Polymer Property : Tensile Strength, Yield = 157 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Yield 157 MPa
22800 psi
ASTM D638
Samyang Tripet® 2550GN45 Polyethylene Terephthalate, 45% Glass Fiber Reinforced, Flame Retardant  (discontinue
TRIPET® has excellent heat resistance, good surface, chemical resistance and high electrical performance.Applications:Coil BobbinConnectorMotor HousingLamp HousingRelay BaseIron bodyAll information..
Tensile Strength, Yield 157 MPa

@Thickness 3.20 mm
22800 psi

@Thickness 0.126 in
5mm/min; ASTM D638
LG Chemical LUMID GP2200B(W) PA66+GF20%, General Purpose
Feature: Injection Molding, PA66+GF20%, General PurposeApplication: Automotive PartsCAS No. 32131-17-2 and 65997-17-3Information provided by LG Chemical
Tensile Strength, Yield 157 MPa
22800 psi
ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP RFL34 PA 66
LNP* LUBRICOMP* RFL34 is a compound based on Nylon 66 resin containing 20% Glass Fiber, 15% PTFE. Added feature of this material is: Wear Resistant.
Tensile Strength, Yield 157 MPa
22800 psi
ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP RFL34 PA 66 (Asia Pacific)
LNP* Lubricomp* RFL34 is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
Tensile Strength, Yield 157 MPa
22700 psi
ASTM D638
Techmer ES Luriblend® PA6 CF30 TS15 BK 30% Carbon Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber, 30% Filler by WeightAdditive: PTFE Lubricant (15%) and Silicone LubricantFeatures: LubricatedAppearance: Natural ColorPro..
Tensile Strength, Yield 157 MPa
22800 psi
5 mm/min; ASTM D638
Samsung Cheil Industries Infino® AR-9301 PA, Glass Filled General Purpose
Information provided by Samsung Cheil Industries.
Tensile Strength, Yield 157 MPa
22800 psi
5 mm/min; ASTM D638
Samsung Cheil Industries Infino® XP-2140 PPS
Information provided by Samsung Cheil Industries.
Tensile Strength, Yield 157 MPa
22800 psi
5 mm/min; ASTM D638
Samsung Cheil Industries Infino® XP-2150IM PPS, 50% Glass Reinforced
PPS/GS that is used in mobile phone LCD bracketInformation provided by Samsung Cheil Industries.
Tensile Strength, Yield 157 MPa
22800 psi
5 mm/min; ASTM D638
Samsung Cheil Industries Infino® AR-9301 PA, Glass Filled General Purpose
Information provided by Samsung Cheil Industries.
Tensile Strength, Yield 157 MPa
22800 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP OCF62 PPS - Branched
LNP* THERMOCOMP* OCF62 is a compound based on PPS-Branched resin containing 10% Carbon Fiber, 30% Glass Fiber. Added feature of this material includes: Easy Molding
Tensile Strength, Yield 157 MPa
22800 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP OCF62E PPS - Branched
LNP* THERMOCOMP* OCF62E is a compound based on PPS-Branched resin containing 10% Carbon Fiber, 30% Glass Fiber. Added feature of this material includes: Easy Molding
Tensile Strength, Yield 157 MPa
22800 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP QF007 PA 6/10
LNP* THERMOCOMP* QF007 is a compound based on Nylon 6/10 resin containing 35% Glass Fiber.
Tensile Strength, Yield 157 MPa
22700 psi
ASTM D638
Techmer ES HiFill® PPS GF40 BK 40% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 40% Filler by WeightAppearance: BlackInformation provided by TP Composites, Inc.
Tensile Strength, Yield 157 MPa
22800 psi
5 mm/min; ASTM D638
Samsung Cheil Industries Infino® XP-2150IM PPS, 50% Glass Reinforced
PPS/GS that is used in mobile phone LCD bracketInformation provided by Samsung Cheil Industries.
Tensile Strength, Yield 157 MPa
22800 psi
SABIC - Japan Method
SABIC Innovative Plastics NORYL GTX GTX6801 PPE+PA (Asia Pacific)
PPE+PA, GF 30%
Tensile Strength, Yield 157 MPa
22800 psi
ISO 527
Polyram PlusTek PA7800G33 Nylon 6.6 for Injection Molding, 33% Glass Fiber Reinforced, Heat Stabilized, Impact Modified
33% Glass fiber reinforced, heat stabilized, impact modified Nylon 6.6 for injection molding applications.Information provided by Polyram.
Tensile Strength, Yield 157 MPa
22800 psi
ASTM D638
Cheng Yu Plastic NG1300S Nylon 66, 30% Glass Fiber Reinforced
Tensile Strength, Yield 157 MPa
22800 psi
ASTM D638
Ensinger Tecapeek® GF30 Polyetheretherketone, 30% Glass Reinforced (PEEK)
Tecapeek™, made from Victrex PEEK polymer, is an excellent material for a wide spectrum of applications where thermal, chemical, and combustion properties are critical to performance. Excellent fle..
Tensile Strength, Yield 157 MPa
22800 psi
ASTM D638
E-Polymers TEKAMID® TA250GFR , Flame Retardant, 25% Glass Fiber Reinforced PA66, DAM
GF reinforced, Flame RetardantInformation provided by E-Polymers Co. Ltd.
Tensile Strength, Yield 157 MPa
22800 psi
ASTM D638
Cheng Yu Plastic FR200GV30 Flame Retardant Nylon 66, 30% Glass Fiber
Tensile Strength, Yield 157 MPa
22800 psi
Wet; ASTM D638
Asahi Kasei Leona® 13G43 43% Glass Filled Nylon 66
43% Glass Fiber Reinforced. Enhanced strength and stiffnessApplications:Mechanical and electrical parts such as micromotors, automotive parts such as radiator tanks and shift leversInformation provi..
Tensile Strength, Yield 157 MPa
22800 psi
Wet; ASTM D638
Asahi Kasei Leona® 90G33 33% Glass Filled Nylon 66
Enhanced strength and stiffness; with 33% GF. Superior fluidity and appearance.Applications:Automotive parts Information provided by Asahi Kasei
Tensile Strength, Yield 157 MPa
22800 psi
5 mm/min; ASTM D638
Samsung Cheil Industries Infino® XP-2140 PPS
Information provided by Samsung Cheil Industries.