Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Adhesive Bond Strength | 24.1 MPa @Temperature 25.0 °C |
3500 psi @Temperature 77.0 °F |
Lap Shear |
Henkel Hysol PL 737 Film Adhesive Nonmetallic, modified epoxy film specifically designed for use in structural aircraft components. Low flow characteristics.Application: Metal and Honeycomb Bonding |
|||
Adhesive Bond Strength | >= 24.1 MPa @Temperature 93.0 °C |
>= 3500 psi @Temperature 199 °F |
Tensile Lap Shear |
Henkel Hysol EA 9380 Paste Adhesive System Cures at low temperature. Offers strength, toughness and high temperature resistance of heat-curing film adhesives, with greater flexibility and ease of use. Can be applied to large parts with contr.. |
|||
Adhesive Bond Strength | 24.1 MPa @Temperature 25.0 °C |
3500 psi @Temperature 77.0 °F |
Lap Shear |
Henkel Hysol EA 9689 Film Adhesive Modified epoxy film adhesive with high temperature strength and long-term thermal durability. Data from 0.10 psf, 500 g/m2.Applications: Composite Bonding Metal and Honeycomb Bonding |
|||
Adhesive Bond Strength | 24.1 MPa @Temperature -55.0 °C |
3500 psi @Temperature -67.0 °F |
Lap Shear |
Henkel Hysol PL 795 Film Adhesive Epoxy film adhesive designed for composite bonding applications. May cure at 250°F / 121°C or 350°F / 177°C, with service temperatures up to 350°F / 177°C. Ideal for co-cure or secondary bondi.. |
|||
Adhesive Bond Strength | 24.1 MPa @Temperature 25.0 °C |
3500 psi @Temperature 77.0 °F |
Tensile Lap Shear |
Henkel Hysol EA 9390 Paste Adhesive System Low viscosity system for high temperature wet lay-up composite repair. Qualified to BMS 8-301.Applications: Structural Bonding Low Viscosity Wet Lay-Up Composite Bonding |
|||
Adhesive Bond Strength | 24.1 MPa @Temperature 93.0 °C |
3500 psi @Temperature 199 °F |
Tensile Lap Shear |
Henkel Hysol EA 9394/C-2 Paste Adhesive System Elevated cure, thixotropic adhesive with structural properties to 450°F / 232°C.Application: Structural Repair |
|||
Adhesive Bond Strength | 24.1 MPa @Temperature 25.0 °C |
3500 psi @Temperature 77.0 °F |
Tensile Lap Shear |
Henkel Hysol EA 9396 Paste Adhesive System Two-part, low viscosity, unfilled version of Hysol EA 9394. Qualified to BMS 8-301.Applications: Structural Repair Low Viscosity Wet Lay-Up Composite Bonding |