Polymer Property : Tensile Strength, Yield = 17.00 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Yield 17.00 MPa
2465 psi
ASTM D638
Fiberfil® PP-61/CC/40 Polypropylene Copolymer, 40% Calcium Carbonate
Information provided by FIBERFIL Engineered Plastics
Tensile Strength, Yield 17.00 MPa
2465 psi
50 mm/min; ASTM D638
ICO Polymers ICORENEâ„¢ 110-1329 LMDPE Rotational Molding Resin
Description: ICORENE 110-1329 is a linear medium density polyethylene developed for use in rotational molding. This is a very fast processing material that quickly molds out to offer low surface po..
Tensile Strength, Yield 17.00 MPa
2465 psi
50 mm/min; ASTM D638
ICO Polymers ICORENEâ„¢ 110-1332 LMDPE Rotational Molding Resin
Description: ICORENE 110-1332 is a linear medium density polyethylene developed for use in rotational molding. This is a very fast processing material that quickly molds out to offer low surface po..
Tensile Strength, Yield 17.00 MPa
2466 psi
2"/min; ASTM D638
ICO Polymers ICORENEâ„¢ 115-1328 LMDPE Rotational Molding Resin
Description: ICORENE 115-1328 polyethylene developed for use in rotational molding. It is an easy processing material with good surface gloss, scratch resistance and generally balanced physical pro..
Tensile Strength, Yield 17.00 MPa
2465 psi
50 mm/min; ASTM D638
ICO Polymers ICORENEâ„¢ 115-1329 LMDPE Rotational Molding Resin
Description: ICORENE 115-1329 is a linear medium density polyethylene developed for use in rotational molding. It is an easy processing material with good surface gloss, scratch resistance and gene..
Tensile Strength, Yield 17.00 MPa
2465 psi
50 mm/min; ASTM D638
ICO Polymers ICORENEâ„¢ 115-1332 LMDPE Rotational Molding Resin
Description: ICORENE 115-1332 is a linear medium density polyethylene developed for use in rotational molding. It is an easy processing material with good surface gloss, scratch resistance and gene..
Tensile Strength, Yield 17.00 MPa
2465 psi
50 mm/min; ASTM D638
ICO Polymers ICORENEâ„¢ 115-1333 LMDPE Rotational Molding Resin
Description: ICORENE 115-1333 is a linear medium density polyethylene developed for use in rotational molding. It is an easy processing material with good surface gloss, scratch resistance and gene..
Tensile Strength, Yield 17.00 MPa
2466 psi
2"/min; ASTM D638
ICO Polymers ICORENEâ„¢ 115-1649 LMDPE Rotational Molding Resin
Description: ICORENE 115-1649 polyethylene developed for use in rotational molding. It is an easy processing material with good surface gloss, scratch resistance and generally balanced physical pro..
Tensile Strength, Yield 17.00 MPa
2466 psi
2"/min; ASTM D638
ICO Polymers ICORENEâ„¢ 115-1652 LMDPE Rotational Molding Resin
Description: ICORENE 115-1652 polyethylene developed for use in rotational molding. It is an easy processing material with good surface gloss, scratch resistance and generally balanced physical pro..
Tensile Strength, Yield 17.00 MPa
2465 psi
50 mm/min; ASTM D638
ICO Polymers ICORENEâ„¢ 190-1329 LMDPE Rotational Molding Resin
Description: ICORENE 190-1329 is a compounded linear medium density polyethylene copolymer developed for rotational molding. It has a good balance of properties such as toughness, easy flow and sti..
Tensile Strength, Yield 17.00 MPa
2465 psi
50 mm/min; ASTM D638
ICO Polymers ICORENEâ„¢ 190-1332 LMDPE Rotational Molding Resin
Description: ICORENE 190-1332 is a compounded linear density polyethylene copolymer developed for rotational molding. It has a good balance of properties such as toughness, easy flow and stiffness..
Tensile Strength, Yield 17.00 MPa
2465 psi
At 50 mm/min; ISO 527-2
Borealis Borpact™ SG321MO Polypropylene Random Heterophasic Copolymer for Injection Molding
Borpact SG321MO is a specially designed modified relatively soft and transparent polypropylene random heterophasic copolymer intended for injection molding. Borpact SG321MO has excellent flow, is f..
Tensile Strength, Yield 17.00 MPa
2465 psi
At 50 mm/min; ISO 527-2
Borealis Daplen™ EE115AE TPO Compound
Daplen EE115AE is a 10% mineral and elastomer modified polypropylene compound intended for injection molding. Daplen EE115AE is a material with excellent impact /stiffness ratio. Thanks to its low ..
Tensile Strength, Yield 17.00 MPa
2465 psi
At 50 mm/min; ISO 527-2
Borealis Daplen™ EE115T TPO Compound
Daplen EE115T is a 10% mineral and elastomer modified polypropylene compound intended for injection molding. Daplen EE115T is a material with excellent impact /stiffness ratio. Thanks to its low th..
Tensile Strength, Yield 17.00 MPa
2465 psi
Change in tensile strength after 504 hours at 248°F; ASTM D638
Teknor Apex Sinvicomp SIH 5005A Polyvinyl Chloride, Flexible
Availability: Asia Pacific Features: Good Stiffness Uses: Wire and Cable Applications Wire Types: V-90HT Agency Ratings: AS 3147-1992 Forms: Pellets Processing Method: ExtrusionInformation Provided ..
Tensile Strength, Yield 17.00 MPa
2465 psi
Change in tensile strength after 504 hours at 239°F; ASTM D638
Teknor Apex Sinvicomp SIH 5008A Polyvinyl Chloride, Flexible
Availability: Asia Pacific Features: Good Stiffness Uses: Wire and Cable Applications Wire Types: V-75 Agency Ratings: AS 3147-1992 Forms: Pellets Processing Method: ExtrusionInformation Provided by..
Tensile Strength, Yield 17.00 MPa
2465 psi
At 50 mm/min; ISO 527-2
Borealis Daplen™ EE109AE TPO Compound
Daplen EE109AE is a 20% mineral and elastomer modified polypropylene compound intended for injection molding. Daplen EE109AE is a material with excellent impact /stiffness ratio. Thanks to its low ..
Tensile Strength, Yield 17.00 MPa
2465 psi
At 50 mm/min; ISO 527-2
Borealis Daplen™ ED135AI TPO Compound
Daplen ED135AI is a 10% mineral filled grade intended for injection molding. ED135AI offers very good balance in stiffness/impact strengthDaplen ED135AI has been developed especially for the car in..