Polymer Property : Tensile Strength at Break = 32.4 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	32.4 MPa	4700 psi	2 in/min; ASTM D638
RheTech Products M15P100-01A 15% Mica Reinforced Polypropylene, Black Applications: Fan shroudsAir ductsElectronicsInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break	32.4 MPa	4700 psi	2 in/min; ASTM D638
RheTech Products P107-00 Polypropylene Homopolymer, Natural Applications: Wire harnessesTrim componentsUnderhood componentsInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break	32.4 MPa	4700 psi	2 in/min; ASTM D638
RheTech Products T15P100-00 12% Talc Reinforced Polypropylene, Natural Applications: Component housingConsumer goodsInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break	32.4 MPa	4700 psi
Indium Corp. Indalloy 153 Tin-Lead Solder Alloy Information Provided by Indium Corporation
Tensile Strength at Break	32.4 MPa	4700 psi	5 mm/min; ASTM D638
Samsung Cheil Industries StarexÂ® HF-0690M ABS, Unreinforced Information provided by Samsung Cheil Industries.
Tensile Strength at Break	32.4 MPa	4700 psi	50 mm/min; ASTM D638
Samsung Cheil Industries StarexÂ® LX-0981 ABS, Unreinforced Metallic-Look Luminous Grade - gives aesthetics of a painted surface without painting. Reduces time, cost, and environmental hazards (such as soilvents).Information provided by Samsung Cheil Industries.
Tensile Strength at Break	32.4 MPa	4700 psi	5 mm/min; ASTM D638
Samsung Cheil Industries StarexÂ® SF-0505HWR MABS, Unreinforced Scratch Resistant Information provided by Samsung Cheil Industries.
Tensile Strength at Break	32.4 MPa	4700 psi	5 mm/min; ASTM D638
Samsung Cheil Industries StarexÂ® SR-0315 V ABS, Unreinforced Heat Resistant Information provided by Samsung Cheil Industries.
Tensile Strength at Break	32.4 MPa	4700 psi	5 mm/min; ASTM D638
Samsung Cheil Industries StarexÂ® HF-0690M ABS, Unreinforced Information provided by Samsung Cheil Industries.
Tensile Strength at Break	32.4 MPa	4700 psi	50 mm/min; ASTM D638
Samsung Cheil Industries StarexÂ® LX-0981 ABS, Unreinforced Metallic-Look Luminous Grade - gives aesthetics of a painted surface without painting. Reduces time, cost, and environmental hazards (such as soilvents).Information provided by Samsung Cheil Industries.
Tensile Strength at Break	32.4 MPa	4700 psi	5 mm/min; ASTM D638
Samsung Cheil Industries StarexÂ® SF-0505HWR MABS, Unreinforced Scratch Resistant Information provided by Samsung Cheil Industries.
Tensile Strength at Break	32.4 MPa	4700 psi	5 mm/min; ASTM D638
Samsung Cheil Industries StarexÂ® SR-0315 V ABS, Unreinforced Heat Resistant Information provided by Samsung Cheil Industries.
Tensile Strength at Break	32.4 MPa	4700 psi	ASTM D638
Chase Plastics CP Pryme® NN300STL (COND, 50% RH) Nylon 66 (Utility Grade), Super Toughened, Internally Lubricated Information provided by Chase Plastics.
Tensile Strength at Break	32.4 MPa @Temperature 22.8 °C	4700 psi @Temperature 73.0 °F	ASTM D638
Ensinger TECAFINE™ PP Polypropylene (PP) TECAFINE™ PP is an anti-stated, polypropylene, random copolymer polyolefin engineering plastic providing excellent chemical resistance and high purity. FDA compliant with better mechanical propert..
Tensile Strength at Break	32.4 MPa	4700 psi	vs. steel; 90 s set time
Elmer's Products Aron Alpha® 403T Cyanoacrylate Adhesive (Industrial Krazy Glue™) Extra tough adhesives with highest heat, peeling, impact and thermal shock resistance.High gap fill. Ethyl base monomer. Excellent on rubber/plastic substrates. Excellent on metal substrates. Fa..
Tensile Strength at Break	32.4 MPa	4700 psi	ASTM D638
Plastics Group Polifil® T-30 30% Talc-Reinforced Polypropylene Polifil® T series compounds are homopolymer polypropylene resins reinforced with asbestos-free talc. They possess high flex modulus, high deflection temperature, good chemical resistance and colora..
Tensile Strength at Break	32.4 MPa	4700 psi	2 in/min; ASTM D638
RheTech Products HP501-01 High Performance Polypropylene Copolymer, Non-UV Stabilized, Black Applications: Battery traysInterior TrimInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break	32.4 MPa	4700 psi	ASTM D638
PlastxWorld CEVIAN® A1300 PA/ABS Alloy, Conditioned Property data is for samples at equilibrium moisture (2.0%)Information provided by PlastxWorld Inc.
Tensile Strength at Break	32.4 MPa @Thickness 2.00 mm	4700 psi @Thickness 0.0787 in	50mm/min; ASTM D638
LG Chemical KEYFLEX BT S5035 Ester Type TPE Description: Injection Molding, TPC-ET, Airbag Cover Deployment, Medium Modulus, Black ColorApplication: Airbag Cover (DAB, PAB, KAB, SAB)CAS: 37282-12-5, 24968-12-5 and 1333-86-4Information provide..
Tensile Strength at Break	32.4 MPa	4700 psi	ASTM D638
Chase Plastics CP Pryme® PPH100-18M Polypropylene Homopolymer, 18 Melt Flow Information provided by Chase Plastics.
Tensile Strength at Break	32.4 MPa	4700 psi	2 in/min; ASTM D638
RheTech Products HP501-00 High Performance Polypropylene Copolymer, Non-UV Stabilized, Natural Applications: Battery traysInterior TrimInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break	32.4 MPa	4700 psi	2 in/min; ASTM D638
RheTech Products M20P100-01A 20% Mica Reinforced Polypropylene, Black Applications: Fan shroudsFiller panelsAir ductsInjection molding conditions reported in table.Information provided by RheTech Products.