Polymer Property : Film Tensile Strength at Yield, MD = 1170 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 8.10 - 9.40 MPa
1170 - 1360 psi
Average value: 8.68 MPa Grade Count:4
Overview of materials for Ethylene Acrylic Acid
This property data is a summary of similar materials in the MatWeb database for the category "Ethylene Acrylic Acid". Each property range of values reported is minimum and maximum values of appropri..
Film Tensile Strength at Yield, MD 8.07 MPa
1170 psi
at 2% offset; ASTM D882
ExxonMobil LD 334.57 Clear, High Impact Film Resin
LD 334 resins produce films with superior impact strength, good heat sealability, and low temperature properties.Information provided by ExxonMobil Chemical
Film Tensile Strength at Yield, MD 8.07 MPa
1170 psi
at 2% offset; ASTM D882
ExxonMobil LD 334.82 Clear, High Impact Film Resin
LD 334 resins produce films with superior impact strength, good heat sealability, and low temperature properties.Information provided by ExxonMobil Chemical
Film Tensile Strength at Yield, MD 8.07 MPa
1170 psi
ASTM D882
Dow AFFINITY™ PL 1881G Polyolefin Plastomer (POP)
AFFINITY™ PL 1881G Polyolefin Plastomer (POP) is produced via INSITE™ Technologies. It is designed for use in a variety of packaging applications, including high-speed, form-fill-seal products.In..
Film Tensile Strength at Yield, MD 8.10 MPa
1170 psi
Dow Primacor® 1430 Ethylene Acrylic Acid (EAA)
Film properties below based on a film thickness of 60 µm. Data provided by Dow Chemical.