Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 86.0 MPa | 12500 psi | ASTM D638 |
NYCOA 512 PA 6 UL and NSF rated nucleated general purpose molding gradeInformation provided by NYCOA, Inc. |
|||
Tensile Strength, Yield | 86.0 MPa | 12500 psi | 50 mm/min; ASTM D638 |
Ovation Polymers OPTRENE 30GF Polypropylene, 30% Glass Reinforced Properties of chemically coupled glass reinforced (30%) polypropylene with high strength and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All .. |
|||
Tensile Strength, Yield | 86.2 MPa | 12500 psi | ASTM D638 |
Polymer Resources NY66-EX1 High Viscosity Nylon 66 Nylon 66, High Viscosity (RV 220 to 260)Process: ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry as .. |
|||
Tensile Strength, Yield | 86.2 MPa | 12500 psi | ASTM D638 |
Polymer Resources NY66-IM2-G13 Nylon 66, 13% Glass Reinforced, Impact Modified Nylon 66, 13% Glass Reinforced, Impact Modified, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylo.. |
|||
Tensile Strength, Yield | 86.2 MPa | 12500 psi | ASTM D638 |
PTS Trimid® N66-100HL Heat Stabilized, Lubed Nylon 6/6 Information provided by Polymer Technology and Services, LLC (PTS). |
|||
Tensile Strength, Yield | 86.2 MPa | 12500 psi | ASTM D638 |
PTS Trimid® N66-100NL Nucleated, Lubricated Nylon 6/6 Information provided by Polymer Technology and Services, LLC (PTS). |
|||
Tensile Strength, Yield | 86.0 MPa | 12500 psi | SABIC - Japan Method |
SABIC Innovative Plastics Lexan® LGN2000 PC (Asia Pacific) |
|||
Tensile Strength, Yield | 86.2 - 2070 MPa | 12500 - 300000 psi | Average value: 399 MPa Grade Count:17 |
Overview of materials for Polyetheretherketone, Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyetheretherketone, Carbon Fiber Filled". Each property range of values reported is minimum and maximu.. |
|||
Tensile Strength, Yield | 86.2 MPa | 12500 psi | Type 1 - Rigids, Yield, 0.2 in/min; ASTM D638 |
PolyOne Edgetek® MLS-10GF/000 Polysulfone Alloy - 10% Glass Fiber Reinforced
(discontinued **) Data provided by PolyOne. |
|||
Tensile Strength, Yield | 86.0 MPa | 12500 psi | ISO value at 50 mm/min. |
BASF Capron® 5202 HS BK-102 Nylon 66 (Dry)
(discontinued **) Capron 5202 HS BK-102 is an unfilled, heat stabilized, pigmented black nylon 6,6, injection molding compound. It combines strength and stiffness as well as excellent chemical resistance. The additi.. |
|||
Tensile Strength, Yield | 86.2 MPa | 12500 psi | ASTM D638 |
Global GAB-130 30% Glass Reinforced, General Purpose ABS Information provided by Global Polymers Corporation. |
|||
Tensile Strength, Yield | 86.0 MPa @Temperature 22.0 °C |
12500 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
Menzolit Menzolit® SMC 0390 Unsaturated Polyester UP SMC 0390 is a standard low profile SMC. Because of its low shrinkage, the material shows good surface quality as well as very low warpage. The product is suitable for applications if a better surfac.. |
|||
Tensile Strength, Yield | 86.0 MPa | 12500 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP EL002 PEI LNP* Lubricomp* EL002 is a compound based on Polyetherimide resin containing 10% PTFE. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength, Yield | 86.0 MPa | 12500 psi | ISO 527 type 1 A |
Solvay TECHNYL® A 50H1 PA66, DRY Description: Flame retardant polyamide 66, unreinforced, heat stabilized, for injection molding.Available in: Asia Pacific, Europe, Latin America and North AmericaProduct Applications: This phospho.. |
|||
Tensile Strength, Yield | 86.0 MPa | 12500 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Valox® VIC4311 PBT VALOX VIC4311 is a 30% glass filled, impact modified PBT with excellent epoxy adhesion. Automotive underhood applications such as ignition coil housings. |
|||
Tensile Strength, Yield | 86.2 MPa | 12500 psi | ASTM D638 |
Techmer ES HiFill® PA6 GF40 L 40% Milled Glass Availability: North AmericaForms: PelletsFiller/Reinforcement: Milled Glass Fiber, 30% Filler by WeightAdditive: LubricantFeatures: LubricatedAppearance: Natural ColorInformation provided by TP Comp.. |
|||
Tensile Strength, Yield | 86.2 MPa | 12500 psi | ASTM D638 |
Techmer ES HiFill® PA6/6 GF/M25HS L BK 25% Glass/Mineral Fiber Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 25% Filler by Weight and Mineral Filler, 25% Filler by WeightAdditive: Lubricant and Heat StabilizerFeatures.. |
|||
Tensile Strength, Yield | 86.2 MPa | 12500 psi | ASTM D638 |
Techmer ES HiFill® PA6/6 GF5 L BK 5% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 5% Filler by WeightAdditive: LubricantFeatures: LubricatedAppearance: BlackInformation provided by TP Compos.. |
|||
Tensile Strength, Yield | 86.2 MPa | 12500 psi | ASTM D638 |
Techmer ES HiFill® PP GF40 CC 40% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 40% Filler by WeightFeatures: Chemically CoupledInformation provided by TP Composites, Inc. |
|||
Tensile Strength, Yield | 86.2 MPa | 12500 psi | ASTM D638 |
Techmer ES Luriblend® TPX-PA6-03034 Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber ReinforcementAdditive: LubricantFeatures: Lubricated, Good Wear Resistance and Low FrictionAppearance: BlackInformation pro.. |
|||
Tensile Strength, Yield | 86.0 MPa | 12500 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL PKN4752 PPE+PS PPE+PS blend. High Heat. Translucent with yellow tint in natural color. FDA compliant. Extrusion and Injection Molding. Typical applications include High Performance Food Packaging, Electronics and .. |
|||
Tensile Strength, Yield | 86.0 MPa | 12500 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL PKN4752 PPE+PS (Asia Pacific) PPE+PS. Translucent. FDA compliant. High heat. Extrusion. Microwavable. Food, electrical/electronic packaging uses. |
|||
Tensile Strength, Yield | 86.0 MPa | 12500 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP QFL32 PA 6/10 LNP* LUBRICOMP* QFL32 is a compound based on Nylon 6/10 containing 10% Glass Fiber, 15% PTFE. Added features of this grade include: Wear Resistant. |
|||
Tensile Strength, Yield | 86.0 MPa | 12500 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON AE002 ABS LNP* STAT-KON* AE002 is a compound based on ABS resin containing 10% Carbon Fiber. Added feature of this material is: Electrically Conductive. |
|||
Tensile Strength, Yield | 86.2 MPa @Temperature 22.8 °C |
12500 psi @Temperature 73.0 °F |
ASTM D638 |
Ensinger TECAPET™ PET Polyethylene Terephthalate (PET) TECAPET™ PET is an unreinforced, semicrystalline thermoplastic polyester derived from polyethylene terephthalate. Its excellent wear resistance, low coefficient of friction, high flexural modulus,.. |
|||
Tensile Strength, Yield | 86.0 MPa | 12500 psi | ISO 527 |
Azoty Tarnow™ TARNOFORM 300 XEC1 POM Electrically conductive, carbon fiber reinforced injection molding grade suitable for the applications where increased strength and stiffness is required.Information provided by Zakłady Azotowe .. |
|||
Tensile Strength, Yield | 86.0 MPa | 12500 psi | 50mm/min; ISO 527 |
BASF Ultramid® 8202CQ PA6 (Dry) Ultramid 8202CQ is a low viscosity, PA6 injection molding homopolymer, possessing a modified crystalline structure or increased property performance and faster cycles. It is also available in pigme.. |
|||
Tensile Strength, Yield | 86.2 MPa | 12500 psi | ASTM D638 |
Techmer ES Plastiblend® ABS/PBT GF15 Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 15% Filler by WeightInformation provided by TP Composites, Inc. |
|||
Tensile Strength, Yield | 86.0 MPa | 12500 psi | 50 mm/min |
Arkema Group Oroglas® V 044 Acrylic, Extrusion Grade
(discontinued **) OROGLAS V 044 is an extrusion grade offering good compromise between physical properties and thermal resistance.OROGLAS V 044 is recommended for extrusion of profiles, tubes and sheets.ISO data prov.. |
|||
Tensile Strength, Yield | 86.0 MPa | 12500 psi | 50 mm/min |
Arkema Group Oroglas® V 045 Acrylic, Extrusion Grade
(discontinued **) OROGLAS V 045 is a lubricated extrusion grade offering good combination of physical and optical properties.OROGLAS V 045 provides easy processing behavior.OROGLAS V 045 is recommended for extrusion.. |