Polymer Property : Tensile Strength at Break = 4120 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	28.4 MPa	4120 psi	2 in/min; ASTM D638
RheTech Products FT4600-00 Thermoplastic Polyolefin, Non-UV Stabilized, Natural Applications: Scuff platesInterior trimI/P componentsInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break	28.4 MPa	4120 psi	2 in/min; ASTM D638
RheTech Products FT4600-152 Thermoplastic Polyolefin, UV Stabilized, JA6A Black Applications: Scuff platesInterior trimI/P componentsInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break	28.4 MPa @Temperature 145 Â°C, Time 2100 sec	4120 psi @Temperature 293 Â°F, Time 0.583 hour	ASTM D412
LG Chemical SBR 1500 High Acrylonitrile Polymer Description: NSBR 1500 is a cold polymerized styrene-butadiene copolymer with staining stabilizer. The cold polymerized SBR exhibits better abrasion, higher tensile strength and higher modulus than ..
Tensile Strength at Break	28.4 MPa @Temperature 145 Â°C, Time 2100 sec	4120 psi @Temperature 293 Â°F, Time 0.583 hour	ASTM D412
LG Chemical SBR 1500H High Acrylonitrile Polymer Description: SBR 1500H is a cold polymerized styrene-butadiene copolymer with non-staining stabilizer and especially well-suited for adhesive applications. It has high internal strength, and excelle..
Tensile Strength at Break	28.4 MPa @Temperature 145 Â°C, Time 2100 sec	4120 psi @Temperature 293 Â°F, Time 0.583 hour	ASTM D412
LG Chemical SBR 1723 High Acrylonitrile Polymer Description: SBR 1723 is an oil extended cold polymerization SBR with 37.5 parts of Low PCA (PolyCyclic Aromatic) oil and styrene-butadiene copolymer of 23.5% bound styrene. Raw materials for this p..
Tensile Strength at Break	>= 28.4 MPa	>= 4120 psi
Sibur SKI-3 1st Grade, 2nd Group Isoprene Rubber (IR) Nipol-IR 2200, Natsyn-2200, Kraton-IR 401. For production of tires and rubber technical articles of wide assortment.
Tensile Strength at Break	>= 28.4 MPa	>= 4120 psi
Sibur SKI-3 1st Grade, 3rd Group Isoprene Rubber (IR) Nipol-IR 2200, Natsyn-2200, Kraton-IR 401. For production of tires and rubber technical articles of wide assortment.
Tensile Strength at Break	28.4 MPa	4120 psi	5 mm/min; ASTM D638
Samsung Cheil Industries StarexÂ® VE-0852 ABS, Unreinforced FR Information provided by Samsung Cheil Industries.
Tensile Strength at Break	28.4 MPa @Treatment Temp. 145 Â°C, Time 2100 sec	4120 psi @Treatment Temp. 293 Â°F, Time 0.583 hour	Cure; ASTM D412
Styron BunaÂ® SB 1502 Schkopau Cold Polymerized Emulsion Styrene Butadiene Rubber (E-SBR) Composition: BunaÂ® SB 1502 â€“ Schkopau is manufactured by cold polymerization using mixed rosin acid /fatty acid soaps. A non-discoloring stabilizer is added during the production process.App..
Tensile Strength at Break	28.4 MPa	4120 psi	5 mm/min; ASTM D638
Samsung Cheil Industries StarexÂ® VE-0852 ABS, Unreinforced FR Information provided by Samsung Cheil Industries.
Tensile Strength at Break	28.4 MPa	4120 psi	50 mm/min; ASTM D638
Supreme Petrochem SH 400 M High Impact Polystyrene Characteristics High gloss Easy flow Processing MoldingApplications Air conditioner and cooler grills, refrigerator components Toys, use and throw camera, household articles Ball pen barrels, nov..
Tensile Strength at Break	28.4 MPa	4120 psi	50 mm/min; ASTM D638
Supreme Petrochem SH 731 High Impact Polystyrene Characteristics Medium flow High Impact Excellent formability Low temperature toughnessProcessing Extrusion Molding FormingApplications Thermoformed containers, extruded profiles, packaging pro..
Tensile Strength at Break	28.4 MPa	4120 psi	50 mm/min; ASTM D638
Supreme Petrochem SP 562 Flame Retardant Polystyrene Characteristics Very good flow properties Free of DBDPO, PBDE & TBBA, complies with ROHS directive of EU Low specific gravity Processing Injection moldingApplications Large size T.V. Cabinets Aud..