- Polymer Property : Tensile Strength, Yield = 111 MPa
Polymer Property : Tensile Strength, Yield = 111 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 111 MPa | 16100 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Lexan® HFD4413 PC Lexan* HFD4413 is a 30% glass filled, injection moldable grade designed for high flow and superior surface appearance. Internal mold release. |
|||
| Tensile Strength, Yield | 111 MPa | 16100 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Lexan® HFD4413 PC (Asia Pacific) Lexan* HFD4413 is a 30% glass filled, injection moldable grade designed for high flow and superior surface appearance. Internal mold release. |
|||
| Tensile Strength, Yield | 111 MPa | 16100 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP RFL449 PA 66 LNP* LUBRICOMP* RFL449 is a compound based on Nylon 66 resin containing 20% Glass Fiber, 20% PTFE. Added features of this grade include: Wear Resistant, Flame Retardant. |
|||
| Tensile Strength, Yield | 111 MPa | 16100 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Valox® SHF436HR PBT PBT, Super High Flow, 30% glass reinforced,hydrolytically resistant. |
|||
| Tensile Strength, Yield | 111 MPa | 16100 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Valox® SHF436HR PBT (Asia Pacific) PBT, Super High Flow, 30% glass reinforced,hydrolytically resistant. |
|||
| Tensile Strength, Yield | 111 MPa | 16100 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Valox® SHF436HR PBT (Europe-Africa-Middle East) PBT, Super High Flow, 30% glass reinforced,hydrolytically resistant. |
|||
| Tensile Strength, Yield | 111 MPa | 16100 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics LNP STAT-KON Lexan_LCF1506 PC LNP* Stat-kon* Lexan_LC1500N compound is a 15% carbon fiber, 6% PTFE reinforced polycarbonate. |
|||
| Tensile Strength, Yield | 111 MPa | 16100 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics LNP STAT-KON Lexan_LCF1506 PC (Europe-Africa-Middle East) LNP* Stat-kon* Lexan_LCF1506 is a 15% carbon fiber, 6% PTFE reinforced polycarbonate. |
|||
| Tensile Strength, Yield | 111 MPa | 16100 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics Valox® V4860HR PBT 30% glass reinforced PBT, UL94 V-0 rated, Hydrolytically stable, Impact Modified. |
|||
| Tensile Strength, Yield | 111 MPa | 16100 psi | ASTM D638 |
| Techmer ES HiFill® PA6 GF15 UV002 15% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 15% Filler by Weight Additive: UV Stabilizer and LubricantFeatures: Good UV Resistance and LubricatedInforma.. |
|||
| Tensile Strength, Yield | 111 MPa | 16100 psi | ASTM D638 |
| Techmer ES Plastiblend® PBT/ABS GF/M40 FR 40/40% Glass/Mineral Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass/Mineral Fiber Reinforcement, 40/40% Filler by WeightFeatures: Flame RetardantInformation provided by TP Composites, Inc. |
|||
| Tensile Strength, Yield | 111 MPa | 16100 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP THERMOCOMP UF009AS PPA (Europe-Africa-Middle East) LNP* Thermocomp* UF009AS is a compound based on Polyphthalamide resin containing Glass Fiber. |
|||
| Tensile Strength, Yield | 111 MPa | 16100 psi | ISO 527 |
| SABIC Innovative Plastics LNP VERTON MX02795 PP (Asia Pacific) LNP* Verton* MX02795 is a compound based on Polypropylene resin containing Long Glass Fiber. Added features of this material include: Chemically Coupled, Heat Stabilized, UV Stabilized. |
|||
| Tensile Strength, Yield | 111 MPa | 16100 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics Valox® V4860HR PBT (Asia Pacific) 30% glass reinforced PBT, UL94 V-0 rated, Hydrolytically stable, Impact Modified. |
|||
| Tensile Strength, Yield | 111 MPa | 16100 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics Valox® V4860HR PBT (Europe-Africa-Middle East) 30% glass reinforced PBT, UL94 V-0 rated, Hydrolytically stable, Impact Modified. |
|||
| Tensile Strength, Yield | 111 MPa | 16100 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP Thermocomp LFZ42XXC PEEK LNP THERMOCOMP* LFZ42XXC is a compound based on Polyetheretherketone resin containing Glass Fiber, Milled Glass. Added features of this material include: Low Warpage.This data was supplied by SABIC.. |
|||
| Tensile Strength, Yield | 111 MPa | 16100 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics LNP THERMOTUF PX95726 PA 6 LNP THERMOTUF* PX95726 is a compound based on Nylon 6 resin containing Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
| Tensile Strength, Yield | 111 MPa | 16100 psi | ISO 527 |
| SABIC Innovative Plastics LNP VERTON MX02795 PP LNP* VERTON* MX02795 is a compound based on Polypropylene resin containing Proprietary Fillers. Added features of this material include: Heat Stabilized, UV Stabilized, Structural. |
|||
| Tensile Strength, Yield | 111 MPa | 16100 psi | ASTM D638 |
| Cheng Yu Plastic T883GV25 Flame Retardant PBT, 25% Glass Fiber |
|||
| Tensile Strength, Yield | 111 MPa | 16100 psi | ASTM D638 |
| Cheng Yu Plastic T889G25 PBT, 25% Glass Fiber |
|||
| Tensile Strength, Yield | 111 MPa | 16100 psi | 5 mm/min; ISO 527 |
| Eurostar Starflam RX06082 PA66/6, Glass Fiber Filled, Flame Retardant, Injection Molded Staramide RX06082 is a Halogen Free and Red Phosphorous Free, flame Retardant, Glass Fiber Reinforced Polyamide 66/Polyamide 6 Injection Molding ResinInformation provided by Eurostar. |
|||
| Tensile Strength, Yield | 111 - 214 MPa @Temperature -40.0 - 80.0 °C |
16100 - 31000 psi @Temperature -40.0 - 176 °F |
Average value: 176 MPa Grade Count:2 |
| Overview of materials for Nylon 6, 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. E.. |
|||
| Tensile Strength, Yield | 111 MPa | 16100 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Lexan® HFD4413 PC (Europe-Africa-Middle East) Lexan* HFD4413 is a 30% glass filled, injection moldable grade designed for high flow and superior surface appearance. Internal mold release. |
|||
| Tensile Strength, Yield | 111 MPa | 16100 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics LNP STAT-KON Lexan_LCF1506 PC (Asia Pacific) 15% carbon fiber, 6% PTFE reinforced polycarbonate. |
|||