Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 5.00 MPa | 725 psi | ASTM D412 |
Multibase TPSiV™ 3040-55A Thermoplastic Silicone Vulcanizate These materials are a novel family of TPV products based on cross-linked silicone rubber dispersed into various engineering thermoplastics. The dispersion of the silicone internal phase is produced.. |
|||
Tensile Strength at Break | 5.00 MPa | 725 psi | ISO 37 |
PolyOne OnFlex™ S EH 60A-3S7003 Thermoplastic Elastomer (TPE) OnFlex™-S EH thermoplastic elastomer compounds are based on hydrogenated styrenic block copolymers. This range of compounds are formulated to deliver a great cost/performance ratio in addition to t.. |
|||
Tensile Strength at Break | <= 5.00 MPa | <= 725 psi | ISO/R527 |
Polykemi AB POLYelast TPE E606 Thermoplastic Elastomer, EPDM-based Information provided by Polykemi AB |
|||
Tensile Strength at Break | 5.00 MPa | 725 psi | ISO 37 |
Huntsman AVALON® 650 B Thermoplastic Polyurethane Performance Features: AVALON® injection molding products are trusted worldwide to deliver:Outstanding flex performanceExcellent slip resistancePerfect surface definitionTransparency and transluce.. |
|||
Tensile Strength at Break | 5.00 MPa | 725 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL WCP700 PPE-TPE (Asia Pacific) Flexible PPE-TPE injection grade suitable for over-molding applications such as plugs, strain relief's, and connectors. Good processability. 70 Shore A hardness. |
|||
Tensile Strength at Break | 5.00 MPa | 725 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL WCP700 PPE-TPE (Europe-Africa-Middle East) Flexible PPE-TPE injection grade suitable for over-molding applications such as plugs, strain relief's, and connectors. Good processability. 70 Shore A hardness. |
|||
Tensile Strength at Break | 5.00 MPa | 725 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP MX95318 PP LNP* THERMOCOMP* MX95318 is a compound based on Polypropylene containing Proprietary Filler(s). |
|||
Tensile Strength at Break | 5.00 MPa | 725 psi | ASTM D412 |
Teknor Apex Telcar® TL-2530F Thermoplastic Elastomer Uses: Automotive Applications; Automotive Exterior Parts; Automotive Exterior Trim; Automotive Interior Parts; Blow Molding Applications; General Purpose; Grommets; Weatherstripping Forms: Pellets .. |
|||
Tensile Strength at Break | 5.00 MPa | 725 psi | ASTM D638 |
ELASTO UK Dryflex® 500400S SEBS Based Material, Unfilled Qualities, 40A Hardness, Translucent The 500-seriesis very favorable when transparency and good scratch resistance are required, as well as when there are high surface finish requirements. Unfilled grades have excellent flow and mecha.. |
|||
Tensile Strength at Break | 5.00 MPa | 725 psi | ASTM D638 |
ELASTO UK Dryflex® 502400S SEBS Based Material, Unfilled Qualities, 40A Hardness, Black The 500-seriesis very favorable when transparency and good scratch resistance are required, as well as when there are high surface finish requirements. Unfilled grades have excellent flow and mecha.. |
|||
Tensile Strength at Break | 5.00 MPa | 725 psi | Across Flow; ASTM D412 |
ExxonMobil Santoprene® 121-58W175 Thermoplastic Elastomer A soft, black, UV resistant thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. This material combines good physical properties and chemical resistance, and is designed for .. |
|||
Tensile Strength at Break | >= 5.00 MPa | >= 725 psi | ISO R 527 |
Fainplast Compounds CR 0118 Flexible PVC, Electrical Bedding Easy strip bedding |
|||
Tensile Strength at Break | >= 5.00 MPa | >= 725 psi | ISO R 527 |
Fainplast Compounds CRKA 91 Flexible PVC, Flame Retardant Electrical Bedding Lead Free Flame retardant bedding |
|||
Tensile Strength at Break | 5.00 MPa | 725 psi | ISO R 527 |
Fainplast Compounds GS 39/T Flexible PVC, Injection Molding for Footwear Sandals |
|||
Tensile Strength at Break | 5.00 MPa | 725 psi | ISO 527-2 |
Ascend Performance Materials Vydyne® ECO315 BK13 Nylon 66, Flame Retardant, Conditioned Vydyne® ECO366 BK13 is a non-halogenated, unfilled, flame-retardant PA66 homopolymer designed with superior flow properties to assist in filling thin-walled, intricate parts. It is lubricated for m.. |
|||
Tensile Strength at Break | 5.00 MPa | 725 psi | ASTM D638 |
Arkema Group EVATANE® 42-60 Copolymer Ethylene - Vinyl Acetate EVATANE 42-60 is a random copolymer of Ethylene and Vinyl Acetate made by high-pressure radicalar polymerisation process. EVATANE 42-60 is stabilized with antioxidants and contains slip and antibloc.. |
|||
Tensile Strength at Break | 5.00 MPa | 725 psi | |
LATI Latimass 53-04 D008 PP Homopolymer, Impact Modified Specific density compound based on Polypropylene homopolymer (PPh), impact modified. Special filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation.. |