Polymer Property : Film Tensile Strength at Break, MD = 39.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Break, MD	39.0 MPa	5660 psi	ASTM D882
NOVA Chemicals Sclair® 19A Homopolymer HDPE Film Resin Film Properties.Data provided by the manufacturer.
Film Tensile Strength at Break, MD	39.0 MPa	5660 psi	ASTM D882
Westlake Mxsite LC78105-C Polyethylene Film, Using Energx Technology Services (discontinued **) Mxsite LC78105-C polyethylene is recommended for the skin layers of blown stretch film. It will provide a very aggressive cling force in both a stretched and unstretched condition. The excellent cli..
Film Tensile Strength at Break, MD	39.0 MPa	5660 psi	ASTM D 882
NOVA Chemicals Sclair® 99K Homopolymer HDPE Film Resin 99K complies with the U.S. FDA specifications for olefin polymers and may thus be used in the United States as an article or component of an article intended for use in contact with food, without te..
Film Tensile Strength at Break, MD	39.0 MPa	5660 psi	ASTM D882-02
Ipiranga Petrochem LB 0216 LLDP IPQ produces Linear Low Density Polyethylene (LLDPE) for use by plastics molding industry segments that employ extrusion processes in the manufacturing of films destined for producing bobbins and ba..
Film Tensile Strength at Break, MD	39.0 MPa	5660 psi	ISO 527-3
Borealis FG5190 Linear Low Density Polyethylene FG5190 is a Butene Linear Low Density Polyethylene for Film Extrusion. Includes Antioxidant. The grade is developed for medium and heavy duty bags, bags and bin liners, dual stretch films, and film..
Film Tensile Strength at Break, MD	39.0 MPa	5660 psi	ISO 527-3
Total EVA 1005 VN 35 Ethylene Vinyl Acetate Copolymer - Blown Film EVA 1005 VN 35 is made by a high pressure tubular process. Grade for flexible films, with high transparency and outstanding mechanical properties. Contains NO antioxidant.Information provided by T..
Film Tensile Strength at Break, MD	39.0 MPa	5660 psi	ISO 527-3
Total Lumicene® mPE M 4707 EP Metallocene Polyethylene, Blown Film This product is a Total Ecosolutions grade.Lumicene® mPE M 4707 EP is a second generation metallocene based High Density Polyethylene with hexene as comonomer.Lumicene® mPE M 4707 EP can be proces..
Film Tensile Strength at Break, MD	39.0 MPa	5660 psi	ISO 527-3
Total Lumicene® mPE M 2735 S01 Metallocene Polyethylene, Cast Film Lumicene® mPE M 2735 S01 is a Lumicene® metallocene based Polyethylene with hexene as comonomer.Lumicene® mPE M 2735 S01 can be processed at high output rates with low extrusion pressure, low nec..
Film Tensile Strength at Break, MD	39.0 MPa	5660 psi	ASTM D882
DuPont™ Sclairfilm® BL-1 LLDPE Film, PVDC Coated, 51 µm Thickness (discontinued **) Data provided by DuPont Packaging Polymers.A one-side PVDC-coated LLDPE sealant film, which provides excellent barrier properties, while retaining the outstanding physical and seal strength characte..
Film Tensile Strength at Break, MD	39.0 MPa	5660 psi	ISO 527-3
Total Lumicene® mPE M 3427 Metallocene Polyethylene, Cast Film Lumicene® mPE M 3427 is a second generation metallocene based Polyethylene with hexene as comonomer.Lumicene® mPE M 3427 can be processed at high output rates with low extrusion pressure, low neck..