Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 14.5 MPa | 2100 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Wire & Cable JAB40L Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications. Provisional Product Information - Physical and Mechanical properties based on initial production.Information provide.. |
|||
Tensile Strength, Yield | 14.5 MPa | 2100 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Wire & Cable JG513GO Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne |
|||
Tensile Strength, Yield | 14.5 MPa | 2100 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Wire & Cable WJAX204L Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications. Provisional Product Information - Physical and Mechanical properties based on initial production.Information provide.. |
|||
Tensile Strength, Yield | 14.5 MPa | 2100 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Wire & Cable WJAX204V Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne |
|||
Tensile Strength, Yield | 14.5 - 59.0 MPa | 2100 - 8560 psi | Average value: 33.1 MPa Grade Count:48 |
Overview of materials for Polystyrene, Molded, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Polystyrene". Each property range of values reported is minimum and maximum values of appropriate MatWeb.. |
|||
Tensile Strength, Yield | 14.5 MPa | 2100 psi | |
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 120 PHR N990 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Tensile Strength, Yield | 14.5 MPa | 2100 psi | 20 in/min; ASTM D638 |
LyondellBasell Microthene® MP564189 Linear Low Density Polyethylene, Injection Molding Grade ApplicationsMicrothene MP564189 exhibits good stiffness and low temperature toughness. Typical applications include trash cans, industrial containers, housewares and toys. MP564189 is 16 mesh powder.. |
|||
Tensile Strength, Yield | 14.5 MPa | 2100 psi | 20"/min; ASTM D638 |
LyondellBasell Petrothene® GA574189 Linear Low Density Polyethylene, Injection Molding Grade PETROTHENE GA574189 exhibits excellent flow and impact with good stiffness. Typical applications include lids, closures, containers, housewares and medical items.Regulatory Status: GA574189 meets th.. |
|||
Tensile Strength, Yield | 14.5 MPa | 2100 psi | ASTM D638 |
I. Stern 550 High Impact Polystyrene Features:Good process propertiesExcellent toughness and environmental stress crackingApplicationsStructural foamDisplaysSmall appliancesAgency RatingsFDA Title 21 CFR 177.1640UL File E220962Informat.. |
|||
Tensile Strength, Yield | 14.5 MPa | 2100 psi | ASTM D1457 |
Greene Tweed Avalon® 11 PTFE, Carbon, Graphite Filled Products made from Avalon® thermoplastics are constructed from proprietary high-performance reinforced PTFE material. Greene, Tweeds Avalon thermoplastics, available in grades ranging from virgin.. |
|||
Tensile Strength, Yield | 14.5 MPa | 2100 psi | Molded; ASTM D638 |
LyondellBasell Petrothene® NA940094 Low Density Polyethylene (Film Grade) ApplicationsPETROTHENE NA 940 is a series of resins designed for heavy duty film applications. Superior puncture resistance combined with excellent impact properties make NA 940 an ideal choice for.. |
|||
Tensile Strength, Yield | 14.5 MPa | 2100 psi | |
Spartech 2850-70 PVC for Regulated Applications Information provided by Spartech |
|||
Tensile Strength, Yield | 14.5 MPa | 2100 psi | 100%; ASTM D412 |
Teknor Apex APEX® 3300-90 Polyvinyl Chloride, Flexible Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTMFeatures-Sterilizable, RadiationUses-Automotive Applications, Food Service Applications, General Purpose, Med.. |
|||
Tensile Strength, Yield | 14.5 MPa | 2100 psi | 100%; ASTM D412 |
Teknor Apex APEX® 3302-90 Polyvinyl Chloride, Flexible Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTM Uses- Medical Applications, Tubing, Appearance-ClearForms-PelletsProcessing-ExtrusionInformation provided by.. |
|||
Tensile Strength, Yield | 14.5 MPa | 2100 psi | ASTM D412 |
Teknor Apex APEX® 3311-75 Polyvinyl Chloride, Flexible Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTM Uses-Automotive Applications, Food Service Applications, General Purpose, Medical Applications, Profiles, To.. |
|||
Tensile Strength, Yield | 14.5 MPa | 2100 psi | ASTM D638-95 |
Lubrizol Stat-Rite® X-5076 Static Control High Impact Polystyrene Stat-Rite® X-5076 is a static dissipative, High Impact Polystyrene alloy. Stat-Rite® X-5076 utilizes the patented Stat-Rite® inherently dissipative polymer (IDP) alloy system to provide clean, p.. |
|||
Tensile Strength, Yield | 14.5 MPa | 2100 psi | |
Trelleborg R408 Commercial Natural Rubber Polyisoprene All information provided by Trelleborg |
|||
Tensile Strength, Yield | 14.5 MPa | 2100 psi | heat aged 70 hours at 300ºF |
TSE Industries Millathane® 5004 Millable Polyurethane Elastomer with 60 PHR N330 (HAF) Black MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c.. |
|||
Tensile Strength, Yield | 14.5 MPa | 2100 psi | ASTM D-638-95 |
Lubrizol Stat-Rite® X5166 Static Dissipative Polystyrene Compound Stat-Rite® X5166 is a static dissipative, High-Impact Polystyrene alloy. Stat-Rite® X5166 utilizes the patented Stat-Rite® inherently dissipative polymer (IDP) alloy system to provide clean, perm.. |
|||
Tensile Strength, Yield | 14.5 MPa | 2100 psi | 2"/min; ASTM D638 |
A. Schulman POLYAXIS® LPA815 LPA 815EVA DescriptionPolyaxis LPA 815 is an EVA which is soft an pliable, even at low temperatures.NOTE: Physical properties are based on rotationally molded samples from unpigmented resin. Density and ESCR .. |
|||
Tensile Strength, Yield | 14.5 MPa | 2100 psi | 2"/min; ASTM D638 |
A. Schulman POLYAXIS® LPA815 LPA 815EVA DescriptionPolyaxis LPA 815 is an EVA which is soft an pliable, even at low temperatures.NOTE: Physical properties are based on rotationally molded samples from unpigmented resin. Density and ESCR .. |
|||
Tensile Strength, Yield | 14.5 MPa | 2100 psi | ASTM D-638 |
Axiall 59770 Wire & Cable Flexible PVC Non-lead stabilized, 105°C rated vinyl elastomer compound suitable for SJEOW insulation and jacket applications per UL 62. UL, QMTT2 recognized for 720 hour sunlight resistance applications.Inform.. |
|||
Tensile Strength, Yield | 14.5 MPa | 2100 psi | ASTM D-638 |
Axiall 9115A Wire & Cable Flexible PVC Low cost tray cable jacket.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013. |
|||
Tensile Strength, Yield | 14.5 MPa | 2110 psi | ASTM D-638 |
Axiall 12812 Moldings & Extrusions Flexible PVC General purpose, flame retardant extrusion compound formulated for good oil resistance. Also suitable for general purpose 80°C rated jacketing applications.Information provided by Georgia GulfGeor.. |
|||
Tensile Strength, Yield | 14.5 MPa | 2100 psi | ASTM D-638 |
Axiall 312 Wire & Cable Flexible PVC General purpose jacketing and insulation compound. UL recognized for 720 hour sunlight resistance in all colors.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013. |
|||
Tensile Strength, Yield | 14.5 MPa | 2100 psi | ASTM D412 |
Teknor Apex APEX® 3202-65 Polyvinyl Chloride, Flexible Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTMUses-Caps, Closure, Connectors, Food Service Applications, Safety Equipment, Valves/Valve Parts Appearance-Cl.. |
|||
Tensile Strength, Yield | 14.5 MPa | 2100 psi | |
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 120 PHR N990 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Tensile Strength, Yield | 14.5 MPa | 2100 psi | Molded; ASTM D638 |
LyondellBasell Petrothene® NA940000 Low Density Polyethylene (Film Grade) ApplicationsPETROTHENE NA 940 is a series of resins designed for heavy duty film applications. Superior puncture resistance combined with excellent impact properties make NA 940 an ideal choice for.. |
|||
Tensile Strength, Yield | 14.5 MPa | 2100 psi | ASTM D412 |
Teknor Apex APEX® 3302-65 Polyvinyl Chloride, Flexible Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTM Uses- Medical Applications, Tubing, Appearance-ClearForms-PelletsProcessing-ExtrusionInformation provided by.. |
|||
Tensile Strength, Yield | 14.5 MPa | 2100 psi | Method A (Dumbbell & Section), 20 in/min, Break; ASTM D412 |
PolyOne Synprene® RT-5145D Thermoplastic Elastomer - SBC
(discontinued **) Description/Features:High Performance Thermoplastic ElastomerNaturalIgnition ResistantApplications:Multi-PurposeMarket:Building and ConstructionConsumer GoodsIndustrialProcessing Method:Injection Mo.. |