Polymer Property : Tensile Strength at Break = 34.5 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength at Break 34.5 MPa
5000 psi
2 in/min; ASTM D638
RheTech Products P104-00 Polypropylene, Natural
Applications: Consumer goodsIP structural componentsInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break 34.5 MPa
5000 psi
ASTM D638
Polymer Resources PPX-GP4 Modified-PPO, General Purpose
Modified-Polyphenylene Oxide, General Purpose, 210F HDTProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Informati..
Tensile Strength at Break >= 34.5 MPa
>= 5000 psi
Cured
Resin Technology Group CT-523LV Cationic UV Cure Epoxy Adhesive
CT-523-LV is an epoxy-based, low viscosity, cationic-curable adhesive and/or sealant. This product is activated by exposure to medium intensity UV radiation resulting in a high strength, chemical re..
Tensile Strength at Break 34.5 MPa
5000 psi
TM R050-36
Resinlab® EP1320 Heat Cure Epoxy Conformal Coating
Resinlab™ EP1320 and EP1320LV are one part heat cure epoxy conformal coatings. They can also be used as a small mass potting compounds, structural adhesives, or insulating polymer systems where the..
Tensile Strength at Break >= 34.5 MPa
>= 5000 psi
Resin Technology Group TIGA HTR-815 High Temperature Resistant, Rigid Thermally Conductive Epoxy
100 parts resin to 28 parts hardener.TIGA HTR-815 is a low viscosity electronic bonding system designed to provide superior thermal shock resistance and high thermal conductivity. This product is an..
Tensile Strength at Break 34.5 MPa
5000 psi
ASTM D638
Albis Plastics Cellulose Acetate Propionate CP801 (UV Inhibitor Added), 13% Plasticizer  (discontinued **)
Amorphous Cellulose Acetate Propionate (CAP)Characteristics: Strength, Hardness, Stiffness, Weatherability and Dimensional StabilityApplications: Brush Handles, Safety Glasses, Optical Products and ..
Tensile Strength at Break 34.5 MPa
5000 psi
ASTM D638
Albis Plastics Cellulose Acetate Propionate CP808 (FDA), 13% Plasticizer  (discontinued **)
Amorphous Cellulose Acetate Propionate (CAP)Characteristics: Strength, Hardness, Stiffness, Weatherability and Dimensional StabilityApplications: Brush Handles, Safety Glasses, Optical Products and ..
Tensile Strength at Break >= 34.5 MPa

@Temperature 23.9 °C
>= 5000 psi

@Temperature 75.0 °F
Master Bond UV15LV One Component, UV Curable Epoxy Based System
Product Description: Master Bond UV15LV is a high strength, low viscosity, epoxy based UV curable system for bonding, sealing and coating. It has low viscosity and it is widely used in a variety of ..
Tensile Strength at Break 34.5 MPa
5000 psi
ASTM D638
Chase Plastics CP Pryme® NN100STL (COND, 50% RH) Nylon 66, Super Toughened, Internally Lubricated
Information provided by Chase Plastics.
Tensile Strength at Break 34.5 MPa
5000 psi
ASTM D 638
RTP Company RTP 299 A X 108950 B Nylon 6 (PA), High Gravity Compound
Tensile Strength at Break 34.5 MPa
5000 psi
2" (50mm) per min.; ASTM D638 Type IV
Formosa Plastics Formolene® HP4401 Pipe HDPE
High Density Hexene CopolymerApplications: Potable water, industrial mining, oil and gas gatheringsFormolene HP4401 is a high performance copolymer that is designed for the most demanding requiremen..
Tensile Strength at Break 34.5 MPa
5000 psi
vs. rigid PVC; 10 s set time
Elmer's Products Aron Alpha® 102 Cyanoacrylate Adhesive (Industrial Krazy Glue™)
Superior tensile and shear strengths, well suited for metal bondingMedium gap fill. Methyl base monomer. Excellent on rubber/plastic substrates. Excellent on metal substrates. Poor on porous sub..
Tensile Strength at Break 34.5 MPa
5000 psi
vs. polycarbonate; 20 s set time
Elmer's Products Aron Alpha® 201 Cyanoacrylate Adhesive (Industrial Krazy Glue™)
General purpose adhesive for a variety of applications. Various viscosities and gap filling properties available.Low gap fill. Ethyl base monomer. Excellent on rubber/plastic substrates. Fair on..
Tensile Strength at Break 34.5 MPa
5000 psi
vs. rigid PVC; 3 s set time
Elmer's Products Aron Alpha® 202F Cyanoacrylate Adhesive (Industrial Krazy Glue™)
Surface insensitive adhesives, ultra-fast setting for porous, soft or tough-to-bond substrates. Series 200TX & Gel: No run, no stringing, excellent gap filling characteristics with good strength on..
Tensile Strength at Break 34.5 MPa
5000 psi
vs. polycarbonate; 5 s set time
Elmer's Products Aron Alpha® 202F Cyanoacrylate Adhesive (Industrial Krazy Glue™)
Surface insensitive adhesives, ultra-fast setting for porous, soft or tough-to-bond substrates. Series 200TX & Gel: No run, no stringing, excellent gap filling characteristics with good strength on..
Tensile Strength at Break 34.5 MPa
5000 psi
vs. rigid PVC; 25 s set time
Elmer's Products Aron Alpha® 203 Cyanoacrylate Adhesive (Industrial Krazy Glue™)
General purpose adhesive for a variety of applications. Various viscosities and gap filling properties available.High gap fill. Ethyl base monomer. Excellent on rubber/plastic substrates. Fair o..
Tensile Strength at Break 34.5 MPa
5000 psi
vs. rigid PVC; 1 s set time
Elmer's Products Aron Alpha® 221F Cyanoacrylate Adhesive (Industrial Krazy Glue™)
Surface insensitive adhesives, ultra-fast setting for porous, soft or tough-to-bond substrates. Series 200TX & Gel: No run, no stringing, excellent gap filling characteristics with good strength on..
Tensile Strength at Break 34.5 MPa
5000 psi
vs. polycarbonate; 20 s set time
Elmer's Products Aron Alpha® 241F Cyanoacrylate Adhesive (Industrial Krazy Glue™)
Surface insensitive adhesives, ultra-fast setting for porous, soft or tough-to-bond substrates. Series 200TX & Gel: No run, no stringing, excellent gap filling characteristics with good strength on..
Tensile Strength at Break 34.5 MPa
5000 psi
vs. polycarbonate; 15 s set time
Elmer's Products Aron Alpha® 282F Cyanoacrylate Adhesive (Industrial Krazy Glue™)
Surface insensitive adhesives, ultra-fast setting for porous, soft or tough-to-bond substrates. Series 200TX & Gel: No run, no stringing, excellent gap filling characteristics with good strength on..
Tensile Strength at Break 34.5 MPa
5000 psi
vs. rigid PVC; 10 s set time
Elmer's Products Aron Alpha® 402X Cyanoacrylate Adhesive (Industrial Krazy Glue™)
Engineered for high temperature and high impact resistance.Medium gap fill. Ethyl base monomer. Excellent on rubber/plastic substrates. Excellent on metal substrates. Poor on porous substrates. ..
Tensile Strength at Break 34.5 MPa
5000 psi
vs. rigid PVC; 10 s set time
Elmer's Products Aron Alpha® 241 Cyanoacrylate Adhesive (Industrial Krazy Glue™)
General purpose adhesive for a variety of applications. Various viscosities and gap filling properties available.Low gap fill. Ethyl base monomer. Excellent on rubber/plastic substrates. Fair on..
Tensile Strength at Break 34.5 MPa
5000 psi
vs. polycarbonate; 10 s set time
Elmer's Products Aron Alpha® 252E Cyanoacrylate Adhesive (Industrial Krazy Glue™)
For clean, fast applications. Best for high speed automated assembly.High gap fill. Ethyl base monomer. Excellent on rubber/plastic substrates. Fair on metal substrates. Excellent on porous sub..
Tensile Strength at Break 34.5 - 48.3 MPa
5000 - 7000 psi
Abatron AboCast 7802-1/AboCure 50-3 (40 pbw) Epoxy
AboCast 7802-1 is a clear resin with low viscosity (600-800 cps.) and a weight of 9.1 lbs/gallon. AboCure 50-3 is a clear, slow converter for lower rigidity. It has an HDT of 60°C, variable ratio, ..
Tensile Strength at Break 34.5 MPa
5000 psi
ASTM D638
Celanese VANDAR 8000 PBT, Unfilled
Vandar 8000 polyester alloy is designed to meet UL94 V-0 requirements at 1/32 inch thickness while retaining excellent impact resistance. The product is characterized by excellent moldability and su..
Tensile Strength at Break 34.5 MPa
5000 psi
ASTM D638
Albis Plastics Cellulose Acetate Butyrate B902 (UV Inhibitor Added), 13% Plasticizer  (discontinued **)
Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and T..
Tensile Strength at Break 34.5 MPa
5000 psi
ASTM D638
Albis Plastics Cellulose Acetate Propionate CP808 (FDA), 12% Plasticizer  (discontinued **)
Amorphous Cellulose Acetate Propionate (CAP)Characteristics: Strength, Hardness, Stiffness, Weatherability and Dimensional StabilityApplications: Brush Handles, Safety Glasses, Optical Products and ..
Tensile Strength at Break 34.5 MPa
5000 psi
2" (50mm) per min, Type IV; ASTM D638
Formosa Plastics Formolene® HP4000 Pipe HDPE
High Density Hexene Copolymer Formolene® HP4000 is a high performance copolymer that is designed for the most demanding requirements of non pressure pipe applications. It has good long-term hoop st..
Tensile Strength at Break 34.5 MPa
5000 psi
ASTM D 412
RTP Company RTP 1200 S-90A TFE 15 Ester-based Thermoplastic Polyurethane Elastomer, PTFE Lubricated
Tensile Strength at Break 34.5 MPa
5000 psi
ASTM D 638
RTP Company RTP 3003 Polymethylpentene (PMP), Glass Fiber
Tensile Strength at Break >= 34.5 MPa
>= 5000 psi
Master Bond EP3HTSMed Silver Filled, Medical Grade Epoxy
Description: Master Bond EP3HTSMed is a one component, silver filled, electrically conductive epoxy system featuring high shear strength and good temperature resistance along with a fast cure schedu..