- Polymer Property : Adhesive Bond Strength = 13.8 MPa
Polymer Property : Adhesive Bond Strength = 13.8 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Adhesive Bond Strength | 13.8 MPa @Temperature -55.0 °C |
2000 psi @Temperature -67.0 °F |
Lap Shear |
| Henkel Hysol EA 9673 (BMI) Film Adhesive Modified BMI film adhesive, superior strength to 550°F / 288°C. Moisture resistant, processes like conventional high temperature epoxies. Minimum order required. Data from 0.10 psf, 500 g / m2.. |
|||
| Adhesive Bond Strength | 13.8 MPa @Temperature 25.0 °C |
2000 psi @Temperature 77.0 °F |
Lap Shear |
| Henkel Hysol EA 9673 (BMI) Film Adhesive Modified BMI film adhesive, superior strength to 550°F / 288°C. Moisture resistant, processes like conventional high temperature epoxies. Minimum order required. Data from 0.10 psf, 500 g / m2.. |
|||
| Adhesive Bond Strength | 13.8 MPa @Temperature 121 °C |
2000 psi @Temperature 250 °F |
Lap Shear |
| Henkel Hysol EA 9696 Film Adhesive Second generation, moisture-resistant, toughened 250°F / 121°C service, modified epoxy film. Qualified to BMS 5-101 and BMS 5-129. Data from .060 psf, 300 g / m2.Applications: Composite Bondin.. |
|||
| Adhesive Bond Strength | 13.8 MPa @Temperature 93.0 °C |
2000 psi @Temperature 199 °F |
Tensile Lap Shear |
| Henkel Hysol EA 934NA Paste Adhesive System Two part adhesive system with superior strengthCures at room temperatureApplications: Potting Structural Repair Liquid Shim |
|||
| Adhesive Bond Strength | 13.8 MPa @Temperature 93.0 °C |
2000 psi @Temperature 199 °F |
Tensile Lap Shear |
| Henkel Hysol EA 9377 Paste Adhesive System Moldable plastic shim, excellent microcracking resistance under thermal cycling. High compressive strength.Application: Liquid Shim |
|||
| Adhesive Bond Strength | 13.8 MPa @Thickness 1.50 mm |
2000 psi @Thickness 0.0591 in |
Lap Shear (CRS St 1203); EN 1465 |
| Dow BETAMATE™ XW 1185 Epoxy BETAMATE™ XW 1185 is a one component heat curing Epoxy paste adhesive. The material is readily pumped at ambient temperatures. It shows excellent adhesion to automotive steel and aluminum, is resi.. |
|||
| Adhesive Bond Strength | 13.8 MPa @Temperature 23.9 °C |
2000 psi @Temperature 75.0 °F |
on steel; ASTM D1002-64 |
| 3M Pronto™ CA-9 Instant Adhesive One-part, room-temperature curing adhesive that is ready-to-use without metering or mixing. Bonded parts reach handling strength in 5-10 seconds on many applications.A slower setting version of CA-.. |
|||
| Adhesive Bond Strength | 13.8 MPa @Temperature 23.9 °C |
2000 psi @Temperature 75.0 °F |
on steel; ASTM D1002-64 |
| 3M Pronto™ CA-100 Instant Adhesive One-part, room-temperature curing adhesive that is ready-to-use without metering or mixing. Bonded parts reach handling strength in 5-10 seconds on many applications.Toughened material that provide.. |
|||
| Adhesive Bond Strength | 13.8 MPa @Temperature 23.9 °C |
2000 psi @Temperature 75.0 °F |
on steel; ASTM D1002-64 |
| 3M Pronto™ CA-5 Instant Adhesive One-part, room-temperature curing adhesive that is ready-to-use without metering or mixing. Bonded parts reach handling strength in 5-10 seconds on many applications.A high viscosity, slower settin.. |
|||
| Adhesive Bond Strength | 13.8 MPa @Temperature 23.9 °C |
2000 psi @Temperature 75.0 °F |
on steel; ASTM D1002-64 |
| 3M Pronto™ CA-50 Gel Instant Adhesive One-part, room-temperature curing adhesive that is ready-to-use without metering or mixing. Bonded parts reach handling strength in 5-10 seconds on many applications.A high-viscosity gel consistenc.. |
|||
| Adhesive Bond Strength | 13.8 MPa @Temperature 23.9 °C |
2000 psi @Temperature 75.0 °F |
on steel; ASTM D1002-64 |
| 3M Pronto™ CA-8 Instant Adhesive One-part, room-temperature curing adhesive that is ready-to-use without metering or mixing. Bonded parts reach handling strength in 5-10 seconds on many applications.Fast setting adhesive with exce.. |
|||
| Adhesive Bond Strength | 13.8 MPa @Temperature 100 °C |
2000 psi @Temperature 212 °F |
Lap Shear Strength vs. Aluminum |
| Aremco Corr-Paint™ CP2060 High Temperature Protective Coating Novolac-Epoxy, Silicon Carbide Filled This epoxy and urethane based coating is used for producing corrosion and wear resistant barriers to 500 °F. Typical applications include tanks, pipelines, boilers, precipitators, scrubbers, bag ho.. |
|||
| Adhesive Bond Strength | 13.8 MPa @Temperature 177 °C |
2000 psi @Temperature 351 °F |
Lap Shear |
| Henkel Hysol EA 9257 Primer Waterborne, corrosion-inhibiting primer, maintains surface bondability after multiple prebonding cure cycles. Meets SCAQMD Rule 1124. Replacement for Hysol EA 9210B.Applications: Sprayable Low Visc.. |
|||
| Adhesive Bond Strength | 13.8 MPa @Temperature -55.0 °C |
2000 psi @Temperature -67.0 °F |
Lap Shear |
| Henkel Hysol EA 9396.6MD Paste Adhesive System Cure syntactic, with excellent high temperature properties. Applications: Potting Syntactic |
|||
| Adhesive Bond Strength | 13.8 MPa @Temperature 121 °C |
2000 psi @Temperature 250 °F |
Lap Shear |
| Henkel Hysol EA 9628 Film Adhesive First generation, modified epoxy film, good stress, environmental resistance and structural propertiesApplications: Composite Bonding, Metal & Honeycomb BondingData from .060 psf, 300 g/m2 |
|||
| Adhesive Bond Strength | 13.8 MPa @Temperature 93.0 °C |
2000 psi @Temperature 199 °F |
Tensile Lap Shear |
| Henkel Hysol EA 9396/C-2 Paste Adhesive System Two-part, elevated cure, unfilled, low viscosity adhesive with structural properties to 400°F / 204°C.Applications: Structural Repair Low Viscosity Wet Lay-Up Composite Bonding |
|||
| Adhesive Bond Strength | 13.8 MPa @Temperature -55.0 °C |
2000 psi @Temperature -67.0 °F |
Tensile Lap Shear |
| Henkel Hysol EA 960F Paste Adhesive System Fast-set fairing and smoothing compound for exterior aircraft surfaces.Sandable after 6 hours |
|||