Polymer Property : Tensile Strength at Break = 44.1 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength at Break 44.1 MPa
6400 psi
ASTM D638
Polymer Resources PC/TP-GP3 PC/Polyester Alloy
High Impact, Superior Chemical ResistanceProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by..
Tensile Strength at Break 44.1 MPa
6400 psi
ASTM D638
Albis Plastics Cellulose Acetate Butyrate B9024 (UVI, Odor Mask Added), 5% Plasticizer  (discontinued **)
Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and T..
Tensile Strength at Break 44.1 MPa
6400 psi
ASTM D638
Albis Plastics Cellulose Acetate Butyrate B902 (UV Inhibitor Added), 5% Plasticizer  (discontinued **)
Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and T..
Tensile Strength at Break 44.1 MPa
6400 psi
after 16 hours in 50°C water
Malvern Minerals Nylon with Novakup® L-337 Silane-Treated Quartz Filler
Product data demonstrates the effect of the Novakup® (lamellar quartz surface treated with A-1100) filler. A separate entry demonstrates the effect of untreated Novacite® filler in nylon. Th..
Tensile Strength at Break 44.1 MPa
6400 psi
2"/min; ASTM D638
Garland Manufacturing GAR-DUR® Ultra High Molecular Weight Polyethylene (UHMW-PE)
GAR-DUR® plastic parts are made from ultra high molecular weight (UHMW) polymer having a molecular weight of 4.2 million and greater. Garland Manufacturing Company has been processing UHMW resin ..
Tensile Strength at Break 44.1 MPa

@Thickness 2.00 mm
6400 psi

@Thickness 0.0787 in
50mm/min; ASTM D638
LG Chemical KEYFLEX BT 1068D Ester Type TPE
Description: Injection Molding, TPC-ET, General Purpose, High ModulusApplication: Injection Parts for Automotives, Leisure & SportsCAS: 37282-12-5Information provided by LG Chemical
Tensile Strength at Break 44.1 MPa

@Thickness 3.20 mm
6400 psi

@Thickness 0.126 in
50mm/min; ASTM D638
LG Chemical Lupox® SG3250M PBT+PET+MF25%
Description: Injection Molding, PBT+PET+MF25%, Good SurfaceApplication: Automotive (Head Lamp Bezel)CAS No. 24968-12-5, 25038-59-9 and 14807-96-6Information provided by LG Chemical
Tensile Strength at Break 44.1 MPa

@Thickness 3.20 mm
6400 psi

@Thickness 0.126 in
Injection Molded; ASTM D638
Styron EMERGEâ„¢ 7600 Polycarbonate (PC) / Acrylonitrile Butadiene Styrene (ABS)
Overview: EMERGEâ„¢ PC/ABS 7600 is an ignition-resistant PC/ABS blend that contains no chlorine or bromine additives. It combines the superior physical properties of PC & the excellent processabi..
Tensile Strength at Break 44.1 MPa
6400 psi
ASTM D638
Unitika elitel UE3203 Polyester, Pellet
High elongation type UE3200UNITIKA l resins are thermoplastic saturated copolymeric polyester resins. l resins are expanding their applications from products such as adhesives, paints, ink binders,..
Tensile Strength at Break 44.1 MPa
6400 psi
ASTM D638
Unitika elitel UE3250 Polyester, Pellet
High elongation type UE3240, Binder paint, Adhesive agentUNITIKA l resins are thermoplastic saturated copolymeric polyester resins. l resins are expanding their applications from products such as a..
Tensile Strength at Break 44.1 MPa
6400 psi
Abatron AboCast 8103-13 One-Component Epoxy
AboCast 8103-13 is the low-viscosity one-component clear epoxy system with deep impregnation that offers high performance at relatively high temperatures. It is best for thin-wall casting. Suggested..
Tensile Strength at Break 44.1 MPa
6400 psi
ASTM D638
Americas Styrenics STYRON® 610 High Heat Crystal Polystyrene
Product CharacteristicsAdditive freeTypical ApplicationsFoamsFilms/opticalCarrier resinSpecialty blendingInformation provided by AmericasStyrenics LLC.
Tensile Strength at Break 44.1 MPa
6400 psi
ASTM D638
Albis Plastics Cellulose Acetate Butyrate B9004 (Odor Mask Added), 5% Plasticizer  (discontinued **)
Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and T..
Tensile Strength at Break 44.1 MPa
6400 psi
50 mm/min; ASTM D638
Supreme Petrochem SP 6605 Toughened Polystyrene
Characteristics Excellent melt strength High stiffness Easy tearability Processing Extrusion Applications Suitable for thin film for candy wrap and window envelope Economic production of clear th..
Tensile Strength at Break 44.1 MPa
6400 psi
ASTM D638
Albis Plastics Cellulose Acetate Butyrate B900 (Base Grade), 5% Plasticizer  (discontinued **)
Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and T..
Tensile Strength at Break 44.1 MPa
6400 psi
2 in/min; ASTM D638
RheTech Products GC20P600-01UV 20% Glass Fiber Reinforced Polypropylene, Chemically Coupled, UV Stabilized, Black
Applications: Sun roof trimFan shroudInjection molding conditions reported in table.Information provided by RheTech Products.