Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

Polymer Property : Tensile Strength at Break = 9200 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength at Break 63.4 MPa
9200 psi
2 in/min; ASTM D638
RheTech Products G20P100-00 20% Glass Fiber Reinforced Polypropylene, Natural
Applications: Arm rest insertVacuum canisterStorage binConsolesBattery traysInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break 63.4 MPa
9200 psi
2 in/min; ASTM D638
RheTech Products GC20P100-177UV 20% Glass Fiber Reinforced Polypropylene, Chemically Coupled, UV Stabilized, (Chrysler HS5) Gray
Applications: Air Ducts - distributionBracketsInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break 63.4 MPa
9200 psi
ASTM D638
Polymer Resources PPX-GP7 Modified-PPO, General Purpose
Modified-Polyphenylene Oxide, General Purpose, 300F HDTProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Informati..
Tensile Strength at Break 63.4 MPa
9200 psi
ASTM D638
Chase Plastics CP Pryme® PC100HFR Polycarbonate Molding Resin, High Flow, Mold Release
Information provided by Chase Plastics.
Tensile Strength at Break 63.4 MPa

@Temperature 22.8 °C
9200 psi

@Temperature 73.0 °F
ASTM D638
Ensinger NORYL® Polyphenylene oxide (PPO)
NORYL®, due to its inherent chemical composition, exhibits unusually low moisture absorption. Therefore, good electrical insulating properties are realized over a wide range of humidity and temper..
Tensile Strength at Break 63.4 MPa
9200 psi
Abatron AboCast 8503-4/AboCure 8503-4 Colorless Epoxy
AboCast 8503-4/AboCure 8503-4 is a general purpose, moderate speed, colorless epoxy casting compound with low viscosity. It offers a convenient 2/1 ratio by volume and lends itself to casting of thi..
Tensile Strength at Break 63.4 MPa
9200 psi
2 in/min; ASTM D638
RheTech Products GC20P100-01 20% Glass Fiber Reinforced Polypropylene, Chemically Coupled, Black
Applications: Air Ducts - distributionBracketsInjection molding conditions reported in table.Information provided by RheTech Products.