Polymer Property : Tensile Strength, Yield = 195 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	>= 195 MPa	>= 28300 psi
MetalTek AGMA CL A UNS C90800 Gear Bronze Copper-tin alloy with high tensile, yield and compressive strength as well as wear resistance.Applications: Worm gears, steel mill nutsInformation provided by MetalTekCast UNS C90800; Cast Grade C90..
Tensile Strength, Yield	>= 195 MPa	>= 28300 psi
MetalTek AGMA CL B UNS C91700 Gear Bronze Copper-tin alloy with high tensile, yield and compressive strength as well as wear resistance.Applications: Worm gears, steel mill nutsInformation provided by MetalTekCast UNS C91700; Cast Grade C91..
Tensile Strength, Yield	>= 195 MPa	>= 28300 psi
MetalTek MTEK 150 Cast UNS C95220 Aluminum Bronze Versatile alloy with high strength, good ductility, unusual toughness, plus exceptional wear resistance. Aluminum Bronze heat treated to higher mechanical properties where necessary.Information prov..
Tensile Strength, Yield	>= 195 MPa	>= 28300 psi
MetalTek MTEK CY-40 Cast UNS N06040 Severe Corrosion and Heat Resistant Alloy Good strength and toughness from cryogenic to elevated temperatures.Applications: Nuclear flow control, chemical process flanges and fittings.Information provided by MetalTek
Tensile Strength, Yield	195 MPa	28300 psi	d.a.m.; ISO 527-1, -2; 50 mm/min
Lanxess DurethanÂ® BKV 40 H2.0 901510 Nylon 6, Glass Fiber Reinforced PA 6, 40% glass fibers, injection molding, heat-aging stabilizedInformation provided by LANXESS.
Tensile Strength, Yield	195 MPa @Strain 0.200 %, Temperature 870 Â°C	28300 psi @Strain 0.200 %, Temperature 1600 Â°F
Haynes HastelloyÂ® X alloy, sheet Solid-solution-strengthened with very good high-temperature strength and very good resistance to oxidizing environments up to about 1095Â°C, and good carburization resistance. Applications includ..
Tensile Strength, Yield	>= 195 MPa	>= 28300 psi
MetalTek MTEK 310 Cast UNS J94202 Austenitic Stainless Steel "300" series, general corrosion resistant alloyApplications: Nuclear, chemical and food processing. Valve and pump trim.Information provided by MetalTek
Tensile Strength, Yield	195 MPa @Strain 0.200 %, Temperature 870 Â°C	28300 psi @Strain 0.200 %, Temperature 1600 Â°F
Haynes 556Â® alloy, cold rolled, solution annealed sheet, 0.8-2.8 mm thick Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Tensile Strength, Yield	195 MPa	28300 psi	ASTM D638
Solvay TECHNYLÂ® SSD 330 KNF/E PA66, 15% glass filled, DRY Description: Polyamide 66, reinforced with 33% of glass fiber, for injection molding specially stabilized to improves its resistance to automotive cooling liquids.Available in: Asia PacificProduct A..
Tensile Strength, Yield	195 MPa	28300 psi	ISO 527-2
Solvay Specialty Polymers AmodelÂ® A-1933 HSL Polyphthalamide (PPA), 33% Glass Fiber AmodelÂ® A-1933 HSL is a 33% glass reinforced grade of polyphthalamide (PPA) resin. This grade was developed specifically for improved performance in a 50/50 ethylene glycol and water environment...
Tensile Strength, Yield	195 MPa	28300 psi	ASTM D638
Techmer ES HiFillÂ® PA6 GF35 HS L 35% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 35% Filler by WeightAdditive: Lubricant and Heat Stabilizer Features: Lubricated and Heat StabilizedProcessi..
Tensile Strength, Yield	195 MPa	28300 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP RF006SXZ PA 66 LNP* THERMOCOMP* RF006SXZ is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added feature of this material is: Heat Stabilized.
Tensile Strength, Yield	195 MPa	28300 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP STAT-KON REF42I PA 66 LNP* STAT-KON* REF42I is a compound based on Nylon 6/6 containing Proprietary Fillers. Added feature of this grade is: Electrically Conductive.
Tensile Strength, Yield	195 MPa	28300 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP Verton RV008ESV_GY7E072 PA 66 Preliminary data for 40% long glass fiber filled, single color pellet gray, PA66This data was supplied by SABIC-IP for the Americas region.
Tensile Strength, Yield	195 MPa	28300 psi	ASTM-D638
Polyram PlusTek PB302G8 Nylon 6, 40%Glass Fiber 40%glass-fiber reinforced, heat stabilized polyamide 6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
Tensile Strength, Yield	195 MPa	28300 psi	ASTM-D638
Polyram Polytron A30B02 Nylon 66, 30% Long Fiber 30% LONG FIBER GLASS REINFORCED BLACK NYLON 6.6 HEAT STABILIZED, UV STABILIZED FOR INJECTION MOLDING APPLICATION.Information provided by Polyram Ram On Ind.
Tensile Strength, Yield	195 MPa	28300 psi	ASTM-D638
Polyram Polytron A30N02 Nylon 66, 30% Long Fiber 30% LONG FIBER GLASS REINFORCED NATURAL NYLON 6.6 HEAT STABILIZED, UV STABILIZED FOR INJECTION MOLDING APPLICATION.Information provided by Polyram Ram On Ind.
Tensile Strength, Yield	195 MPa	28300 psi	dry; ISO 527
Ter Hell Plastic Terez® PA 6.6 7510 GF 50 Polyamide 66, 50% Glass Fiber Description: PA66 with medium viscosity, 50% glass fiber reinforced.Application: For molding parts with very high stiffness at good thermal stability.Information provided by Ter Hell Plastic GMBH...
Tensile Strength, Yield	195 MPa	28300 psi	ASTM D638
E-Polymers Tekaster® F615G45 , 45% Glass Fiber Reinforced PET 45% Glass Fiber reinforced, High strength, Information provided by E-Polymers Co. Ltd.
Tensile Strength, Yield	195 - 270 MPa	28300 - 39200 psi
ArcelorMittal 195 BH Bake hardening steel, Cold rolled Description: The composition and processing of these steels are designed to promote a significant increase in yield strength during low-temperature heat treatment, particularly paint curing. Arcelor..
Tensile Strength, Yield	195 MPa	28300 psi	ISO 527-2
Ascend Performance Materials Vydyne® R530 NAT Nylon 66, 30% Glass Reinforced, DAM Vydyne® R530 NAT is general-purpose, injection-molding grade, 30% glass-fiber reinforced PA66 resin. Available in natural, it is lubricated for good machine feed, flow and mold releaseAvailability:..
Tensile Strength, Yield	195 MPa	28300 psi	ISO 527-2
Solvay Specialty Polymers Amodel® A-1933 HSL Polyphthalamide (PPA) (Unverified Data**) Amodel A-1933 HSL is a 33% glass reinforced grade of polyphthalamide (PPA) resin. This grade was developed specifically for improved performance in a 50/50 ethylene glycol and water environment. Thi..
Tensile Strength, Yield	195 MPa	28300 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP RF007SXN PA 66 LNP* THERMOCOMP* RF007SXN is a Hydro-Stable, 35% Glass Fiber reinforced compound based on Nylon 66. Added features of this grade include: Heat Stabilized, NSF Listed.
Tensile Strength, Yield	195 MPa	28300 psi	ASTM-D638
Polyram Polytron A40B01 Nylon 66, 40% Long Fiber A 40% long fiber glass reinforced black nylon 6.6 heat stabilized for injection molding applications.Information provided by Polyram Ram On Ind.
Tensile Strength, Yield	195 MPa	28300 psi	ASTM D638
Solvay TECHNYL® 2411GF6 PA66, 30% glass fiber, DRY Description: Polyamid 66, 30% glass fiber reinforce, for injection moldingAvailable in: Asia PacificProduct Applications: TECHNYL® 2411GF6 used in all sectors of industry, offering an excellent com..
Tensile Strength, Yield	195 MPa @Strain 0.200 %, Temperature 538 °C	28300 psi @Strain 0.200 %, Temperature 1000 °F
Haynes Hastelloy® N, 1.14 mm sheet, heat treated at 1149°C (2100°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac..