- Polymer Property : Tensile Strength at Break = 15200 psi
Polymer Property : Tensile Strength at Break = 15200 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 105 MPa @Temperature 175 °C |
15200 psi @Temperature 347 °F |
ISO 527 |
| Victrex® PEEK 150CA30 30% Carbon Fiber Reinforced Product Description: High performance thermoplastic material, 30% carbon fiber reinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection molding, easy flow, FDA food contact c.. |
|||
| Tensile Strength at Break | 105 MPa @Temperature 175 °C |
15200 psi @Temperature 347 °F |
ISO 527 |
| Victrex® PEEK 450CA40 Polyetheretherketone, 40% Carbon Fibre Reinforced Product Description:High performance thermoplastic material, 40% carbon fibre reinforced Polyetheretherketone (PEEK), semi crystalline, granules for injection moulding and extrusion, standard flow, .. |
|||
| Tensile Strength at Break | 105 MPa @Temperature 120 °C |
15200 psi @Temperature 248 °F |
|
| LATI Larton GCE/650 PPS, Glass/Mineral Reinforced Polyphenylene Sulfide (PPS) based compound. Glass fibers / Mineral filler. Very good chemical resistance. Very good thermal properties. Low smoke density and low toxicity index.Availability: Africa .. |
|||
| Tensile Strength at Break | 105 MPa @Temperature 120 °C |
15200 psi @Temperature 248 °F |
|
| LATI Larton GK/400 PPS, Glass/Carbon Fiber Reinforced Polyphenylene Sulfide (PPS) based compound. Glass fibers / Carbon fibers. Very good chemical resistance. Very good thermal properties. Low smoke density and low toxicity index.Availability: Africa &.. |
|||
| Tensile Strength at Break | 105 MPa @Temperature 90.0 °C |
15200 psi @Temperature 194 °F |
|
| LATI Larton K/20 PPS, 20% Carbon Fiber Reinforced Polyphenylene Sulfide (PPS) based compound. Carbon fiber. Very good chemical resistance. Very good thermal properties. Low smoke density and low toxicity index.Availability: Africa & Middle East; As.. |
|||
| Tensile Strength at Break | 105 MPa @Temperature 60.0 °C |
15200 psi @Temperature 140 °F |
|
| LATI Latamid 6 H2 G/30-V0HF1 PA 6, 30% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant Polyamide 6 (PA6) based compound. Heat stabilized. Glass fibers. UL94 V-0 classified, halogens-based flame retardants and red phosphorous free. Very good electrical properties.Availability: Africa &.. |
|||
| Tensile Strength at Break | 105 MPa @Temperature 150 °C |
15200 psi @Temperature 302 °F |
|
| LATI Latamid 6 H2 G/55 PA 6, 55% Glass Fiber Reinforced, Heat Stabilized Polyamide 6 (PA6) based compound. Heat stabilized. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termopla.. |
|||
| Tensile Strength at Break | 105 MPa @Temperature 90.0 °C |
15200 psi @Temperature 194 °F |
|
| LATI Latamid 66 H2 G/35-V0KB1 PA 66, 35% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant Polyamide 66 (PA66) based compound. Heat stabilized. Glass fibers. UL94 V-0 classified, with red phosphorous. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaIn.. |
|||
| Tensile Strength at Break | 105 MPa @Temperature 150 °C |
15200 psi @Temperature 302 °F |
|
| LATI Latamid 66 H2 K/40 PA 66, 40% Carbon Fiber Reinforced, Heat Stabilized Polyamide 66 (PA66) based compound. Heat stabilized. Carbon fiber.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termopl.. |
|||
| Tensile Strength at Break | 105 MPa @Temperature 23.0 °C |
15200 psi @Temperature 73.4 °F |
|
| LATI Lapex R G/10 PPSU, 10% Glass Reinforced Polyphenylene Sulfone (PPSU) based compound. Glass fibers. Low smoke density and low toxicity index. Very high dimensional stability.Availability: Africa & Middle East; Asia Pacific; Europe; Latin A.. |
|||
| Tensile Strength at Break | 105 MPa @Temperature 60.0 °C |
15200 psi @Temperature 140 °F |
|
| LATI Lapex R G/20 PPSU, 20% Glass Reinforced Polyphenylene Sulfone (PPSU) based compound. Glass fibers. Low smoke density and low toxicity index. Very high dimensional stability.Availability: Africa & Middle East; Asia Pacific; Europe; Latin A.. |
|||
| Tensile Strength at Break | 105 MPa @Temperature 60.0 °C |
15200 psi @Temperature 140 °F |
|
| LATI Laramid G/15 PPA, 15% Glass Fiber Reinforced Semi-aromatic polyamide (PPA) based compound. Glass fibers. Very good thermal properties. Good chemical resistance. Low moisture absorption.Availability: Africa & Middle East; Asia Pacific; Europe; .. |
|||
| Tensile Strength at Break | 105 MPa @Temperature 60.0 °C |
15200 psi @Temperature 140 °F |
|
| LATI Latamid 6 CUVHPX10 G/35 PA 6, 30% Glass Fiber Reinforced, Heat Stabilized Polyamide 6 (PA6) based compound. High viscosity. Toughened. Glass fibers. Heat stabilized. UV stabilized. Good elongation.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; No.. |
|||
| Tensile Strength at Break | 105 MPa @Temperature 120 °C |
15200 psi @Temperature 248 °F |
|
| LATI Latamid 6 H2 G/65 PA 6, 65% Glass Fiber Reinforced, Heat Stabilized Polyamide 6 (PA6) based compound. Heat stabilized. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termopla.. |
|||
| Tensile Strength at Break | 105 MPa @Temperature 60.0 °C |
15200 psi @Temperature 140 °F |
|
| LATI Latamid 66 H2 G/25-V0HF1 PA 66, 25% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant Polyamide 66 (PA66) based compound. Heat stabilized. Glass fibers. UL94 V-0 classified, halogens-based flame retardants and red phosphorous free. Very good mechanical properties. Very good electrica.. |
|||
| Tensile Strength at Break | 105 MPa @Temperature 60.0 °C |
15200 psi @Temperature 140 °F |
|
| LATI Latamid SP2 H2 G/35 PA 6.12, 35% Glass Fiber Reinforced, Heat Stabilized Polyamide 6.12 (PA6.12) based compound. Heat stabilized. Glass fibers. Low moisture absorption.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provi.. |
|||
| Tensile Strength at Break | 105 MPa @Temperature 23.0 °C |
15200 psi @Temperature 73.4 °F |
|
| LATI Latene® AG7H2 G/50 PP Homopolymer, 50% Glass Fiber Reinforced, Heat Stabilized Polypropylene homopolymer (PPh) based compound. Chemical grafting Heat stabilized. Glass fibers.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation prov.. |
|||
| Tensile Strength at Break | 105 MPa @Temperature 150 °C |
15200 psi @Temperature 302 °F |
|
| LATI Latilub 66-15T K/30 PA66, 30% Carbon Fiber Reinforced, PTFE Filled Self-lubricating product based on Polyamide 66 (PA66). PTFE. Carbon fiber. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industri.. |
|||
| Tensile Strength at Break | 105 MPa @Temperature 120 °C |
15200 psi @Temperature 248 °F |
|
| LATI Latamid 66 H2 G/35 PA 66, 35% Glass Fiber Reinforced, Heat Stabilized Polyamide 66 (PA66) based compound. Heat stabilized. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termop.. |
|||
| Tensile Strength at Break | 105 MPa @Temperature 120 °C |
15200 psi @Temperature 248 °F |
|
| LATI Latamid 66 H2 K/20 PA 66, 20% Carbon Fiber Reinforced, Heat Stabilized Polyamide 66 (PA66) based compound. Heat stabilized. Carbon fiber.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termopl.. |
|||