Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 3.20 MPa | 464 psi | ISO 37 |
PolyOne OnFlex™ S KG 50A-3S2017 Thermoplastic Elastomer (TPE) OnFlex™-S KG thermoplastic elastomer compounds are based on hydrogenated styrenic block copolymers. This range of compounds are specially compatabilized to provide excellent adhesion to polyamide p.. |
|||
Tensile Strength at Break | 3.20 MPa | 464 psi | ASTM-F152 |
GrafTech eGRAF® HITHERM™ HT-1210 Graphite Made from natural graphite, eGRAF® HITHERM™ thermal interface materials are designed for use in applications requiring low contact resistance and high thermal conductivity. HITHERM™ mat.. |
|||
Tensile Strength at Break | 3.20 MPa | 464 psi | ASTM-F152 |
GrafTech eGRAF® HITHERM™ HT-1220 Graphite Made from natural graphite, eGRAF® HITHERM™ thermal interface materials are designed for use in applications requiring low contact resistance and high thermal conductivity. HITHERM™ mat.. |
|||
Tensile Strength at Break | 3.20 MPa | 464 psi | chs 2.0 in/min; ASTM D638 |
Diamond Polymers Softflex® SF 5591 Thermoplastic Vulcanizate (TPV) Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
Tensile Strength at Break | >= 3.20 MPa | >= 464 psi | ISO 527 |
Fainplast Compounds EVAtech 801S Ethylene Vinyl Acetate Foam EVA (ethylene-vinyl acetate) designed for the production of crosslinked expanded products using injection technology.Information provided by Fainplast Compounds |