Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 13.5 MPa | 1960 psi | -10% change after 70 hours @ 100°C; ASTM D412 |
Precision Polymer Engineering N90B Nitrile Rubber General purpose, Nitrile Rubber, 85-95 °IRHD. Copolymer of acrylonitrile and butadiene. ASTM & ISO designation = NBR. ASTM D2000 line call-out: M4CH910, A25, B14, EF31, EO15, EO35, F16.Applications.. |
|||
Tensile Strength, Yield | 13.5 MPa | 1960 psi | -25% change after 70 hours @ 100°C; ASTM D412 |
Precision Polymer Engineering Q50Y Polyurethane Rubber Yellow/Green Polyurethane Rubber, 50-60 °IRHD. ASTM & ISO designation = AU.Applications: Good abrasion resistance and tensile strength, with fluid compatibility approaching that of NBR. Polyuretha.. |
|||
Tensile Strength, Yield | 13.5 MPa | 1960 psi | -10% change after 72 hours @ 250°C; ASTM D412 |
Precision Polymer Engineering V97B Fluoroelastomer Compound Fluoroelastomer Rubber, 90-98 °IRHD. Terpolymer of vinylidene fluoride, hexafluoropropylene and tetrafluoroethylene. To meet ASTM D2000 line call-out M3HK914, A1-10, B37, B38, EF31, EO78, Z1. Wher.. |
|||
Tensile Strength, Yield | 13.5 MPa | 1960 psi | ASTM D412 |
Teknor Apex ELEXAR® EL 8712 Thermoplastic Elastomer Information provided by Teknor Apex Company |
|||
Tensile Strength, Yield | 13.5 MPa | 1960 psi | |
Trelleborg R940 Natural Rubber Polyisoprene All information provided by Trelleborg |
|||
Tensile Strength, Yield | 13.5 MPa | 1960 psi | after aging 1 week @ 135°C; ASTM D638 |
Trelleborg Horda Cable E8560 Strippable Semiconductive Shielding E8560 is a vulcanizing, strippable semiconductive compound, designed for both XLPE and EPDM rubber insulated cables and use in both dry and steam curing processes.E8560 meets the requirements as bel.. |
|||
Tensile Strength, Yield | >= 13.5 MPa | >= 1960 psi | |
Trelleborg Offshore Vikotherm™ 73780 Insulative Elastomer Vikotherm™ is a rubber elastomer chemically modified to provide very high insulating characteristics while maintaining its inherent rubber properties in respect of seawater resistance, pressure res.. |
|||
Tensile Strength, Yield | 13.5 MPa @Strain 300 % |
1960 psi @Strain 300 % |
ASTM D412 |
Dow Buna® SB 1739 Cold polymerized Emulsion Styrene Butadiene Rubber (E-SBR) Buna® SB 1739 - Schkopau is manufactured by cold polymerization using mixed rosin acid / fatty acid soaps. It is plasticized with 37.5 parts of a TDAE oil in relation to solid rubber. A discolori.. |
|||
Tensile Strength, Yield | 13.5 MPa | 1960 psi | ASTM D638 |
Huntsman PE2065 Injection Molding Polyethylene
(discontinued **) Homopolymer and FDA compliant.Features: General purpose injection molding resin with good flow characteristicsApplications: Injection molding: lids.FDA Notes: Conforms to FDA regulation 21 CFR 177.1.. |
|||
Tensile Strength, Yield | 13.5 MPa | 1960 psi | ASTM D638 |
Petroquimica Triunfo Trithene® SX 9003 MDPE - Blow Molding The Trithene® SX 9003 resin is a medium density polyethylene (MDPE) with high molecular weight that presents excellent mechanical properties, thermal stability and high stiffness when compared with.. |
|||
Tensile Strength, Yield | 13.5 MPa | 1960 psi | |
Kraton® D1102 + PP blend (50/50) Unmodified polypropylene has high rigidity and good heat resistance, but poor impact resistance, especially at low temperatures. Blending KRATON D and G polymers with PP significantly improves the .. |