Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	8.06 MPa	1170 psi	ASTM D412
Precision Polymer Engineering C70G Chloroprene Rubber Green Chloroprene Rubber, 72-78 °IRHDApplications: A versatile rubber with good compression set properties, giving moderate resistance to petroleum based oils, ozone and weather.
Tensile Strength, Yield	8.10 MPa	1170 psi	-10% change after 70 hours @ 70°C; ASTM D412
Precision Polymer Engineering N50C Nitrile Rubber Nitrile Butadiene Rubber, 45-55 °IRHD. High acrylonitrile (ACN) content. Copolymer of acrylonitrile and butadiene. To meet British Gas Specification BGC/PS/LC6 Class B, approval ref.: 67/6.11.iv. M..
Tensile Strength, Yield	8.10 MPa	1170 psi	-10% change after 70 hours @ 70°C; ASTM D412
Precision Polymer Engineering N60C Nitrile Rubber Nitrile Butadiene Rubber (NBR). High acrylonitrile (ACN) content. Copolymer of acrylonitrile and butadiene. To meet British Gas Specification BGC/PS/LC6 Class "C", 55-65 IRHD. Approval ref.: 31/6.1...
Tensile Strength, Yield	8.10 MPa	1170 psi	-10% change after 168 hours @ 100°C; ASTM D412
Precision Polymer Engineering N60N Nitrile Rubber Nitrile Butadiene Rubber (NBR) 55-65 °IRHD. Copolymer of acrylonitrile and butadiene. To meet Aerospace Material Specification DTD5595A Grade 60.Applications: Synthetic rubber resistant to petrole..
Tensile Strength, Yield	8.10 MPa	1170 psi	-10% change after 70 hours @ 100°C; ASTM D412
Precision Polymer Engineering N70C Nitrile Rubber Nitrile Butadiene Rubber (NBR), 65-75 °IRHD. High acrylonitrile (ACN) content. Copolymer of acrylonitrile and butadiene. To meet British Gas Specification BGC/PS/LC6 Class D, approval ref.: 31/6.1...
Tensile Strength, Yield	8.10 MPa	1170 psi	-10% change after 70 hours @ 100°C; ASTM D412
Precision Polymer Engineering N80C Nitrile Rubber High Nitrile Rubber, 75-85 °IRHD. High acrylonitrile (ACN) content (38%). Copolymer of acrylonitrile and butadiene. ASTM designation = NBR. ISO designation = NBR. British Gas Specification BGC/PS/L..
Tensile Strength, Yield	8.10 MPa	1170 psi
Silon Tabond 3032 Adhesive Resin Tabond 3032 is a chemically modified LDPE / LLDPE. Its functional groups improve considerably the bonding between polar polymers, for film applications.Characteristics: â€¢ Strong adhesion to PA ..
Tensile Strength, Yield	8.10 MPa	1170 psi	ASTM D412
Vicone High Performance Rubber VicoSil™ C240Q-RD High Performance Silicone Rubber Information provided by Vicone
Tensile Strength, Yield	8.07 MPa	1170 psi	Neat Resin, RT
Hexcel® Redux® HP655 Toughened BMI film Adhesive Redux® HP655 is a toughened BMI structural adhesive designed for metal to metal, composite to composite, and honeycomb sandwich bonding for both co-cured and precured composite skins. Redux® HP655..
Tensile Strength, Yield	8.10 MPa	1170 psi
Dow DOWLEX™ 2535 Linear Low Density Polyethylene, Narrow MW Distribution DOWLEX® 2535 Polyethylene resin is a narrow molecular weight distribution copolymer designed to offer excellent impact strength and stress crack resistance with good flexibility. It has good proces..
Tensile Strength, Yield	8.10 MPa	1170 psi	Molded property
Dow Primacor® 1430 Ethylene Acrylic Acid (EAA) Film properties below based on a film thickness of 60 µm. Data provided by Dow Chemical.
Tensile Strength, Yield	8.10 MPa @Strain 50.0 %	1170 psi @Strain 50.0 %	50 mm/min
Arkema Group Pebax® 4033 SN 01 Polyether Block Amide (PEBA) (Dry) POLYETHER BLOCK AMIDE (PEBA) hardness 40 shore D Non plasticized flexible Polyamide Outstanding mechanical properties at low temperature (-40°C) Applications: molded parts for sport goods (softness..