Polymer Property : Film Tensile Strength at Break, MD = 12300 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Break, MD	84.8 MPa	12300 psi	ASTM D822
LyondellBasell AlathonÂ® L5906 High Density Polyethylene ApplicationsALATHON XL 5906 is a high molecular weight high density polyethylene homopolymer with a broad bimodal molecular weight distribution. This resin exhibits excellent stiffness, very high t..
Film Tensile Strength at Break, MD	85.0 MPa	12300 psi	parallel; ISO 527-3
DSM Akulon® XP36-C1 PA6 Film Extrusion, Medium Viscosity, Lubricated
Film Tensile Strength at Break, MD	85.0 MPa	12300 psi	ISO 527-3
EMS-Grivory Grivory® CF 6 S PA* Product description: Grilon CF 6 S is an extracted copolyamide with a low melting point. Very high flexibility and toughnessVery good thermoforming and orientation propertiesHigh shrinkVery good tra..
Film Tensile Strength at Break, MD	84.8 MPa	12300 psi	ASTM D882
ExxonMobil EXACT™ 4151 Plastomer for Cast Film Product Description: Exact 4151 is an ethylene-based hexane plastomer produced using ExxonMobil Chemical’s EXXPOL® Catalyst Technology. Exact 4151 is designed for both monolayer multilayer coextru..
Film Tensile Strength at Break, MD	84.8 MPa	12300 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Label-Lyte™ 38DL247 OPP Film Product Description: A super white opaque, high gloss, high yield and highly cavitated BOPP film designed for use in reel-fed wrap-around labeling applications where superior graphics are desired.Av..
Film Tensile Strength at Break, MD	84.8 MPa	12300 psi	20 in/min, 2.0 in Jaw Separation; ExxonMobil Method
ExxonMobil Label-Lyte™ 70LT447 OPP Film Product Description: A matte finish, coated, white, polypropylene film designed for use in demanding thermal transfer, pressure-sensitive label applications. It is also compatible with a wide range ..
Film Tensile Strength at Break, MD	84.8 MPa	12300 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Oppalyte™ 38DO447 OPP Film Product Description: A super white opaque BOPP film. The Diamex technology allows for super low density and very high yield. Diamex makes it possible to lower the density, without decreasing the mod..
Film Tensile Strength at Break, MD	85.0 MPa	12300 psi	parallel; ISO 527-3
DSM Akulon® XP32-C1 PA6 Film Extrusion, Medium Viscosity, Lubricated
Film Tensile Strength at Break, MD	85.0 MPa	12300 psi	ISO 527-3
EMS-Grivory Grivory® G 25 PA6I/6T Product description: Grivory G 25 is a very high viscous amorphous copolyamide. It is suitable for injection stretch blow molding, injection blow molding, extrusion blow molding, the manufacture of ..
Film Tensile Strength at Break, MD	85.0 MPa	12300 psi	ASTM D882
Braskem Green PE SGM9450F Blow Film Extrusion and Cast Film Extrusion High Density Polyethylene Description: SGM9450F is a high-density polyethylene, developed for the high molecular weight film extrusion segment produced with bimodal technology. The film produced from this resin has high tena..
Film Tensile Strength at Break, MD	85.0 MPa	12300 psi	ISO 527-3
EMS-Grivory Grivory® G 21 PA6I/6T Product description: Grivory G 21 natural 6506 is a high viscosity, partially aromatic, amorphous copolyamide with processing aid. Improved gas and aroma barrier at elevated relative humidityExcelle..
Film Tensile Strength at Break, MD	84.8 MPa	12300 psi	20 in/min, 2.0 in Jaw Separation; ExxonMobil Method
ExxonMobil Oppalyte™ 30 HM-3 OPP Film Product Description: A white opaque OPP film with a proprietary cavitated core. HM-3 is designed for cold seal applications and is used as a surface print, monoweb, or as the inside of lamination. I..