- Polymer Property : Tensile Strength, Yield = 310 MPa
Polymer Property : Tensile Strength, Yield = 310 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 310 MPa @Strain 1.00 % |
45000 psi @Strain 1.00 % |
EN min.,RT; EN 10002-1 |
| Outokumpu 4311 Cr-Ni Austenitic Stainless Steel Applications: Wet corrosion resistance and general service.Available in hot rolled plate (Quarto), hot rolled strip/sheet (CPP), cold rolled strip/sheet, cold rolled narrow strip, bar, and rod forms.. |
|||
| Tensile Strength, Yield | 310 MPa @Strain 1.00 % |
45000 psi @Strain 1.00 % |
Outokumpu Typical,Hot Rolled Plate (Quarto); EN 10002-1 |
| Outokumpu 4435 Cr-Ni-Mo Austenitic Stainless Steel Applications: Wet corrosion resistance and general service.Available in hot rolled plate (Quarto), hot rolled strip/sheet (CPP), cold rolled strip/sheet, cold rolled narrow strip, bar, and rod forms.. |
|||
| Tensile Strength, Yield | 310 MPa @Strain 0.200 % |
45000 psi @Strain 0.200 % |
Outokumpu Typical,Hot Rolled Plate (Quarto); EN 10002-1 |
| Outokumpu 4439 Austenitic Stainless Steel Applications: Wet corrosion resistance and general service.Available in hot rolled plate (Quarto), hot rolled strip/sheet (CPP), and cold rolled strip/sheet forms. |
|||
| Tensile Strength, Yield | 310 MPa @Strain 1.00 % |
45000 psi @Strain 1.00 % |
Outokumpu Typical,Hot Rolled Plate (Quarto); EN 10002-1 |
| Outokumpu 4571 Cr-Ni-Mo Austenitic Stainless Steel Very good corrosion resistance, weldable, and resistant to sensitization.Available in hot rolled plate (Quarto), hot rolled strip/sheet (CPP), cold rolled strip/sheet, cold rolled narrow strip, bar,.. |
|||
| Tensile Strength, Yield | 310 MPa @Strain 1.00 % |
45000 psi @Strain 1.00 % |
Outokumpu Typical,Hot Rolled Plate (Quarto); EN 10002-1 |
| Outokumpu 4845 High Temperature Austenitic Stainless Steel Standardized high-temperature steel for use at temperatures up to 1100°C in dry air. Prone to embrittlement after exposure between 600-900°C. Applications: Heat and creep resistance. For use o.. |
|||
| Tensile Strength, Yield | 310 MPa @Temperature 216 °C |
45000 psi @Temperature 420 °F |
0° Direction, Dry; ASTM D638 |
| Park Electrochemical Nelcote® E-720 Epoxy Prepreg, 7781 E-Glass Reinforced Nelcote® E-720 is a modified epoxy resin system designed to retain excellent mechanical properties after extended exposure to high temperature. E-720 has a proven history in many demanding aerospac.. |
|||
| Tensile Strength, Yield | 310 MPa @Temperature 216 °C |
45000 psi @Temperature 420 °F |
0° Direction, Dry, Autoclave; ASTM D638 |
| Park Electrochemical Nelcote® E-746 Epoxy Prepreg, 7781 E-Glass Reinforced Nelcote® E-746 is a modified epoxy resin system designed to retain excellent mechanical properties after extended exposure to high temperature. E-746 has a proven history in many demanding aerospac.. |
|||
| Tensile Strength, Yield | >= 310 MPa @Temperature 150 °C |
>= 45000 psi @Temperature 302 °F |
|
| PEAK Werkstoff DISPAL S226 Aluminum Alloy, AlSi30CuMg, Condition T6 Heat Treatment Condition T6 (Quench in water at RT)abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials allow the manufacturing of p.. |
|||
| Tensile Strength, Yield | 310 MPa @Thickness 1.57 mm |
45000 psi @Thickness 0.0620 in |
LW; ASTM D638 |
| Industrial Laminates/Norplex NP130 Glass Fabric Description: Woven glass fabric combined with a halogenated epoxy resin system. Produced to printed circuit board quality standards. Flame retardant, meets UL-94 flammability classification V-0.Thic.. |
|||
| Tensile Strength, Yield | 310 MPa @Thickness 1.57 mm |
44900 psi @Thickness 0.0620 in |
LW; ASTM D638 |
| Industrial Laminates/Norplex NP424 Laminate Description: Composite material composed of woven glass fabric surfaces and paper core combined with epoxy resin. Primarily used in the printed circuit board industry. Easy punching and excellent el.. |
|||
| Tensile Strength, Yield | 310 MPa @Strain 1.00 % |
45000 psi @Strain 1.00 % |
Typical |
| Industeel CLC 17.12.2 Ti Titanium Stabilized 18Cr-11Ni-2Mo Austenitic Stainless Steel CLC 17-12-2Ti is a Titanium stabilized austenitic stainless steel. 2% Molybdenum bearing ensures better corrosion resistance than CLC 18-9 L grade, particularly regarding to uniform and localized co.. |
|||
| Tensile Strength, Yield | >= 310 MPa @Strain 1.00 % |
>= 45000 psi @Strain 1.00 % |
|
| Industeel CLC 18.10 LN Nitrogen Containing 18Cr-10Ni Austenitic Stainless Steel Description: CLC 18.10LN is a 18Cr-10Ni austenitic stainless steel with specific Nitrogen additions. Its low carbon content avoids intergranular corrosion, even on welded pieces without an ulterior .. |
|||
| Tensile Strength, Yield | 310 MPa @Strain 1.00 % |
45000 psi @Strain 1.00 % |
Typical |
| Industeel CLC 18.10Ti Titanium-Stabilized 18Cr-10Ni Austenitic Stainless Steel CLC 18-10Ti is a 18Cr-9Ni austenitic stainless steel stabilized with some Titanium additions. This is a basic grades in the stainless steel range. Titanium bearing (carbide forming element) avoids i.. |
|||
| Tensile Strength, Yield | 310 MPa @Strain 0.200 % |
45000 psi @Strain 0.200 % |
Typical |
| Industeel NUCL 18.10 B4 Natural Boron (Min 1% wt) Alloyed 304 Stainless Steel Description: Isotope B10 has the property to capture neutrons produced by nuclear reactions. Natural boron contains about 19.9 at% or 18.45 wt % of B10 isotope, the remaining being B11 isotope. NUCL.. |
|||
| Tensile Strength, Yield | 310 MPa @Thickness 19.0 mm, Temperature 538 °C |
45000 psi @Thickness 0.750 in, Temperature 1000 °F |
0.2% offset |
| Haynes Ultimet® alloy, plate, GMAW weld (short) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Tensile Strength, Yield | 310 MPa @Thickness 12.7 mm, Temperature 538 °C |
45000 psi @Thickness 0.500 in, Temperature 1000 °F |
0.2% offset |
| Haynes Hastelloy® C-22® alloy, transverse, GTAW weldment, sheet - plate HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Tensile Strength, Yield | 310 MPa @Thickness 12.7 mm, Temperature 260 °C |
45000 psi @Thickness 0.500 in, Temperature 500 °F |
0.2% Offset |
| Haynes Hastelloy® G-35® Nickel Alloy Gas Tungsten Arc Welded (GTAW) Plate Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process†phosphoric acid, which is widely used in the production of fertilizers. Tests indicat.. |
|||
| Tensile Strength, Yield | >= 310 MPa @Strain 2.00 % |
>= 45000 psi @Strain 2.00 % |
bake hardening after 2% strain and heating to 170°C for 20 min. |
| SSAB Tunnplat Docol® 260 BH High-strength Steel High-strength SteelComments: Docol BH - Cold Rolled Steel - rephosphorized steel with bake hardening effect. Property values are for cold-rolled steel; thicknesses 0.40 - 2.0 mm. Iron content is ap.. |
|||
| Tensile Strength, Yield | 310 MPa @Strain 0.200 %, Temperature 20.0 °C |
45000 psi @Strain 0.200 %, Temperature 68.0 °F |
|
| Magnesium Elektron Elektron® 675 Magnesium Wrought Alloy High strength wrought Mg alloy used for high performance components, including at elevated temperature. Excellent corrosion resistance and easily machined. Can be extruded, forged and hot formed. .. |
|||
| Tensile Strength, Yield | 310 MPa @Strain 0.200 %, Thickness 20.0 - 80.0 mm |
45000 psi @Strain 0.200 %, Thickness 0.787 - 3.15 in |
Typical Strength |
| Constellium Planoxal® 60 Aluminum plate The advantage of Planoxal®-60 plates over other standard EN AW-6082 alloy products is their low level of internal stress. They are also suitable for technical anodizing. Planoxal®-60 is mainly use.. |
|||
| Tensile Strength, Yield | 310 MPa @Strain 0.200 % |
45000 psi @Strain 0.200 % |
|
| Crucible Steel 20 Cb Plus Stainless Steel Crucible 20 Cb Plus is a non-hardenable stabilized stainless steel with exceptional resistance to sulfuric, phosphoric, and nitric acid. This grade also has good resistance to stress corrosion crack.. |
|||
| Tensile Strength, Yield | 310 MPa @Strain 0.200 %, Thickness 60.0 - 140 mm |
45000 psi @Strain 0.200 %, Thickness 2.36 - 5.51 in |
Typical Strength |
| Constellium ALPLAN® 6082 Rolled Precision Aluminum Plate, Milled Both Sides Precision plates in ALPLAN® 6082 are milled on both sides and have a very low level of residual stress, thus avoiding excessive deformation during machining. Thanks to its very good dimensional sta.. |
|||
| Tensile Strength, Yield | 310 MPa @Strain 0.200 % |
45000 psi @Strain 0.200 % |
|
| ATI Allegheny Ludlum AL 453™ Stainless Steel Single phase iron-chromium ferritic stainless steel alloy. Should be annealed between 1450 and 1600°F and quickly cooled. Information provided by Allegheny Ludlum |
|||
| Tensile Strength, Yield | 310 MPa @Thickness 1.60 mm |
45000 psi @Thickness 0.0630 in |
LT Direction |
| Aleris AA5024-H116 Aluminum Magnesium Scandium Alloy Features good weldability, excellent damage tolerance, good corrosion resistance, creep-formability. Aleris AlMgSc alloy AA5024 H116 allows simplification of the manufacturing process of aircraft f.. |
|||
| Tensile Strength, Yield | 310 MPa @Thickness 12.7 mm, Temperature 538 °C |
45000 psi @Thickness 0.500 in, Temperature 1000 °F |
0.2% offset |
| Haynes Hastelloy® C-22® alloy, transverse, GTAW short arc weldment, plate HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| Tensile Strength, Yield | 310 MPa @Strain 0.200 %, Temperature 20.0 °C |
45000 psi @Strain 0.200 %, Temperature 68.0 °F |
Solution Annealed Tubing |
| Special Metals INCOLOY® alloy 803 Fe-Ni-Cr Alloy INCOLOY® alloy 803 (UNS S35045), an iron-nickel-chromium alloy, is designed for use in petrochemical, chemical and thermal processing applications. The nickel and chromium contents of alloy 803 ar.. |
|||