Polymer Property : Tensile Strength at Break = 30600 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength at Break 211 MPa
30600 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP RCL34 PA 66
LNP* LUBRICOMP* RCL34 is a compound based on Nylon 66 containing 20% Carbon Fiber, 15% PTFE. Added features of this grade includes: Wear Resistant, Electrically Conductive.
Tensile Strength at Break 211 MPa
30600 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP STAT-KON EX11318C PEI (Asia Pacific)
LNP* Stat-Kon* EX11318C is a polyetherimide compound reinforced with carbon fiber for good stiffness, dimension stability and has extremely high level of cleanliness for the most demanding applicati..
Tensile Strength at Break 211 MPa
30600 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP RF009S PA 66
LNP* THERMOCOMP* RF009S is a compound based on Nylon 66 resin containing 45% Glass Fiber. Added features of this material include: Heat Stabilized.
Tensile Strength at Break 211 MPa

@Temperature -40.0 °C
30600 psi

@Temperature -40.0 °F
ISO Data
BASF Petra® 130 BK-112 30% Glass Filled PET
Petra 130 BK-112 is a 30% glass fiber reinforced, black pigmented polyethylene terephthalate injection molding compound. It exhibits a combination of performance properties including good strength ..
Tensile Strength at Break 211 MPa
30600 psi
Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics LNP Verton RX93407D PA 66
LNP* Verton* RX93407D is a compound based on Nylon 66 resin.This data was supplied by SABIC-IP for the Americas region.