Polymer Property : Film Tensile Strength at Break, MD = 7690 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Break, MD	53.0 MPa	7690 psi	ASTM D882
NOVA Chemicals Sclair® 19H Homopolymer HDPE Film Resin Features: High stiffnessGood processability Low gel Applications: BlendingCo-extrusionInformation provided by Nova Chemicals
Film Tensile Strength at Break, MD	53.0 MPa	7690 psi	ASTM D882
Chevron Phillips 7109DT LLDPE Blown Film Resin, Hexene Copolymer (discontinued **) Resin Type: Hexene Copolymer, No Slip, No Antiblock Version of 7109T with Process Aid, Cast/Blown Film ResinCharacteristics: Good Stiffness at Thin Gauges, Good Drawdown, Can be used straight or ble..
Film Tensile Strength at Break, MD	53.0 MPa	7690 psi	ASTM D882
Chevron Phillips 7109T LLDPE Blown Film Resin, Hexene Copolymer (discontinued **) Resin Type: Hexene CopolymerCharacteristics: Good Stiffness at Thin Gauges, Good Drawdown, Can be used straight or blended with LDPE or HDPEApplications:Industrial Liners, Stretch Wrap, Garment Bags..
Film Tensile Strength at Break, MD	53.0 MPa	7690 psi	ASTM D882
Solvay Specialty Polymers Ajediumâ„¢ Films -- HalarÂ® 500LC Ethylene Chlorotrifluoroethylene Copolymer (ECTFE) HalarÂ® ECTFE is a semi-crystalline fluoropolymer with a chemical structure of a 1:1 alternating copolymer of ethylene and chlorotrifluoroethylene.HalarÂ® film is a strong, hard, tough, abrasion..
Film Tensile Strength at Break, MD	53.0 MPa	7690 psi	ASTM D882
Teknor Apex Terraloy™ BP 10000A Thermoplastic Starch + LLDPE Notes: Terraloy™ BP-10001A is a Thermoplastic Starch/LLDPE ready-to-process compound that contains up to 30% of TPS renewable content. This compound is for blown film application. Forms: Pellets A..
Film Tensile Strength at Break, MD	53.0 MPa	7690 psi	ASTM D882
Eastman Eastman Embrace Copolyester for Extrusion/Cast Film Applications:Flexible packagingIV containersLabels to fit high contour containersShrink packagingWrap around designKey Attributes:Excellent clarityExcellent printabilityGood chemical resistanceGood ..
Film Tensile Strength at Break, MD	53.0 MPa	7690 psi	ASTM D882
Huntsman Rexell® L8404 Cast Film Extrusion LLDPE (discontinued **) Linear-low density copolymer, and FDA compliant.Applications: Blown film extrusion: general purpose.Film properties based on 1.0 guage (25 µm) thickness; blow-up ratio 2:1.Information provided by H..