Polymer Property : Tensile Strength, Yield = 20200 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Yield 139 MPa
20200 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM 2210F PEI
20% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming. US FDA Food Contact compliant in recognized colors.
Tensile Strength, Yield 139 MPa
20200 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM 2210K PEI
20% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming.
Tensile Strength, Yield 139 MPa
20200 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM 2210K PEI (Asia Pacific)
20% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming.
Tensile Strength, Yield 139 MPa
20200 psi
Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics Ultem 2210K PEI (Europe-Africa-Middle East)
20% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Tensile Strength, Yield 139 MPa
20200 psi
Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics Ultem ATX202R PEI+PCE
20% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Americas region.
Tensile Strength, Yield 139 MPa
20200 psi
Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics Ultem ATX202R PEI+PCE (Asia Pacific)
20% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Asia Pacific region.
Tensile Strength, Yield 139 MPa
20200 psi
Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics Ultem ATX202R PEI+PCE (Europe-Africa-Middle East)
20% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Europe-Africa-Middle East regio..
Tensile Strength, Yield 139 MPa
20200 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM HU2210 PEI
20% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP ..
Tensile Strength, Yield 139 MPa
20200 psi
5 mm/min; ISO 527
SABIC Innovative Plastics Valox® IQ420 PBT
Environmentally responsible Valox iQ420 resin: iQ-PBT+ 30% glass fiber reinforcement. Targeted for use in electrical motors, connectors, pump housings, spotlights, appliance handles, etc.
Tensile Strength, Yield 139 MPa
20200 psi
5 mm/min; ISO 527
SABIC Innovative Plastics Valox® IQ420 PBT (Asia Pacific)
Environmentally responsible Valox iQ420 resin: iQ-PBT+ 30% glass fiber reinforcement. Targeted for use in electrical motors, connectors, pump housings, spotlights, appliance handles, etc.
Tensile Strength, Yield 139 MPa
20200 psi
5 mm/min; ISO 527
SABIC Innovative Plastics Valox® IQ420 PBT (Europe-Africa-Middle East)
Environmentally responsible Valox iQ420 resin: iQ-PBT+ 30% glass fiber reinforcement. Targeted for use in electrical motors, connectors, pump housings, spotlights, appliance handles, etc.
Tensile Strength, Yield 139 MPa
20200 psi
5 mm/min; ISO 527
SABIC Innovative Plastics Valox® IQ420HP PBT (Asia Pacific)
Environmentally responsible, low carbon footprint Valox iQ* resin - Valox* iQ420HP resin is made using iQ-PBT resin and 30% glass fiber reinforcement. Valox* iQ420HP may be used for the production..
Tensile Strength, Yield 139 MPa
20200 psi
ASTM D638
Techmer ES HiFill® PA6/6 GF20 HS L 20% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 20% Filler by WeightAdditive: Heat Stabilizer and LubricantFeatures: Lubricated and Heat StabilizedInformati..
Tensile Strength, Yield 139 MPa
20200 psi
ASTM D638
Techmer ES HiFill® PA6/6 GF20 L 20% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 20% Filler by WeightAdditive: LubricantFeatures: LubricatedInformation provided by TP Composites, Inc.
Tensile Strength, Yield 139 MPa
20200 psi
5 mm/min; ISO 527
SABIC Innovative Plastics Valox® IQ420HP PBT
Environmentally responsible, low carbon footprint Valox iQ* resin - Valox* iQ420HP resin is made using iQ-PBT resin and 30% glass fiber reinforcement. Valox* iQ420HP may be used for the production..
Tensile Strength, Yield 139 MPa
20200 psi
5 mm/min; ISO 527
SABIC Innovative Plastics Valox® IQ420HP PBT (Europe-Africa-Middle East)
Environmentally responsible, low carbon footprint Valox iQ* resin - Valox* iQ420HP resin is made using iQ-PBT resin and 30% glass fiber reinforcement. Valox* iQ420HP may be used for the production..
Tensile Strength, Yield 139 MPa
20200 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP RF006EUC PA 66
LNP* THERMOCOMP* RF006EUC is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added features of this material include Easy Molding, UV Stabilized.