Polymer Property : Tensile Strength at Break = 3750 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	25.9 MPa	3750 psi	2 in/min; ASTM D638
RheTech Products T20P200-01BG 20% Talc Reinforced Polypropylene Copolymer, General Purpose Black, Blow Molding Grade Applications: HVAC ductsSeat backsInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break	25.9 MPa	3750 psi	chs 2 in/min; ASTM D638
Network Polymers NPP 50-2753 Description: High Density Polyethylene (HDPE)Information provided by Network Polymers Inc.
Tensile Strength at Break	25.9 MPa	3750 psi	ASTM D638
Plastics Group Polifil® RMT-40 40% Talc-Reinforced Polypropylene, High Impact Polifil® RMT series compounds are high impact polypropylenes reinforced with asbestos-free talc. In addition to high impact strength, they possess a high flex modulus and high heat deflection resis..
Tensile Strength at Break	25.9 MPa	3750 psi	ASTM D412
Teknor Apex Uniprene® UN-2420H Thermoplastic Vulcanizate Notes: Injection Rate: Fast Uses: Expansion Joint; Grommets; Tubing; Gaskets; Plugs; Weatherstripping; Glazing; Shock Absorbing Pads Forms: Pellets Processing Method: Extrusion; Injection Molding Ex..
Tensile Strength at Break	25.9 MPa	3750 psi	ASTM D3759
3M Scotch® 2364 Performance Masking Tape Scotch® Performance Masking Tape 2364 is a tan colored crepe paper masking tape for general masking applications in the industrial market where good holding power and temperature performance is req..
Tensile Strength at Break	25.9 MPa	3750 psi	ASTM D638
Plastics Group Polifil® RMT-40V 40% Talc-Reinforced Polypropylene, High Impact, UV Stabilized Polifil® RMT-V series compounds are high impact, UV stabilized polypropylenes reinforced with asbestos-free talc. In addition to high impact strength, they possess a high flex modulus and the abili..