Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 28.4 MPa | 4120 psi | 2 in/min; ASTM D638 |
RheTech Products FT4600-00 Thermoplastic Polyolefin, Non-UV Stabilized, Natural Applications: Scuff platesInterior trimI/P componentsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 28.4 MPa | 4120 psi | 2 in/min; ASTM D638 |
RheTech Products FT4600-152 Thermoplastic Polyolefin, UV Stabilized, JA6A Black Applications: Scuff platesInterior trimI/P componentsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 28.4 MPa @Temperature 145 °C, Time 2100 sec |
4120 psi @Temperature 293 °F, Time 0.583 hour |
ASTM D412 |
LG Chemical SBR 1500 High Acrylonitrile Polymer Description: NSBR 1500 is a cold polymerized styrene-butadiene copolymer with staining stabilizer. The cold polymerized SBR exhibits better abrasion, higher tensile strength and higher modulus than .. |
|||
Tensile Strength at Break | 28.4 MPa @Temperature 145 °C, Time 2100 sec |
4120 psi @Temperature 293 °F, Time 0.583 hour |
ASTM D412 |
LG Chemical SBR 1500H High Acrylonitrile Polymer Description: SBR 1500H is a cold polymerized styrene-butadiene copolymer with non-staining stabilizer and especially well-suited for adhesive applications. It has high internal strength, and excelle.. |
|||
Tensile Strength at Break | 28.4 MPa @Temperature 145 °C, Time 2100 sec |
4120 psi @Temperature 293 °F, Time 0.583 hour |
ASTM D412 |
LG Chemical SBR 1723 High Acrylonitrile Polymer Description: SBR 1723 is an oil extended cold polymerization SBR with 37.5 parts of Low PCA (PolyCyclic Aromatic) oil and styrene-butadiene copolymer of 23.5% bound styrene. Raw materials for this p.. |
|||
Tensile Strength at Break | >= 28.4 MPa | >= 4120 psi | |
Sibur SKI-3 1st Grade, 2nd Group Isoprene Rubber (IR) Nipol-IR 2200, Natsyn-2200, Kraton-IR 401. For production of tires and rubber technical articles of wide assortment. |
|||
Tensile Strength at Break | >= 28.4 MPa | >= 4120 psi | |
Sibur SKI-3 1st Grade, 3rd Group Isoprene Rubber (IR) Nipol-IR 2200, Natsyn-2200, Kraton-IR 401. For production of tires and rubber technical articles of wide assortment. |
|||
Tensile Strength at Break | 28.4 MPa | 4120 psi | 5 mm/min; ASTM D638 |
Samsung Cheil Industries Starex® VE-0852 ABS, Unreinforced FR Information provided by Samsung Cheil Industries. |
|||
Tensile Strength at Break | 28.4 MPa @Treatment Temp. 145 °C, Time 2100 sec |
4120 psi @Treatment Temp. 293 °F, Time 0.583 hour |
Cure; ASTM D412 |
Styron Buna® SB 1502 Schkopau Cold Polymerized Emulsion Styrene Butadiene Rubber (E-SBR) Composition: Buna® SB 1502 – Schkopau is manufactured by cold polymerization using mixed rosin acid /fatty acid soaps. A non-discoloring stabilizer is added during the production process.App.. |
|||
Tensile Strength at Break | 28.4 MPa | 4120 psi | 5 mm/min; ASTM D638 |
Samsung Cheil Industries Starex® VE-0852 ABS, Unreinforced FR Information provided by Samsung Cheil Industries. |
|||
Tensile Strength at Break | 28.4 MPa | 4120 psi | 50 mm/min; ASTM D638 |
Supreme Petrochem SH 400 M High Impact Polystyrene Characteristics High gloss Easy flow Processing MoldingApplications Air conditioner and cooler grills, refrigerator components Toys, use and throw camera, household articles Ball pen barrels, nov.. |
|||
Tensile Strength at Break | 28.4 MPa | 4120 psi | 50 mm/min; ASTM D638 |
Supreme Petrochem SH 731 High Impact Polystyrene Characteristics Medium flow High Impact Excellent formability Low temperature toughnessProcessing Extrusion Molding FormingApplications Thermoformed containers, extruded profiles, packaging pro.. |
|||
Tensile Strength at Break | 28.4 MPa | 4120 psi | 50 mm/min; ASTM D638 |
Supreme Petrochem SP 562 Flame Retardant Polystyrene Characteristics Very good flow properties Free of DBDPO, PBDE & TBBA, complies with ROHS directive of EU Low specific gravity Processing Injection moldingApplications Large size T.V. Cabinets Aud.. |