Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 131 MPa | 19000 psi | ISO METHOD 527 |
NYCOA 2256 30% Glass Filled Nylon 6 30% glass filled, impact modified nylon 6Information provided by NYCOA, Inc. |
|||
Tensile Strength, Yield | 131 MPa | 19000 psi | ASTM D638 |
Oxford Polymers 30GF 30% Glass Fiber Reinforced Polybutylene Terephthalate (PBT) 30% Glass Fiber Reinforced Polybutylene Terephthalate (PBT)Information provided by Oxford Polymers. |
|||
Tensile Strength, Yield | 131 MPa @Temperature 23.9 °C |
19000 psi @Temperature 75.0 °F |
0° Direction, Dry; 325°F Autoclave; ASTM D638 |
Park Electrochemical Nelcote® F-554 Phenolic Prepreg, Commercial Silica Fabric Reinforced Nelcote® F-554 is a high purity silica filled phenolic resin coated on Commercial or Aerospace grade silica fabric. F-554 is used in the manufacture of intermediate temperature ablative rocket nozz.. |
|||
Tensile Strength, Yield | 131 MPa | 19000 psi | ASTM D638 |
Polymer Resources NY66-M25G15 Nylon 66, 25% Mineral, 15% Glass Reinforced Nylon 66, 25% Mineral, 15% Glass Reinforced, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon gr.. |
|||
Tensile Strength, Yield | 131 MPa | 19000 psi | ASTM D638 |
Ravago Manufacturing Americas Hylon® N2040MGHL Nylon 6 (DAM) Information provided by Ravago. |
|||
Tensile Strength, Yield | 131 MPa | 19000 psi | 0.125 in; ASTM D638 |
Matrixx Group 84S7301 Flame Retardant 30% Glass Reinforced PET (V0)
(discontinued **) Data provided by The Matrixx Group, formerly RePlas. |
|||
Tensile Strength, Yield | 131 MPa | 19000 psi | ASTM D638 |
Polymer Resources NY6-M25G15 Nylon 6, 25% Mineral, 15% Glass Reinforced Nylon 6, 25% Mineral, 15% Glass Reinforced, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon gra.. |
|||
Tensile Strength, Yield | 131 - 159 MPa | 19000 - 23000 psi | Average value: 141 MPa Grade Count:5 |
Overview of materials for Polyphenylene Sulfide (PPS), PTFE/Glass-Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS), PTFE/Glass-Fiber Filled". Each property range of values reported is minimum.. |
|||
Tensile Strength, Yield | 131 - 138 MPa | 19000 - 20000 psi | Average value: 136 MPa Grade Count:3 |
Overview of materials for Nylon 6, Stainless Steel Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Stainless Steel Filled". Each property range of values reported is minimum and maximum values o.. |
|||
Tensile Strength, Yield | 131 MPa | 19000 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM 2200F PEI 20% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming. US FDA Food Contact compliant in recognized colors. |
|||
Tensile Strength, Yield | 131 MPa | 19000 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics ULTEM 2200F PEI 20% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming. US FDA Food Contact compliant in recognized colors. |
|||
Tensile Strength, Yield | 131 MPa | 19000 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM HU2200 PEI 20% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP .. |
|||
Tensile Strength, Yield | 131 MPa | 19000 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM UC1200 PEI (Asia Pacific) 12% carbon fiber reinforced Polyetherimide (Tg 217C). ECO Conforming. UL94 V0 listing in recognized colors. |
|||
Tensile Strength, Yield | 131 MPa | 19000 psi | ASTM D638 |
Techmer ES HiFill® PA6/6 GF20 SL4 HS BK 20% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 20% Filler by WeightAdditive: Heat Stabilizer, Silicone Lubricant (4%) and LubricantFeatures: Heat Stabilize.. |
|||
Tensile Strength, Yield | 131 MPa | 19000 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-KON RX98063 PA 66 (Europe-Africa-Middle East) LNP* STAT-KON* RX98063 is a compound based on PA 66 resin containing Glass Fiber, Stainless Steel Fiber. Added features include; Antistatic. |
|||
Tensile Strength, Yield | 131 MPa @Temperature 93.3 °C |
19000 psi @Temperature 200 °F |
ASTM D638 |
Techmer ES HiFill® PA6/6 GF45 TL10 45% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 45% Filler by WeightAdditive: PTFE Lubricant (10%)Features: LubricatedInformation provided by TP Composites.. |
|||
Tensile Strength, Yield | 131 MPa | 19000 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON Ultem_UC1200 PEI (Europe-Africa-Middle East) LNP* Stat-kon* Ultem_UC1200 compound is a 12% carbon fiber reinforced PEI. High modulus with ESD characteristics for high-heat applications. |
|||
Tensile Strength, Yield | 131 MPa | 19000 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP KF008 Acetal Copolymer (Europe-Africa-Middle East) LNP* THERMOCOMP* KF008 is a compound based on Acetal Copolymer resin containing Glass Fiber. |
|||
Tensile Strength, Yield | 131 MPa | 19000 psi | ASTM D638 |
Techmer ES Statiblend® PPS GF40 EC BK 40% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 40% Filler by WeightFeatures: Semi ConductiveUL File Number: E157318Appearance: BlackInformation provided by TP Composites.. |
|||
Tensile Strength, Yield | 131 MPa | 19000 psi | ISO 527 |
SABIC Innovative Plastics LNP STAT-KON RE002 PA 66 LNP* STAT-KON* RE002 is a compound based on Nylon 66 resin containing 10% Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
Tensile Strength, Yield | 131 MPa | 19000 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Thermocomp RFB53U PA 66 (Europe-Africa-Middle East) LNP*THERMOCOMP*RFB53U is a compound based on PA 66 resin containing Glass Bead, Glass Fiber. Added features include: UV-Stabilized.This data was supplied by SABIC-IP for the Europe-Africa-Middle E.. |
|||
Tensile Strength, Yield | 131 MPa | 19000 psi | ASTM D638 |
Westlake Plastics Zelux® 30% GF Polycarbonate 30% Glass Filled Zelux polycarbonate is a transparent engineering plastic with excellent dimensional stability and good mechanical and electrical properties. It is used for structural applications when clarity and .. |
|||
Tensile Strength, Yield | 131 MPa | 19000 psi | chs 2.0 in/min; ASTM D638 |
Diamond Polymers DIAMALOY 1001 CF30 30% Carbon Fiber Filled ABS Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
Tensile Strength, Yield | 131 MPa | 19000 psi | 5 mm/min; ISO 527 |
Eurostar Staramide RFB53U PA66, 50% Glass Bead/Fiber Filled, Injection Molded RFB53U is a Glass Bead/ Glass Fiber Reinforced Polyamide 66 Injection Molding Resin (also known as Staramide 66 1525 VK Z4)Information provided by Eurostar. |
|||
Tensile Strength, Yield | 131 MPa | 19000 psi | chs 2.0 in/min; ASTM D638 |
Diamond Polymers DIAMALOY 1001 CF40 40% Carbon Fiber Filled ABS Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
Tensile Strength, Yield | 131 MPa | 19000 psi | 50 mm/min; ISO 527 |
Eurostar Staramide PF003U PA6, 15% Glass Fiber Filled, Injection Molded Staramide PF003U is an 15% Glass Fiber Reinforced, Polyamide 6 Injection Molding Resin, UV Stabilized (also known as Staramide 6 15V S4)Information provided by Eurostar. |
|||
Tensile Strength, Yield | 131 MPa | 19000 psi | ASTM D 638 |
SABIC Innovative Plastics LNP Verton NV006E PC/ABS LNP* Verton* NV006E is a compound based on PC/ABS resin containing Long Glass Fiber. Added features of this material include: Easy Molding.This data was supplied by SABIC-IP for the Americas region.. |
|||
Tensile Strength, Yield | 131 MPa | 19000 psi | ASTM D638 |
SABIC Innovative Plastics LNP VERTON NV006E PC/ABS (Asia Pacific) LNP* Verton* NV006E is a compound based on PC/ABS resin containing Long Glass Fiber. Added features of this material include: Easy Molding. |
|||
Tensile Strength, Yield | 131 MPa | 19000 psi | ASTM D638 |
Oxford Polymers 30GF-25PTFE 30% Glass Fiber/PTFE Reinforced Polyphenylene Sulfide
(discontinued **) 30% Glass Fiber/PTFE Reinforced Polyphenylene SulfideInformation provided by Oxford Polymers. |
|||
Tensile Strength, Yield | 131 MPa | 19000 psi | ASTM D638 |
SABIC Innovative Plastics LNP VERTON NV006E PC+ABS LNP* Verton* NV006E is a compound based on PC+ABS blend resin containing 30% Long Glass Fiber. Added features of this material include: Easy Molding, Structural. |