Polymer Property : Tensile Strength at Break = 3650 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength at Break 25.2 MPa
3650 psi
2 in/min; ASTM D638
RheTech Products P250-00 Polypropylene Copolymer, Natural
Applications: ConsolesComponent housingsInterior componentsInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break 25.2 MPa
3650 psi
2 in/min; ASTM D638
RheTech Products P250-00UV Polypropylene Copolymer, UV Stabilized, Natural
Applications: ConsolesConsumer goodsInterior componentsInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break 25.2 MPa
3650 psi
2 in/min; ASTM D638
RheTech Products P250-247 Polypropylene Copolymer, UV Stabilized, Black
Applications: Center consolesInterior trimI/P componentsInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break 25.2 MPa
3650 psi
2 in/min; ASTM D638
RheTech Products P251-00 Polypropylene Copolymer, Natural
Applications: Fuse panel coversCenter consolesDoor panelsInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break 25.2 MPa
3650 psi
2 in/min; ASTM D638
RheTech Products P254-00 Polypropylene Copolymer, Natural
Applications: Air ducts - distributionInterior trimI/P componentsElectrical housingsInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break 25.2 MPa
3650 psi
2 in/min; ASTM D638
RheTech Products P256-00 Polypropylene Copolymer, Natural
Applications: Door/trunk scuffUnderhood componentsSplash shieldsElectrical enclosuresInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break 25.2 MPa
3650 psi
2 in/min; ASTM D638
RheTech Products P256-670UV Polypropylene Copolymer, UV Stabilized, 134B Stone
Applications: Interior trimElectrical housingsInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break 25.2 MPa
3650 psi
2 in/min; ASTM D638
RheTech Products P256-674UV Polypropylene Copolymer, UV Stabilized, 447B Fawn
Applications: Interior trimElectrical housingsInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break 25.2 MPa
3650 psi
2 in/min; ASTM D638
RheTech Products P256-762 Polypropylene Copolymer, Medium Grey
Applications: Misc. ClipsElectrical housingInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break 25.2 MPa
3650 psi
ASTM D638
Resirene Resirene® 9720 High Impact Polystyrene
Features:Medium FlowHigh Thermal ResistantMechanical StrengthFDA Rating: 21 CFR 177.1640Applications:Extrusion/ThermoformingInjectionDisposablesGPPS/HIPS BlendsInformation provided by US distributor..
Tensile Strength at Break 25.2 MPa
3650 psi
2 in/min; ASTM D638
RheTech Products HP513-00A High Performance Polypropylene Copolymer, Non-UV Stabilized, Natural
Applications: Interior trimI/P componentsCenter consolesInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break 25.2 MPa
3650 psi
Type IV specimen, compression molded, crosshead speed 2 in/min; ASTM D638
DuPont Nucrel® 2906 Ethylene-Methacrylic Acid Copolymer Resin  (discontinued **)
Nucrel® 2906 is a tough, lightweight, easily processed ethylene copolymer resin. This resin is inherently flexible without the need for plasticizers. The resin can be pigmented, UV-stabilized for..
Tensile Strength at Break 25.2 MPa
3650 psi
ASTM D638
M. Holland Company PS20 Polystyrene, Ignition Resistant  (discontinued **)
Additives: Ignition ResistantFeatures: Flame RetardantUses: Appliance Components, Business Equipment, Electrical/Electronic ApplicationsApprovals: FDA 21 CFR 177.1520Processing Method: Injection Mol..
Tensile Strength at Break 25.2 MPa
3650 psi
Type IV, 510 mm/min; ASTM D638
PolyOne Geon™ Vinyl Flexible P512 Polyvinyl Chloride, Flexible (PVC, Flexible)
Information provided by PolyOne
Tensile Strength at Break 25.2 MPa

@Temperature 145 °C,
Time 2100 sec
3650 psi

@Temperature 293 °F,
Time 0.583 hour
ASTM D412
LG Chemical SBR 1723H High Acrylonitrile Polymer
Description: SSBR 1723H is an oil extended cold polymerization SBR with 37.5 parts of Low PCA (PolyCyclic Aromatic) oil and styrene-butadiene copolymer of 23.5% bound styrene. Raw materials for this..
Tensile Strength at Break 25.2 MPa
3650 psi
ASTM D4745
3M Dyneon™ CC132 Custom Fluoropolymer Compound  (discontinued **)
This compound consists of a 10% carbon filled PTFE.Information provided by Dyneon, A 3M Company