Polymer Property : Tensile Strength, Yield = 142 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Yield 142 MPa
20600 psi
5 mm/min; ASTM D638
Samsung Cheil Industries Infino® AR-6508 PBT/PET, Glass Filled
Good WeatherabilityInformation provided by Samsung Cheil Industries.
Tensile Strength, Yield 142 MPa
20600 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP QF0069 PA6.10 (Europe-Africa-Middle East)
LNP* THERMOCOMP* QF0069 is a compound based on PA610 resin contaning Glass Fiber, Flame Retardant. Added features include: Flame retardant.
Tensile Strength, Yield 142 MPa
20600 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP JCL36E PES
LNP* LUBRICOMP* JCL36E is a compound based on Polyethersulfone (PES) resin containing 30% Carbon Fiber, 15% PTFE. Added feature of this grade is: Wear Resistant.
Tensile Strength, Yield 142 MPa
20600 psi
5 mm/min; ASTM D638
Samsung Cheil Industries Infino® AR-6508 PBT/PET, Glass Filled
Good WeatherabilityInformation provided by Samsung Cheil Industries.
Tensile Strength, Yield 142 MPa
20600 psi
SABIC - Japan Method
SABIC Innovative Plastics Noryl GTX GTX6801 PPE+PS+PA66 (Asia Pacific)
This data was supplied by SABIC-IP for the Asia Pacific region.
Tensile Strength, Yield 142 MPa
20600 psi
ASTM D638
Cheng Yu Plastic N6GV20 Flame Retardant Nylon 6, 20% Glass Filled
Tensile Strength, Yield 142 MPa

@Temperature -40.0 °C
20600 psi

@Temperature -40.0 °F
ASTM Test
BASF Ultramid® 8202C HS PA6 (Conditioned)
Ultramid 8202C HS is a heat stabilized, low viscosity, PA6 injection molding homopolymer possessing a modified crystalline structure for increased property performance and faster cycles. It is also..
Tensile Strength, Yield 142 MPa

@Temperature -40.0 °C
20600 psi

@Temperature -40.0 °F
ISO Data
BASF Ultramid® 8202C HS PA6 (Conditioned)
Ultramid 8202C HS is a heat stabilized, low viscosity, PA6 injection molding homopolymer possessing a modified crystalline structure for increased property performance and faster cycles. It is also..
Tensile Strength, Yield 142 MPa

@Temperature -40.0 °C
20600 psi

@Temperature -40.0 °F
ASTM Test
BASF Ultramid® 8202C PA6 (Conditioned)
Ultramid 8202C is a modified crystalline and low viscosity, nylon 6 injection molding homopolymer. It is also available in heat stabilized (Ultamid 8202C HS) and/or pigmented versions. Its unique ..
Tensile Strength, Yield 142 MPa

@Temperature -40.0 °C
20600 psi

@Temperature -40.0 °F
ISO Data
BASF Ultramid® 8202C PA6 (Conditioned)
Ultramid 8202C is a modified crystalline and low viscosity, nylon 6 injection molding homopolymer. It is also available in heat stabilized (Ultamid 8202C HS) and/or pigmented versions. Its unique ..
Tensile Strength, Yield 142 MPa

@Temperature -40.0 °C
20600 psi

@Temperature -40.0 °F
ISO Data
BASF Ultramid® 8202CQ PA6 (Conditioned)
Ultramid 8202CQ is a low viscosity, PA6 injection molding homopolymer, possessing a modified crystalline structure or increased property performance and faster cycles. It is also available in pigme..
Tensile Strength, Yield 142 MPa

@Temperature -40.0 °C
20600 psi

@Temperature -40.0 °F
ASTM Test
BASF Ultramid® 8202CQ PA6 (Conditioned)
Ultramid 8202CQ is a low viscosity, PA6 injection molding homopolymer, possessing a modified crystalline structure or increased property performance and faster cycles. It is also available in pigme..