Polymer Property : Tensile Strength at Break = 254 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength at Break 254 MPa
36800 psi
ASTM D638
SABIC Innovative Plastics LNP VERTON RV00AES PA 66 (Asia Pacific)
LNP VERTON* RV00AES is a compound based on Nylon 66 resin containing Long Glass. Added features of this material include: Easy Molding.
Tensile Strength at Break 254 MPa
36800 psi
ASTM D638
SABIC Innovative Plastics LNP VERTON RV00AES PA 66 (Europe-Africa-Middle East)
LNP VERTON* RV00AES is a compound based on PA 66 resin containing Long Glass Fiber. Added features of this material include: Easy Molding, Heat Stabilized.
Tensile Strength at Break 254 MPa
36800 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP VERTON RV00AESC PA 66 (Europe-Africa-Middle East)
LNP* VERTON* RV00AESC is a compound based on PA 66 resin containing Long Glass Fiber. Added features include; Easy Molding, Heat Stabilized.
Tensile Strength at Break 254 MPa
36800 psi
ASTM D3759
3M 5153 PTFE Glass Cloth Tape
3M™ PTFE Glass Cloth Tape 5151 is constructed using (PTFE) polytetra-fluoroethylene impregnated glass cloth and silicone adhesive. This tape is used in many applications requiring high temperature ..
Tensile Strength at Break 254 MPa
36800 psi
ASTM D638
SABIC Innovative Plastics LNP VERTON RV00AES PA 66
LNP VERTON* RV00AES is a compound based on Nylon 66 resin containing 50% Long Glass Fiber. Added features of this material include: Easy Molding, Heat Stabilized, Structural.
Tensile Strength at Break 254 MPa
36800 psi
ASTM D638
SABIC Innovative Plastics LNP VERTON RX06422 PA 66
LNP VERTON* RX06422 is a compound based on Nylon 66 resin containing 50% Long Glass Fiber. Added features of this material include: Easy Molding, Heat Stabilized, UV Stabilized, Structural.
Tensile Strength at Break 254 MPa
36800 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP VERTON RV00CEXS PA 66
LNP* VERTON* RV00CEXS is a compound based on Nylon 66 resin containing 60% Long Glass Fiber. Added features of this grade include: Easy Molding, Structural.
Tensile Strength at Break 254 MPa
36800 psi
ASTM D638
SABIC Innovative Plastics LNP VERTON RX06422 PA 66 (Asia Pacific)
LNP VERTON* RX06422 is a compound based on Nylon 66 resin containing Long Glass. Added features of this material include: Easy Molding.