Polymer Property : Tensile Strength at Break = 2610 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	18.0 MPa @Treatment Temp. 25.0 Â°C, Time 259000 sec	2610 psi @Treatment Temp. 77.0 Â°F, Time 72.0 hour	Aged fuel C
LG Chemical NBR 3280 High Acrylonitrile Polymer Description: NBR 3280 is a copolymer of butadiene and acrylonitrile manufactured by cold emulsion polymerization technology of Goodyear Tire and Rubber Company, USA. NBR 3280 is a non staining, high..
Tensile Strength at Break	18.0 MPa @Temperature 100 Â°C, Time 259000 sec	2610 psi @Temperature 212 Â°F, Time 72.0 hour	Circulating Oven Aging
LG Chemical NBR 6840 High Acrylonitrile Polymer Description: NBR 6840 is a copolymer of butadiene and acrylonitrile manufactured by advanced emulsion polymerization technology of Goodyear and LG Chem. NBR 6840 is a non staining, medium low moon..
Tensile Strength at Break	18.0 MPa @Treatment Temp. 100 Â°C, Time 259000 sec	2610 psi @Treatment Temp. 212 Â°F, Time 72.0 hour	Aged ASTM D #3 Oil
LG Chemical NBR 6840 High Acrylonitrile Polymer Description: NBR 6840 is a copolymer of butadiene and acrylonitrile manufactured by advanced emulsion polymerization technology of Goodyear and LG Chem. NBR 6840 is a non staining, medium low moon..
Tensile Strength at Break	18.0 MPa @Temperature 175 Â°C, Time 2990 sec	2610 psi @Temperature 347 Â°F, Time 0.830 hour	Cured
LG Chemical NBR 7150 High Acrylonitrile Polymer Description: NBR 7150 is a copolymer of butadiene and acrylonitrile manufactured by cold emulsion polymerization technology of Goodyear Tire and Rubber Company, USA. NBR 7150 is a non staining, medi..