Polymer Property : Film Tensile Strength at Break, MD = 38.6 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Film Tensile Strength at Break, MD 38.6 MPa
5600 psi
ASTM D882
M. Holland Company LL104 LLDPE  (discontinued **)
Additives: Antiblock, SlipFeatures: Unspecified Antiblocking, Butene Comonomer, Copolymer, Good Drawdown, Good Processability, Unspecified SlipUses: Film, LinersApprovals: FDA 21 CFR 177.1520(c) 2.2..
Film Tensile Strength at Break, MD 38.6 MPa
5600 psi
50 µm (2 mil) film; ASTM D882
DuPont Nucrel® 1202HC Ethylene-Methacrylic Acid Copolymer Resin for Blown and Cast Film
11.5 wt% Methacrylic Acid.Nucrel® 1202HC (High-Clarity) is an ethylene-methacrylic acid copolymer resin available for use in conventional blown and cast film extrusion and coextrusion equipment des..
Film Tensile Strength at Break, MD 38.6 MPa
5600 psi
Dow Elite® 5200 Linear Low Density Polyethylene
5200 enhanced polyethylene resin is a copolymer produced via INSITE Technology from Dow Plastics. This resin offers high impact strength and good puncture resistance at moderate stretch levels for ..
Film Tensile Strength at Break, MD 38.6 MPa
5600 psi
ASTM D882
Bapolene® 122F Polyethylene, Film Grade
Bapolene LL122F is a general purpose LLDPE for blown film extrusion applications. This resin offers excellent tensile and toughness properties. Contains medium levels of slip/antiblock additives. ..