Polymer Property : Tensile Strength at Break = 3280 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	22.6 MPa	3280 psi	Type IV specimen, compression molded, crosshead speed 2 in/min; ASTM D638
DuPont Nucrel® 2806 Ethylene-Acrylic Acid Copolymer Resin (discontinued **) Nucrel® 2806 is a tough, lightweight, easily processed ethylene copolymer resin. This resin is inherently flexible without the need for plasticizers. The resin can be pigmented, UV-stabilized for..
Tensile Strength at Break	22.6 MPa @Thickness 2.00 mm	3280 psi @Thickness 0.0787 in	50mm/min; ASTM D638
LG Chemical KEYFLEX BT 3038D Ester Type TPE Description: Injection Molding, TPC-ET, Functional, Fast Molding, Low ModulusApplication: Automotive Interior, Soft Touch GripsCAS: 37282-12-5Information provided by LG Chemical
Tensile Strength at Break	22.6 MPa @Thickness 2.00 mm	3280 psi @Thickness 0.0787 in	50mm/min; ASTM D638
LG Chemical KEYFLEX BT 3055D Ester Type TPE Description: Injection Molding, TPC-ET, Functional, Fast Molding, Medium ModulusApplication: Injection Parts for Leisure & SportsCAS: 37282-12-5Information provided by LG Chemical
Tensile Strength at Break	22.6 MPa @Thickness 2.00 mm	3280 psi @Thickness 0.0787 in	50mm/min; ASTM D638
LG Chemical KEYFLEX BT GN7155F Ester Type TPE Description: Extrusion Molding, TPC-ET, Halogen Free Flame Retardant, Medium ModulusApplication: Cable & Wire Jackets, Hose & Tubing, SheetInformation provided by LG Chemical
Tensile Strength at Break	22.6 MPa	3280 psi
LG Chemical LGflex GL300 Plasticizer Features: Excellent Viscosity, Heat Stability and Non-endocrine disrupterApplication: PVC Calenderings/Leathers, Sheets, Gloves, HoseInformation provided by LG Chemical
Tensile Strength at Break	22.6 MPa @Temperature 145 Â°C, Time 2100 sec	3280 psi @Temperature 293 Â°F, Time 0.583 hour	ASTM D412
LG Chemical SBR 1778 High Acrylonitrile Polymer Description: SBR 1778 is an oil extended cold polymerization SBR with 37.5 parts of discoloring paraffinic/naphthenic oil and light colored high molecular weight styrene-butadiene copolymer of 23.5%..
Tensile Strength at Break	22.6 MPa	3280 psi	ASTM D638
Teknor Apex APEXÂ® 4304 Polyvinyl Chloride, Flexible Notes: RoHS Compliant Features: Flame Retardant Uses: Communication Wire Jacketing; Telephone Retractile Cord Jacketing Wire Types: SPT-1 Forms: PelletsInformation Provided by Teknor Apex
Tensile Strength at Break	22.6 MPa	3280 psi	50 mm/min; ASTM D638
Supreme Petrochem SP 554 Flame Retardant Polystyrene Characteristics Very good flow properties Good balance of toughness and rigidity Processing Molding Gas assist molding Applications Large size T.V. Cabinets VCR cabinets Electrical boxes, electr..
Tensile Strength at Break	22.6 MPa	3280 psi	ASTM D638
3M Scotchkote™ RS 820 Epoxy Screed Scotchkote Epoxy Sceed RS 820 has been specially developed as a three component 100% solids resurfacing screed for application to concrete floor surfacesProduct Features:Combines good application ch..
Tensile Strength at Break	22.6 MPa	3280 psi	ASTM D638
3M Scotchkote™ XF 895 Fast Curing Floor Coating Scotchkote Fast Curing Floor Coating XF 895 has been specifically developed as a high build floor protection system for application to concrete surfaces, to provide rapid return to serviceProduct Fe..