Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 24.1 MPa | 3500 psi | UL 1581 |
PolyOne OnFlex™ AW 300-02 Thermoplastic Elastomer (TPE) OnFlex™ AW 300-02 is a non-halogen flame retardant material designed for appliance wire applications. New Product. Commercial specifications have not been established.Purge thoroughly before and af.. |
|||
Tensile Strength at Break | 24.1 MPa | 3500 psi | 2 in/min; ASTM D638 |
RheTech Products M25UVP250-01 25% Mica Reinforced Polypropylene Copolymer, UV Stabilized, Black Applications: BracketsCowl screensRigid exterior componentsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | >= 24.1 MPa | >= 3500 psi | ASTM D638 |
Niche Polymer PPCM6BK Copolymer PP Information provided by Niche Polymer |
|||
Tensile Strength at Break | 24.1 MPa | 3500 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible 90046 Polyvinyl Chloride, Flexible (PVC, Flexible) Automotive OEM approval(s).Information provided by PolyOne |
|||
Tensile Strength at Break | 24.1 MPa | 3500 psi | ASTM D638 |
Albis Plastics Cellulose Acetate Butyrate B9024 (UVI, Odor Mask Added), 16% Plasticizer
(discontinued **) Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and T.. |
|||
Tensile Strength at Break | 24.1 MPa | 3500 psi | 50 mm/min; ASTM D638 |
LyondellBasell Alathon® M4855 High Density Polyethylene, Injection Molding Grade ALATHON M4855 is a high density copolymer for use in injection molding applications. It exhibits excellent impact, warp and environmental stress crack resistance. Typical applications for M4855X01 a.. |
|||
Tensile Strength at Break | 24.1 MPa | 3500 psi | ASTM D638 |
LyondellBasell Alathon® M5370WC High Density Polyethylene ApplicationsALATHON M 5370WC is a natural, high density, polyethylene copolymer resin with a narrow molecular weight distribution formulated for use as primary insulation for coaxial and control cab.. |
|||
Tensile Strength at Break | 24.1 MPa | 3500 psi | ASTM D638 |
Teknor Apex APEX® 60001 Polyvinyl Chloride, Flexible Notes: 75°C Insulation; RoHS Compliant Features: Flame Retardant Uses: Communication Wire InsulationAgency Ratings: NEC Article 725; NEC Article 760; NEC Article 770; NEC Article 800; UL 13; UL 1.. |
|||
Tensile Strength at Break | 24.1 MPa | 3500 psi | ASTM D638 |
A. Schulman POLYTROPE™ TPP 512 Injection Molding Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 512 is an injection molding grade olefinic thermoplastic elastomer. This product has excellent low temperature impact properties and flow characteristics suitable for moldi.. |
|||
Tensile Strength at Break | 24.1 MPa | 3500 psi | at max load; ASTM D638 |
A. Schulman PP 1277A-01 Polypropylene High-Impact Polypropylene DescriptionPolypropylene PP 1277A is a low-flow, high-impact polypropylene for film, profile, tubing and coating.Information provided by A. Schulman. |
|||
Tensile Strength at Break | 24.1 MPa | 3500 psi | ASTM D412 |
Teknor Apex Telcar® TL-2683B Thermoplastic Elastomer Uses: Automotive Applications; Automotive Exterior Parts; Automotive Exterior Trim; Automotive Interior Parts; Blow Molding Applications; General Purpose; Grommets; Weatherstripping Forms: Pellets .. |
|||
Tensile Strength at Break | >= 24.1 MPa | >= 3500 psi | |
Master Bond LED401 White One Part, LED Curable Compound Description: Master Bond LED401 White is a one part LED type system that cures fully upon exposure to a 405 nm wavelength light source where the presence of any UV light is minimal or incidental. In.. |
|||
Tensile Strength at Break | 24.1 MPa | 3500 psi | ASTM D638 |
Plastics Group Polifil® RMC-40 40% Calcium Carbonate-Reinforced Polypropylene, High Impact Polifil® RMC series compounds are high impact polypropylenes reinforced with fine particle size calcium carbonate. In addition to the highest impact possible, they possess good stiffness, heat agin.. |
|||
Tensile Strength at Break | 24.1 MPa | 3500 psi | ASTM D638 |
A. Schulman POLYTROPE™ TPP 512 Injection Molding Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 512 is an injection molding grade olefinic thermoplastic elastomer. This product has excellent low temperature impact properties and flow characteristics suitable for moldi.. |
|||
Tensile Strength at Break | 24.1 MPa | 3500 psi | ASTM D638 |
A. Schulman POLYTROPE™ TPP 512 Injection Molding Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 512 is an injection molding grade olefinic thermoplastic elastomer. This product has excellent low temperature impact properties and flow characteristics suitable for moldi.. |
|||
Tensile Strength at Break | 24.1 MPa | 3500 psi | PVC (50)/CP80AS2(50) |
Lubrizol Estane® CP80AS2 Thermoplastic Polyurethane Type: Estane® CP80AS2 is a soft, polyester based thermoplastic polyurethane resin.Features: Outstanding compatibility with flexible PVC allowing easy dispersion without pre-compounding.Uses: Tube/H.. |
|||
Tensile Strength at Break | 24.1 MPa | 3500 psi | ASTM D638 |
Chesterton MRS S4+ Metal Rebuilding System An advanced polymer composite formulated to protect equipment from extreme chemical attack and corrosion. It is typically applied by spray, roller or brush at a nominal thickness of 375 microns (15 .. |
|||
Tensile Strength at Break | 24.1 MPa | 3500 psi | ASTM D638 |
ExxonMobil HD 9856B Blow Molding Resin Product Description: HD 9856B is a HDPE blow molding resin designed for high performance packaging applications. Containers made from HD 9856B exhibit a unique combination of stiffness and environme.. |
|||
Tensile Strength at Break | 24.1 MPa | 3500 psi | ASTM D638 |
Ravago Manufacturing Americas Echo® RPEHD BK HDPE Available in North AmericaDescription: Fractional Melt Recycled Content: Yes Color: Black Form: Pellets Information provided by Entec |
|||
Tensile Strength at Break | 24.1 MPa | 3500 psi | ASTM D638 |
Albis Plastics Cellulose Acetate Butyrate B9004 (Odor Mask Added), 16% Plasticizer
(discontinued **) Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and T.. |
|||
Tensile Strength at Break | 24.1 MPa @Temperature 175 °C |
3500 psi @Temperature 347 °F |
ISO 527-2 |
Solvay Specialty Polymers Amodel® A-1240 L Polyphthalamide (PPA)
(discontinued **) Amodel A-1240 L is a 40% mineral filled polyphthalamide (PPA) that offers low warpage and excellent dimensional stability. This resin also has a high deflection temperature, flexural modulus and ten.. |
|||
Tensile Strength at Break | 24.1 MPa | 3500 psi | ASTM D412 |
DuPont Performance Polymers Kalrez® 3065 Fluoroelastomer DuPont™ Kalrez® 3065 is a highly-filled product containing carbon black and fiber reinforcement, designed to function without extrusion under extreme pressure. It has good all round chemical resis.. |
|||
Tensile Strength at Break | 24.1 MPa | 3500 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Wire & Cable W1349L-xx05FRD Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications. Provisional Product Information - Physical and Mechanical properties based on initial production.Information provide.. |
|||
Tensile Strength at Break | 24.1 MPa | 3500 psi | ASTM D638 |
Chase Plastics CP Pryme® PPC100-8M Polypropylene Copolymer Information provided by Chase Plastics. |
|||
Tensile Strength at Break | 24.1 MPa | 3500 psi | TM R050-36 |
Resinlab® EP1046FG Black Electronic Grade Epoxy Encapsulant Resinlab™ EP1046FG Black is a two part unfilled very fast curing electronic grade epoxy encapsulant designed for small castings (less than 25 grams). It cures very quickly with low exotherm to a to.. |
|||
Tensile Strength at Break | 24.1 MPa | 3500 psi | TM R050-36 |
Resinlab® EP1046FG Clear Electronic Grade Epoxy Encapsulant Resinlab™ EP1046FG Clear is a two part unfilled very fast curing electronic grade epoxy encapsulant designed for small castings (less than 25 grams). It cures very quickly with low exotherm to a to.. |
|||
Tensile Strength at Break | 24.1 MPa | 3500 psi | ASTM D638 |
PlastxWorld DAICEL STYROL® GW50 HIPS UV stable flame retarded HIPSThese are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld Inc. |