength, Yield	15.5 MPa	2250 psi	2"/min; ASTM D638
A. Schulman POLYAXIS® CP812 Stabilized Compounded Rotational Molding Resin DescriptionPolyaxis CP 812 is a stabilized compounded rotational molding resin with a combination of good flow and stiffness. NOTE: Physical properties are based on rotationally molded samples from ..
Tensile Strength, Yield	15.5 MPa	2250 psi	2"/min; ASTM D638
A. Schulman POLYAXIS® CP812 Stabilized Compounded Rotational Molding Resin DescriptionPolyaxis CP 812 is a stabilized compounded rotational molding resin with a combination of good flow and stiffness. NOTE: Physical properties are based on rotationally molded samples from ..
Tensile Strength, Yield	15.5 MPa	2250 psi	ASTM D638
Washington Penn Medium Impact Copolymer 50% Calcium Carbonate Filled Calcium carbonate-filled polypropylene compounds have been tailored specifically to meet the requirements of each of the major automobile producers. Grades are available to meet FDA food and drug pa..
Tensile Strength, Yield	15.5 MPa	2250 psi	37% Ret.
UBE UBESTA® 3030U Nylon 12 (After Chloroform for 1000 hours) Description: UBESTA has a strong resistance to chemicals. Under normal conditions, it is not significantly affected by alkalis, alcohols, ethers, ketones, hydrocarbons, lubricating oils, gasoline, c..
Tensile Strength, Yield	15.5 MPa	2250 psi	2"/min; ASTM D638
A. Schulman POLYAXIS® CP812 Stabilized Compounded Rotational Molding Resin DescriptionPolyaxis CP 812 is a stabilized compounded rotational molding resin with a combination of good flow and stiffness. NOTE: Physical properties are based on rotationally molded samples from ..
Tensile Strength, Yield	15.5 MPa	2250 psi
Trelleborg R798 Commercial Natural Rubber Polyisoprene All information provided by Trelleborg
Tensile Strength, Yield	15.5 MPa	2250 psi	2"/min; ASTM D638
A. Schulman POLYAXIS® CP812 Stabilized Compounded Rotational Molding Resin DescriptionPolyaxis CP 812 is a stabilized compounded rotational molding resin with a combination of good flow and stiffness. NOTE: Physical properties are based on rotationally molded samples from ..
Tensile Strength, Yield	15.5 MPa	2250 psi	2"/min; ASTM D638
A. Schulman POLYAXIS® CP812 Stabilized Compounded Rotational Molding Resin DescriptionPolyaxis CP 812 is a stabilized compounded rotational molding resin with a combination of good flow and stiffness. NOTE: Physical properties are based on rotationally molded samples from ..
Tensile Strength, Yield	15.5 MPa	2250 psi	ASTM D412
ACC EP RSP-AL EPI Engineered Polymers Aromatic Silicone Polyurea EP RSP-AL, Aromatic Silicone Polyurea, “Powered by Reactamine® Technology”, is a two component 100% solid Polyurea. This increases UV resistance without sacrificing physical properties. EP RSP-AL..
Tensile Strength, Yield	15.5 MPa	2250 psi	ASTM D-638
Axiall 10805 Wire & Cable Flexible PVC Non-lead stabilized, 75°C rated compound recommended for integral insulation/jacket constructions.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013.
Tensile Strength, Yield	15.5 MPa	2250 psi	ASTM D-638
Axiall 12802 Wire & Cable Flexible PVC Non-lead stabilized general purpose jacket recommended for 75C applications.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013.
Tensile Strength, Yield	15.5 MPa	2250 psi	ASTM D-638
Axiall 1651 Clear 7002 Flexible PVC Flexible polyvinyl chloride compound formulated for USP Class VI applications. The compound possesses exceptional clarity.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation ..
Tensile Strength, Yield	15.5 MPa	2250 psi	ASTM D-638
Axiall 16782 Wire & Cable Flexible PVC Non-lead stabilized, 90C jacketing compound with excellent low temperature performance.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013.
Tensile Strength, Yield	15.5 MPa	2250 psi	ASTM D-638
Axiall 6690 Moldings & Extrusions Flexible PVC General purpose, elastomeric vinyl compound well suited for co-extrusion with rigid PVC.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013.
Tensile Strength, Yield	15.5 MPa	2250 psi	ASTM D-638
Axiall 873 Wire & Cable Flexible PVC 80°C rated, low migratory, oil resistant coil cord jacket.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013.
Tensile Strength, Yield	15.5 MPa	2250 psi	ASTM D412
ACC EP RSP EPI Engineered Polymers Silicone Polyurea EP RSP Silicone Polyurea, “Powered by Reactamine®Technology”, is a two component 100% solid Polyurea with superior performance in industrial applications. EP RSP displays extremely fast cure time..
Tensile Strength, Yield	15.5 MPa	2250 psi	ASTM D-638
Axiall 18750 Wire & Cable Flexible PVC Jacketing compound with excellent low temperature performance. Maximum 105°C service temperature at 40+ mil thickness.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in ..
Tensile Strength, Yield	15.5 MPa	2250 psi	ASTM D-638
Axiall 2192 Wire & Cable Flexible PVC Non-lead stabilized SJTO, SJTOO oil resistant flexible cord jacket. UL recognized for 720 hour sunlight resistance in all colors.Information provided by Georgia GulfGeorgia Gulf became Axiall Corpo..
Tensile Strength, Yield	15.5 MPa	2250 psi	ASTM D-638
Axiall 19801 Wire & Cable Flexible PVC Primary insulation and jacketing compound recommended for 105°C applications at a minimum wall of 15 mils. CSA approved AWM, SVT, SJT, ST, SVTO, SVTOO, SJTO, SJTOO, STO, STOO constructions. 60°C..
Tensile Strength, Yield	15.5 MPa	2250 psi	ASTM D-638
Axiall 38602 Coax & Telecom Flexible PVC CATV and general purpose jacket with excellent low temperature properties. UL recognized for 720 hour sunlight resistance in all colors.Information provided by Georgia GulfGeorgia Gulf became Axial..