Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 25.0 - 27.0 MPa | 3630 - 3920 psi | ASTM D683 |
Loxim 820 02C HB Polypropylene Compound, 20% Calcite Filled, Flame Retardant Information provided by Loxim Industries |
|||
Tensile Strength at Break | 25.0 - 27.0 MPa | 3630 - 3920 psi | ASTM D683 |
Loxim 830 02T V0 Polypropylene Compound, 30% Talc Filled, Flame Retardant Information provided by Loxim Industries |
|||
Tensile Strength at Break | 20.0 - 27.0 MPa | 2900 - 3920 psi | ASTM D638 |
Arkema Group KYNAR FLEX® 2950-05 Polyvinylidene Fluoride Copolymer - Extrusion & Molding Characteristics: Natural resin - translucent, off-white hemispheres. Very flexible, flame and smoke suppressant. High stability in harsh thermal, chemical and ultraviolet environments. High toug.. |
|||
Tensile Strength at Break | 20.0 - 27.0 MPa | 2900 - 3920 psi | ASTM D638 |
Arkema Group KYNAR FLEX® 2750-01 Polyvinylidene Fluoride Copolymer - Extrusion & Molding Characteristics: Natural resin - translucent, off-white hemispheres. Very flexible, lubricated. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechani.. |