Polymer Property : Film Tensile Strength at Yield, MD = 14.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 14.0 MPa
2030 psi
ISO 527-3
Polimeri Europa Riblene® FM 50 Low Density Polyethylene - Blown Film Extrusion
Riblene FM 50 is a low density polyethylene (LDPE) suitable for blown film extrusion. Riblene FM 50 is characterized by optimum optical properties and rigidity.Films manufactured with Riblene FM 50..
Film Tensile Strength at Yield, MD 14.0 MPa
2030 psi
ISO 527-3
Polimeri Europa Riblene® FM 53 Low Density Polyethylene - Blown Film Extrusion
Riblene FM 53 is a low density polyethylene (LDPE) with added slip and antiblocking agents, suitable for blown film extrusion. Riblene FM 53 is characterized by optimum optical properties and rigid..
Film Tensile Strength at Yield, MD 14.0 MPa
2030 psi
ISO 527
Premix Thermoplastics PRE-ELEC® CP 1317
PRE-ELEC CP 1317 is a conductive thermoplastic compound based on EVA. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC CP 1317 ..
Film Tensile Strength at Yield, MD 14.0 MPa
2030 psi
ASTM D882
ExxonMobil Escorene® LD-129 MDPE Cast Overwrap Film Resin  (discontinued **)
Data provided by the manufacturer, Exxon Chemical.A homopolymer film resin with good clarity and excellent stiffness. Film made from LD-129 can be used in overwrap applications and in push-through ..
Film Tensile Strength at Yield, MD 14.0 MPa
2030 psi
ASTM D882
SCG Chemicals EL-Leneâ„¢ L1810F Linear Low Density Polyethylene Film
Key Characteristics:High productivityGood optical propertiesContains 1600 ppm slip agent and 1900 ppm antiblocking agentRecommended Applications:Film for heavy duty bag, industrial bag, rice bag, su..
Film Tensile Strength at Yield, MD 14.0 MPa
2030 psi
ASTM D882
SCG Chemicals EL-Leneâ„¢ L1810FI Linear Low Density Polyethylene Film
Key Characteristics:High gloss and clarityContains 3200 ppm slip agent and 2400 ppm antiblocking agentRecommended Applications:Water-quench blown film for general purpose bags such as vegetable or f..
Film Tensile Strength at Yield, MD 14.0 MPa
2030 psi
ASTM D882
Chevron Phillips MarFlex® D139DK Metallocene Linear Low Density Polyethylene, Blown Film
This mLLDPE is tailored for applications that require:Excellent clarityExcellent glossExcellent toughnessExcellent heat sealTypical blown film applications include:Seal layer in coextrusionsHeavy du..
Film Tensile Strength at Yield, MD 14.0 MPa
2030 psi
ASTM D882
Chevron Phillips MarFlex® D139FK Metallocene Linear Low Density Polyethylene, Blown Film
This mLLDPE is tailored for applications that require:Excellent clarityExcellent glossExcellent toughnessExcellent heat sealTypical blown film applications include:Seal layer in coextrusionsHeavy du..
Film Tensile Strength at Yield, MD 14.0 MPa
2030 psi
ASTM D882
Chevron Phillips MarFlex® D143FK Metallocene Linear Low Density Polyethylene, Blown Film
This mLLDPE is tailored for applications that require:Excellent clarityExcellent glossExcellent toughnessExcellent heat sealTypical blown film applications include:Seal layer in coextrusionsHeavy du..
Film Tensile Strength at Yield, MD 14.0 MPa
2030 psi
at 2% offset; ASTM D882
ExxonMobil Pax-Plus™ 3204 Blown Film Resin
Pax-Plus 3204 is a rubber modified high density polyethylene film resin which is used primarily in film requiring good impact strength. It is specially formulated to provide easy tear in the machin..
Film Tensile Strength at Yield, MD 14.0 MPa
2030 psi
Dow Elite® 5110 Linear Low Density Polyethylene
5110 enhanced polyethylene resin is a copolymer produced via INSITE Technology from Dow Plastics. It offers unique combination of high modulus and excellent impact strength, allowing for downgaugin..