Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 192 MPa | 27800 psi | ISO 527 |
SABIC Innovative Plastics LNP Lubricomp RFN18SXZ PA 66 LNP LUBRICOMP* RFN18SXZ is a compound based on Nylon 66 resin containing Glass Fiber, MOS2. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP for the Ameri.. |
|||
Tensile Strength at Break | 192 MPa | 27800 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP UFL36AS PPA LNP* LUBRICOMP* UFL36AS is a Polyphthalamide (PPA) base resin containing 30% Glass Fiber, 15% PTFE. Added features of this material are: Heat Stabilized, Wear Resistant. |
|||
Tensile Strength at Break | 192 MPa | 27800 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics LNP Thermocomp OC008A PPS - Branched LNP* Thermocomp* OC008A is a compound based on Branched Polyphenylene Sulfide containing Carbon Fiber.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 192 MPa | 27800 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP PF009 PA 6 LNP THERMOCOMP* PF009 is a compound based on Nylon 6 resin containing 45% Glass Fiber. |
|||
Tensile Strength at Break | 192 MPa | 27800 psi | ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP UFW49S PPA LNP* THERMOCOMP* UFW49S is a compound based on Polyphthalamide resin containing 45% Glass Fiber, 20% Wollastonite. Added features of this material include: Heat Stabilized, Low Warpage. |
|||
Tensile Strength at Break | 192 MPa | 27800 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP UX93847 PPA (Asia Pacific) LNP* Thermocomp* UX93847 is a compound based on Polyphthalamide resin containing Proprietary Filler(s). |
|||
Tensile Strength at Break | 192 MPa | 27800 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP QFL17RS PA 6/10 LNP LUBRICOMP* QFL17RS is a compound based on Nylon 6/10 resin containing 35% Glass Fiber, 5% PTFE. Added features of this material include: Easy Release, Heat Stabilized, Wear Resistant. |
|||
Tensile Strength at Break | 192 MPa | 27800 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON OE006C1 PPS - Linear LNP* STAT-KON* OE006C1 is a compound based on PPS - Linear resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
Tensile Strength at Break | 192 MPa | 27800 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP PF009 PA 6 (Asia Pacific) LNP THERMOCOMP* PF009 is a compound based on Nylon 6 resin containing Glass Fiber. |
|||
Tensile Strength at Break | 192 MPa | 27800 psi | ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP UFW49S PPA (Asia Pacific) LNP* Thermocomp* UFW49S is a compound based on Polyphthalamide resin containing Glass Fiber, Mineral. Added features of this material include: Heat Stabilized, Low Warpage. |
|||
Tensile Strength at Break | 192 MPa | 27800 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP UX93847 PPA LNP* Thermocomp* UX93847 is a compound based on Polyphthalamide resin containing Proprietary Filler(s). |
|||
Tensile Strength at Break | 192 MPa | 27800 psi | ASTM D638 |
LNP Lubricomp® QFL-4017 ER HS Polyamide 6/10 Copolymer, Glass Fiber Reinforcement, PTFE Lubricant
(discontinu Features: Heat Stabilized, Good Mold Release, LubricatedForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; .. |
|||
Tensile Strength at Break | 192 MPa | 27800 psi | ISO 527-1, -2 |
LNP Thermocomp® UFM-3249 HS BK8-115 Polyphthalamide, Glass Mineral Reinforcement
(discontinued **) Features: Heat StabilizedForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are sti.. |
|||
Tensile Strength at Break | 192 MPa | 27800 psi | ISO 527-1/-2 |
Lanxess Durethan® DP AKV 35 LT H2.0 904040 Nylon 66, 35% Glass Fiber PA 66, injection molding grade, 35% glass fibers, black colored for laser transmission- welding (laser-transparent), good heat-ageing resistance |