Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 24.0 MPa | 3480 psi | |
Plastcom SLOVALEN EQ 18 N PP, basic type FeaturesModified PE with special heat and processional stabilization. Application in extrusion of profiles and pipes, blowing of bottles and jerrycans. Delivered in black colour.Packaging, transport.. |
|||
Tensile Strength at Break | 24.0 MPa | 3480 psi | 50 mm/min; ISO 527 |
Polimeri Europa Edistir R 850E Polystyrene Super high impact polystyrene with good heat resistance. Designed for sheet extrusion and thermoforming of deep drawn containers even
diluted with high percentage of GP. Suitable for general injecti.. |
|||
Tensile Strength at Break | 24.0 MPa | 3480 psi | 50 mm/min; ISO 527 |
Polimeri Europa Edistir RT 441M Polystyrene High impact polystyrene combining high toughness and high stiffness with good flowability for easy processing. Designed for injection moulding of technical parts, housings and covers.
Especially rec.. |
|||
Tensile Strength at Break | <= 24.0 MPa | <= 3480 psi | ISO/R527 |
Polykemi AB POLYfill PP CIP6015F Polypropylene, Mineral Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | <= 24.0 MPa | <= 3480 psi | ISO/R527 |
Polykemi AB POLYfill PPC T3020 Polypropylene Copolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | <= 24.0 MPa | <= 3480 psi | ISO/R527 |
Polykemi AB POLYfill PP CIP6015F VTUV Polypropylene, Mineral Reinforced, Heat and UV Stabilized Information provided by Polykemi AB |
|||
Tensile Strength at Break | 24.0 MPa | 3480 psi | ISO 527-2 |
Total Lacqrene® 4241 High Impact Polystyrene
(discontinued **) DescriptionLACQRENE® 14240 is a high heat resistance, high impact polystyrene for the extrusion industry. Good mechanical and thermal properties leads to the production of thermoformed articles of.. |
|||
Tensile Strength at Break | 24.0 - 26.0 MPa | 3480 - 3770 psi | ASTM D683 |
Loxim 831 02T HB Polypropylene Compound, 30% Talc Filled, Flame Retardant Information provided by Loxim Industries |
|||
Tensile Strength at Break | 24.0 - 26.0 MPa | 3480 - 3770 psi | ASTM D683 |
Loxim 841 02T HB Polypropylene Compound, 40% Talc Filled, Flame Retardant Information provided by Loxim Industries |
|||
Tensile Strength at Break | 24.0 MPa | 3480 psi | ISO 527 |
Lubrizol Advanced Materials Pearlbond® 12C75 Thermoplastic Polyurethane Pearlbond® 12C75 is polyester-based thermoplastic polyurethane, supplied in form of colourless, translucent granules, combining hardness with excellent low-temperature flexibility and a low softe.. |
|||
Tensile Strength at Break | 24.0 MPa | 3480 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-KON AX01706 ABS LNP* STAT-KON* AX01706 is a compound based on ABS containing proprietary fillers. Added feature of this grade is: Electrically Conductive. |
|||
Tensile Strength at Break | 24.0 MPa | 3480 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Stat-kon TD000 LNP* Stat-kon* TD000 is a compound based on Polyurethane resin. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 24.0 MPa | 3480 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-LOY A3000T ABS LNP* STAT-LOY A3000T is a compound based on ABS. Added features of this grade include: Antistatic, Clear. |
|||
Tensile Strength at Break | 24.0 MPa | 3480 psi | ASTM D 638 |
SABIC Innovative Plastics LNP Stat-loy A3000Z ABS LNP* Stat-loy* A3000Z is a compound based on Acrylonitrile Butadiene Styrene resin containing Anti-Static. Added features of this material include: Antistat.This data was supplied by SABIC-IP for t.. |
|||
Tensile Strength at Break | >= 24.0 MPa | >= 3480 psi | |
Sibur Nitrilast-26 Nitrile-Butadiene Rubber (NBR) 2895 BAYER. For production of oil-benzene resistant articles for the automobile, aviation and rubber technical industries. Rubbers on the base of Nitrilast possess good oil-benzene resistance. Ru.. |
|||
Tensile Strength at Break | 24.0 MPa | 3480 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL HIPS3190 HIPS Complies with FDA Regulation 21 CFR 177.1640 for rubber modified polystyrene. HB rating from 0.062-0.125"" pending. Natural only. |
|||
Tensile Strength at Break | 24.0 MPa | 3480 psi | ASTM D638 |
Total PS CPDS 814 UV Stabilized, Flame Retardant Polystyrene Total Petrochemicals Polystyrene 814 is a heat resistant, UV stabilized V0 Non Deca Polystyrene for injection molding. It is recommended for the manufacturing of articles which require good dimensi.. |
|||
Tensile Strength at Break | 24.0 MPa | 3480 psi | ASTM D638 |
Eastman Eastar GN119 Copolyester Applications:Personal care and CosmeticsProduct Description: Eastar GN119 Copolyester is a low-I.V. PETG, for sale only in Asia as a high-flow formulation. This product has been GREENGUARD INDOOR .. |
|||
Tensile Strength at Break | 24.0 MPa | 3480 psi | ASTM D638 |
Eastman Eastar MN059 Copolyester Eastar copolyesters are brilliantly clear polymers that have excellent impact strength, chemical resistance, dimensional stability, and low shrinkage rates. Eastar MN059 Copolyester is a medical gra.. |
|||
Tensile Strength at Break | 24.0 MPa | 3480 psi | ASTM D 638 |
Cossa Polimeri ESTADIENE 4009 Acrylonitrile Butadiene Styrene ABS with high impact resistanceHigh impact resistance at low temperature, high gloss, good processabilityInformation provided by Cossa Polimeri S.r.l. |
|||
Tensile Strength at Break | 24.0 MPa | 3480 psi | 50 mm/min; ISO 527 |
Chi Mei Polyrex® PH-88S Polystyrene - Extrusion Extrusion |
|||
Tensile Strength at Break | >= 24.0 MPa | >= 3480 psi | ISO R 527 |
Fainplast Compounds HL 100/2 Flexible PVC, Insulation for High Temperatures Operating temperature 80°C |
|||
Tensile Strength at Break | 24.0 MPa | 3480 psi | ASTM-D638 |
Braskem RD34U3 LLDPE Rotomolding Polyethylene The resin RD34U3 is a linear low-density polyethylene, 1-butene based, with excellent processability and a good balance of stiffness and impact strength. It contains long term UV6 stabilization and .. |
|||
Tensile Strength at Break | 24.0 MPa | 3480 psi | ASTM D412 |
Alliance Polymers Zythane™ 6070A Thermoplastic Polyurethane Elastomer Zythane™ 6070A is a polycaprolactone-based TPU specifically formulated for injection molding applications .It exhibits excellent low compression set, abrasion resistance and toughness and has good .. |
|||
Tensile Strength at Break | 24.0 MPa | 3480 psi | ASTM D638 |
3M Scotchkote™ 162HB Epoxy Coating 3M Scotchkote Epoxy Coating 163HB has been specifically developed as a 100% solids lining for the internals of pipes, tanks, vessels and other equipment in contact with fresh water, sea water, raw w.. |
|||
Tensile Strength at Break | 24.0 MPa | 3480 psi | Conditioned; ISO R 527 |
Addiplast Addilene J 490 M40S Flame Retardant Polypropylene, 40% Mineral Filled Flame retardant, mineral filled, with halogensInformation provided by Addiplast. |
|||
Tensile Strength at Break | 24.0 MPa | 3480 psi | |
Plastcom SLOVALEN PH 61 GB 30 PP, 30% glass beads, mod. of mech. prop. FeaturesModified homopolymer PP for injection moulding, chemically reinforced with 30% glass beads, contains the modifier of mechanical properties. Increased strength in comparison with unfilled PP... |
|||
Tensile Strength at Break | <= 24.0 MPa | <= 3480 psi | ISO/R527 |
Polykemi AB POLYfill PP 150ENH Polypropylene, Flame Retardant, Halogen Free Information provided by Polykemi AB |
|||
Tensile Strength at Break | <= 24.0 MPa | <= 3480 psi | ISO/R527 |
Polykemi AB POLYfill PPHC K8030 Polypropylene, Mineral Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | <= 24.0 MPa | <= 3480 psi | ISO/R527 |
Polykemi AB POLYfill PPHC K9030 Polypropylene, Mineral Reinforced Information provided by Polykemi AB |