Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 67.6 MPa | 9800 psi | ASTM D638 |
Polymer Resources AH-GP1 Acetal Homopolymer, Low Flow, High Melt Strength, Heat Stabilized Process: Molding or ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation. |
|||
Tensile Strength at Break | 67.6 MPa | 9800 psi | ASTM D638 |
Polymer Resources AH-GP1-[color]-H Acetal Homopolymer, Low Flow, High Melt Strength, Heat Stabilized Process: Molding or ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
Tensile Strength at Break | 67.6 MPa | 9800 psi | ASTM D638 |
Polymer Resources AH-GP2 Acetal Homopolymer, Medium Flow, Heat Stabilized Process: Molding or ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation. |
|||
Tensile Strength at Break | 67.6 MPa | 9800 psi | ASTM D638 |
Polymer Resources AH-GP2-[color]-H Acetal Homopolymer, Medium Flow, General Purpose Molding, Heat Stabilized Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
Tensile Strength at Break | 67.6 MPa | 9800 psi | ASTM D638 |
Polymer Resources AH-GP3 Acetal Homopolymer, High Flow Resin, Heat Stabilized Process: Molding or ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation. |
|||
Tensile Strength at Break | 67.6 MPa | 9800 psi | ASTM D638 |
Parker Chomerics PREMIER™ A220-HT EMI Shielding Plastic Description: PREMIER™ is the world’s first and most versatile commercially available conductive thermoplastic for real world EMI shielding solutions. It is a blend of PC/ABS thermoplastic polymer .. |
|||
Tensile Strength at Break | 67.6 MPa | 9800 psi | ASTM D638 |
Polymer Resources AH-GP3-[color]-H Acetal Homopolymer, High Flow Resin, Heat Stabilized Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
Tensile Strength at Break | 67.6 MPa | 9800 psi | ASTM D638 |
Polymer Resources AH-GP3 Acetal Homopolymer, High Flow Resin
(Unverified Data**) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
Tensile Strength at Break | 67.6 MPa | 9800 psi | ASTM D 638 |
Shakespeare Isocorâ„¢ CN30XT Nylon 610 Isocorâ„¢ CN30XT is a low viscosity PA-610 based copolymer. This transparent nylon resin is specifically suited for applications requiring increased solvent resistance and UV stability. Isocor.. |
|||
Tensile Strength at Break | 67.6 MPa | 9800 psi | ASTM D638 |
Techmer ES Electrablend® PPS 06001 Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber ReinforcementFeatures: Electrically ConductiveInformation provided by TP Composites, Inc. |
|||
Tensile Strength at Break | 67.6 MPa @Temperature 22.8 °C |
9800 psi @Temperature 73.0 °F |
ASTM D638 |
Ensinger TECANYL™ MT Autoclavable Polymer TECANYL™ MT is a new family of autoclavable materials developed for medical device applications. The material offers the desired performance properties of PPSU based resins with the machining ease.. |
|||
Tensile Strength at Break | 67.6 MPa @Temperature 22.8 °C |
9800 psi @Temperature 73.0 °F |
ASTM D638 |
Ensinger TECANYL™ MT XRO Autoclavable Polymer TECANYL™ MT is a new family of autoclavable materials developed for medical device applications. The material offers the desired performance properties of PPSU based resins with the machining ease.. |
|||
Tensile Strength at Break | 67.6 MPa | 9800 psi | ASTM D638 |
Polymer Resources AH-GP1 Acetal Homopolymer, Low Flow, High Melt Strength
(Unverified Data**) Process: Molding or ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
Tensile Strength at Break | 67.6 MPa | 9800 psi | ASTM D638 |
Polymer Resources AH-GP2 Acetal Homopolymer, Medium Flow, General Purpose Molding
(Unverified Data**) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
Tensile Strength at Break | 67.6 MPa | 9800 psi | ASTM D 638 |
Shakespeare Isocor™ CN30BT Nylon 610 Isocor™ CN30BT is a medium viscosity PA-610 based copolymer. This transparent nylon resin is specifically suited for applications requiring increased solvent resistance and clarity. Isocor™ CN.. |