Polymer Property : Tensile Strength at Break = 3210 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	22.1 MPa	3210 psi	Type IV, 510 mm/min; ASTM D638
PolyOne Geon™ Vinyl Flexible R 980A Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne
Tensile Strength at Break	22.1 MPa	3210 psi	Type IV, 510 mm/min; ASTM D638
PolyOne Geon™ Vinyl Flexible XV3863 Polyvinyl Chloride, Flexible (PVC, Flexible) XV3863 is a flexible (95A durometer) vinyl compound formulated from FDA-santioned raw materials. XV3863 Clear 1859 has been tested to USP Class VI.NOTE: All ingredients used in the formulation of th..
Tensile Strength at Break	22.1 MPa	3210 psi	ASTM D638
DuPont Surlyn® 8945 Thermoplastic Ionomer Resin Surlyn® 8945 provides high flow properties and consistent, easy processing in molded and extruded applications. It is positioned in the medium/high acid, high neutralization area of the ionomer sp..
Tensile Strength at Break	22.1 MPa	3210 psi	500mm/min; ASTM D638
Westlake MC3016 High Density Polyethylene Coating Westlake MC3016 is a high density polyethylene designed for extrusion coating and lamination applications. MC3016 provides improved barrier properties, temperature resistance, stress crack resistanc..
Tensile Strength at Break	22.1 MPa	3210 psi	ASTM D882
3M Scotch-Weld™ DP805 Acrylic Adhesives 3M™ Scotch-Weld™ Acrylic Adhesive DP805 is a two-part, 1:1 mix ratio, toughened acrylic structural adhesives. They exhibit excellent shear and peel strengths along with good impact and durability ..
Tensile Strength at Break	22.1 MPa	3210 psi	ASTM D638 Die C
3M Scotch-Weld™ TE230 Black Polyurethane Reactive Adhesive 3M™ Scotch-Weld™ Polyurethane Reactive Adhesives are a family of one-component, moisture curing, urethane adhesives. These adhesives are applied warm and bond a wide variety of substrates such as ..
Tensile Strength at Break	22.1 MPa	3210 psi
Asahi Glass Fluon® PA1020Z 20% Glass Fiber, PTFE Filled Compound Fluon®PTFE FC has improved creep and wear resistance. A wide range of fillers such as glass fiber, graphite, bronze, carbon fiber are available. Information provided by Asahi Glass Company, Inc.
Tensile Strength at Break	22.1 MPa	3210 psi	ASTM D638 Die C
3M Scotch-Weld™ TS115 HGS Polyurethane Reactive Adhesive 3M™ Scotch-Weld™ Polyurethane Reactive Adhesives are a family of one-component, moisture curing, urethane adhesives. These adhesives are applied warm and bond a wide variety of substrates such as ..