Polymer Property : Tensile Strength at Break = 64.1 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength at Break 64.1 MPa
9300 psi
2 in/min; ASTM D638
RheTech Products G20P100-01 20% Glass Fiber Reinforced Polypropylene, Black
Applications: Arm rest insertVacuum canisterStorage binConsolesBattery traysInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break 64.1 MPa
9300 psi
chs 2 in/min; ASTM D638
Network Polymers MS 110 Styrene Methyl Methacrylate Terpolymer
Description: Styrene Methyl Methacrylate TerpolymerInformation provided by Network Polymers Inc.
Tensile Strength at Break 64.1 MPa
9300 psi
ASTM D638
Polymer Resources PPX-FR3-[color]EN Modified PPO, UL 94 V-1 with HDT of 265 F, Extrusion Grade
Process: ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
Tensile Strength at Break 64.1 MPa
9300 psi
5.1 mm/min; ASTM D638
PolyOne Edgetek® AS-10GF/000 FR V0 BLACK Acrylonitrile Butadiene Styrene (ABS)
Information provided by PolyOne
Tensile Strength at Break 64.1 MPa
9300 psi
ASTM D638
Chase Plastics CP Pryme® NN300TL (Dry) Nylon 66, Lubricated, Impact Modified, Recycled Content
Features: Impact modifiedGood toughnessLubricatedRecycled ContentForm: PelletsInformation provided by Chase Plastics.
Tensile Strength at Break 64.1 MPa
9300 psi
ASTM D638
Chase Plastics CP Pryme® PC100R Polycarbonate Molding Resin, Mold Release
Information provided by Chase Plastics.
Tensile Strength at Break 64.1 MPa
9300 psi
ASTM D638
Chase Plastics CP Pryme® PC100RUV Polycarbonate, Mold Release, UV Stabilized
Information provided by Chase Plastics.
Tensile Strength at Break 64.1 MPa
9300 psi
ASTM D638
A. Schulman SCHULAMID® 66 PTFE20 HS 20% PTFE Lubricated, Heat Stabilized Nylon 6/6
Information provided by A. Schulman.
Tensile Strength at Break 64.1 MPa
9300 psi
ASTM D638
A. Schulman SCHULAMID® 66 PTFE20 HS 20% PTFE Lubricated, Heat Stabilized Nylon 6/6
Information provided by A. Schulman.
Tensile Strength at Break 64.1 MPa
9300 psi
ASTM D638
A. Schulman SCHULAMID® 66 PTFE20 HS 20% PTFE Lubricated, Heat Stabilized Nylon 6/6
Information provided by A. Schulman.
Tensile Strength at Break 64.1 MPa
9300 psi
ASTM D638
A. Schulman SCHULAMID® 66 PTFE20 HS 20% PTFE Lubricated, Heat Stabilized Nylon 6/6
Information provided by A. Schulman.
Tensile Strength at Break 64.1 MPa
9300 psi
ASTM D638
A. Schulman SCHULAMID® 66 PTFE20 HS 20% PTFE Lubricated, Heat Stabilized Nylon 6/6
Information provided by A. Schulman.
Tensile Strength at Break 64.1 MPa
9300 psi
ASTM D638
A. Schulman SCHULAMID® 66 PTFE20 HS 20% PTFE Lubricated, Heat Stabilized Nylon 6/6
Information provided by A. Schulman.
Tensile Strength at Break 64.1 MPa
9300 psi
ASTM D638
Polymer Resources PPX-FR3 Modified PPO, UL 94 V-1 with HDT of 265 F  (Unverified Data**)
Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.