Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 131 MPa | 19000 psi | ASTM D638 |
Oxford Polymers 30GF 30% Glass Fiber Reinforced Polybutylene Terephthalate (PBT) 30% Glass Fiber Reinforced Polybutylene Terephthalate (PBT)Information provided by Oxford Polymers. |
|||
Tensile Strength, Yield | 131 MPa @Temperature 23.9 °C |
19000 psi @Temperature 75.0 °F |
0° Direction, Dry; 325°F Autoclave; ASTM D638 |
Park Electrochemical Nelcote® F-554 Phenolic Prepreg, Commercial Silica Fabric Reinforced Nelcote® F-554 is a high purity silica filled phenolic resin coated on Commercial or Aerospace grade silica fabric. F-554 is used in the manufacture of intermediate temperature ablative rocket nozz.. |
|||
Tensile Strength, Yield | 131 MPa | 19000 psi | ASTM D638 |
Ravago Manufacturing Americas Hylon® N2040MGHL Nylon 6 (DAM) Information provided by Ravago. |
|||
Tensile Strength, Yield | 131 MPa | 19000 psi | ASTM D638 |
Polymer Resources NY6-M25G15-[color]-H Nylon 6, 25% Mineral, 15% Glass Reinforced, Heat Stabilized Nylon 6, 25% Mineral, 15% Glass Reinforced, Heat Stabilized, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test s.. |
|||
Tensile Strength, Yield | 131 - 159 MPa | 19000 - 23000 psi | Average value: 141 MPa Grade Count:5 |
Overview of materials for Polyphenylene Sulfide (PPS), PTFE/Glass-Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS), PTFE/Glass-Fiber Filled". Each property range of values reported is minimum.. |
|||
Tensile Strength, Yield | 131 - 138 MPa | 19000 - 20000 psi | Average value: 136 MPa Grade Count:3 |
Overview of materials for Nylon 6, Stainless Steel Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Stainless Steel Filled". Each property range of values reported is minimum and maximum values o.. |
|||
Tensile Strength, Yield | 131 MPa | 19000 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics ULTEM 2200F PEI 20% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming. US FDA Food Contact compliant in recognized colors. |
|||
Tensile Strength, Yield | 131 MPa | 19000 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM HU2200 PEI 20% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP .. |
|||
Tensile Strength, Yield | 131 MPa | 19000 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics ULTEM HU2200 PEI 20% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP .. |
|||
Tensile Strength, Yield | 131 MPa | 19000 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON DEL13EXC PC LNP STAT-KON* DEL13EXC is a compound based on Polycarbonate resin containing 15% Carbon Fiber, 5% PTFE. Added features of this material include: Easy Molding, Electrically Conductive, Wear Resistan.. |
|||
Tensile Strength, Yield | 131 MPa | 19000 psi | ASTM D638 |
Techmer ES HiFill® PA6 G/C40 L UV 40% Glass/Mineral Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass/Mineral, 40% Filler by WeightAdditive: Lubricant and UV StabilizerFeatures: Good UV Resistance and LubricatedTPCI# 6024102Informa.. |
|||
Tensile Strength, Yield | 131 MPa | 19000 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-KON RX98063 PA 66 (Europe-Africa-Middle East) LNP* STAT-KON* RX98063 is a compound based on PA 66 resin containing Glass Fiber, Stainless Steel Fiber. Added features include; Antistatic. |
|||
Tensile Strength, Yield | 131 MPa @Temperature 93.3 °C |
19000 psi @Temperature 200 °F |
ASTM D638 |
Techmer ES HiFill® PA6/6 GF45 TL10 45% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 45% Filler by WeightAdditive: PTFE Lubricant (10%)Features: LubricatedInformation provided by TP Composites.. |
|||
Tensile Strength, Yield | 131 MPa | 19000 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON Ultem_UC1200 PEI LNP* Stat-kon* Ultem_UC1200 is a 12% carbon fiber reinforced PEI. High modulus with ESD characteristics for high-heat applications. |
|||
Tensile Strength, Yield | 131 MPa | 19000 psi | ASTM D638 |
Techmer ES HiFill® PPS 0231 B LE Availability: North AmericaForms: PelletsFeatures: High Density and Low ExtractablesAppearance: OpaqueInformation provided by TP Composites, Inc. |
|||
Tensile Strength, Yield | 131 MPa | 19000 psi | ASTM D638 |
Techmer ES Electrablend® PA6 04001 FR MB Glass/Stainless Steel Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass/Stainless Steel FiberAdditive: LubricatedFeatures: Electromagnetic Shielding (EMI), Lubricated, Flame Retardant and Radio Frequen.. |
|||
Tensile Strength, Yield | 131 MPa | 19000 psi | ASTM D638 |
Techmer ES HiFill FR® PA4/6 GF15 FR HS L 15% Glass Filled (Dry) Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 15% Filler by WeightAdditive: Heat Stabilizer and LubricantFeatures: Flame Retardant, Lubricated and Heat St.. |
|||
Tensile Strength, Yield | 131 MPa | 19000 psi | ISO 527 |
SABIC Innovative Plastics LNP STAT-KON RE002 PA 66 (Asia Pacific) LNP* Stat-kon* RE002 is a compound based on Nylon 66 resin containing Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
Tensile Strength, Yield | 131 MPa | 19000 psi | ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON RE0029 PA 66 LNP* STAT-KON* RE0029 is a compound based on Nylon 66 resin containing 10% Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant. |
|||
Tensile Strength, Yield | 131 - 324 MPa | 19000 - 47000 psi | 0.2% offset |
Eagle Brass 220 Commercial Bronze, 1/4 Hard CDA 220 is known for having very good corrosion resistance, great cold workability and good hot workability for drawing, blanking, coining, stamping, piercing and punching. Typical uses include plum.. |
|||
Tensile Strength, Yield | 131 - 200 MPa | 19000 - 29000 psi | 0.2% offset |
Eagle Brass 510 Phosphor Bronzes 5% A, Annealed Alloy C510 is an alloy with good strength, formability and stress relaxation characteristics, and solderability. Applications include electronic parts, springs, switches, contacts and fasteners.Info.. |
|||
Tensile Strength, Yield | 131 MPa | 19000 psi | chs 2.0 in/min; ASTM D638 |
Diamond Polymers DIAMALOY 1001 CF30 30% Carbon Fiber Filled ABS Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
Tensile Strength, Yield | 131 MPa @Strain 0.200 %, Temperature 871 °C |
19000 psi @Strain 0.200 %, Temperature 1600 °F |
|
Carpenter 20Cb-3® Stainless Steel Data provided by Carpenter Technology Corporation.20Cb-3® is an austenitic stainless steel possessing excellent resistance to hot sulfuric acid and many other aggressive environments which would re.. |
|||
Tensile Strength, Yield | 131 MPa @Strain 0.200 %, Temperature 871 °C |
19000 psi @Strain 0.200 %, Temperature 1600 °F |
|
Carpenter Gall-Tough® Stainless Data provided by Carpenter Technology Corporation.6.4 mm diameter tensile specimens from center of 25.4 mm diameter bar annealed 1066°C 1 hour, water quenched, and ground.Threshold Galling Stress 1.. |
|||
Tensile Strength, Yield | 131 - 131 MPa @Temperature 93.3 - 93.3 °C |
19000 - 19000 psi @Temperature 200 - 200 °F |
Average value: 131 MPa Grade Count:1 |
Overview of materials for Nylon 66, PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, PTFE Filled". Each property range of values reported is minimum and maximum values of appropri.. |
|||
Tensile Strength, Yield | 131 MPa | 19000 psi | ASTM D638 |
Ashley Polymers Ashlene® PE126WO PET Polyester, 30% Glass Reinforced PET Polyester with 30% glass reinforcement, flame retardant, natural. Note: Colors will modify properties.Data provided by the manufacturer |
|||
Tensile Strength, Yield | 131 MPa | 19000 psi | Type 1 - Rigids, Yield, 0.2 in/min; ASTM D638 |
PolyOne Edgetek® ES-06CF-09GF/000 GREEN Polyethersulfone - 6% Carbon - 9% Glass Fiber Reinforced - ESD Applications
&am Data provided by PolyOne. |
|||
Tensile Strength, Yield | 131 MPa | 19000 psi | ASTM D638 |
SABIC Innovative Plastics LNP VERTON NV006E PC/ABS (Asia Pacific) LNP* Verton* NV006E is a compound based on PC/ABS resin containing Long Glass Fiber. Added features of this material include: Easy Molding. |
|||
Tensile Strength, Yield | 131 MPa | 19000 psi | ASTM D638 |
Oxford Polymers 30GF-25PTFE 30% Glass Fiber/PTFE Reinforced Polyphenylene Sulfide
(discontinued **) 30% Glass Fiber/PTFE Reinforced Polyphenylene SulfideInformation provided by Oxford Polymers. |
|||
Tensile Strength, Yield | 131 MPa | 19000 psi | ASTM D638 |
SABIC Innovative Plastics LNP VERTON NV006E PC+ABS LNP* Verton* NV006E is a compound based on PC+ABS blend resin containing 30% Long Glass Fiber. Added features of this material include: Easy Molding, Structural. |