Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 2.10 MPa | 304 psi | at 200%, post cured- 2 hours at 177°C; ASTM D412 |
Multibase C6-135 Dow-Corning Class VI Elastomer Information provided by Multibase |
|||
Tensile Strength, Yield | 2.10 MPa | 304 psi | AVG Stress at Elongation M50; ASTM D412 Method A |
Seals Eastern 5433 Nitrile Rubber General purpose Nitrile; Low water swellInformation provided by Seals Eastern, Inc. |
|||
Tensile Strength, Yield | >= 2.10 MPa | >= 305 psi | Stress at Elongation M100; ASTM D412 Method A |
Seals Eastern 4503 Natural Rubber General purpose Natural RubberInformation provided by Seals Eastern, Inc. |
|||
Tensile Strength, Yield | 2.10 MPa | 305 psi | 508 mm/min; ASTM D638 |
Dow Engage® 8100 Polyolefin Elastomer Description: Engage® 8100 polyolefin elastomer is an ethyleneoctene copolymer that has excellent flow characteristics and performs well in a wide range of general purpose thermoplastic elastomer ap.. |
|||
Tensile Strength, Yield | 2.10 MPa | 305 psi | 508 mm/min; ASTM D638 |
Dow Engage® 8107 Polyolefin Elastomer Description: Engage® 8107 polyolefin elastomer is a loose talc surface coated ethylene-octene copolymer. The talc is untreated and has a nominal 1µm particle size. This product offers the exceptio.. |
|||
Tensile Strength, Yield | 2.10 MPa | 305 psi | 508 mm/min; ASTM D638 |
Dow Engage® 8200 Polyolefin Elastomer Description: Engage® 8200 and Engage® 8207 polyolefin elastomers are ethylene-octene copolymers that have excellent flow characteristics and performs well in a wide range of general purpose thermo.. |
|||
Tensile Strength, Yield | 2.10 MPa | 305 psi | 508 mm/min; ASTM D638 |
Dow Engage® 8207 Polyolefin Elastomer Description: Engage® 8207 polyolefin elastomer is a loose talc surface coated ethylene-octene copolymer. The talc is untreated and has a nominal 1µm particle size. This product offers the exceptio.. |