Polymer Property : Tensile Strength at Break = 24800 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength at Break 171 MPa
24800 psi
5 mm/min; ISO 527
SABIC Innovative Plastics ULTEM SF2350 PEI Blend
High flow Ultem blends for thin wall application
Tensile Strength at Break 171 MPa
24800 psi
5 mm/min; ISO 527
SABIC Innovative Plastics ULTEM SF2350 PEI Blend (Asia Pacific)
High flow Ultem blends for thin wall application
Tensile Strength at Break 171 MPa
24800 psi
5 mm/min; ISO 527
SABIC Innovative Plastics Ultem SF2350 PEI Blend (Europe-Africa-Middle East)
High flow Ultem blends for thin wall applicationThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Tensile Strength at Break 171 MPa
24800 psi
ASTM D638
SABIC Innovative Plastics LNP STAT-KON RX05489 PA 66 (Asia Pacific)
LNP* STAT-KON* RX05489 is a compound based on Nylon 66 resin containing PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive, Internally Lubricated.
Tensile Strength at Break 171 MPa
24800 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP QF008 PA 6/10 (Asia Pacific)
LNP* Thermocomp* QF008 is a compound based on Nylon 6/10 resin containing Glass Fiber.
Tensile Strength at Break 171 MPa
24800 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP QF008 PA6.10
LNP* THERMOCOMP* QF008 is a compound based on Nylon 6/10 resin containing 40% Glass Fiber.
Tensile Strength at Break 171 MPa
24800 psi
Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics LNP Thermocomp QF008R PA 6/10
LNP* Thermocomp* QF008R is a compound based on Nylon 6/10 containing Glass Fiber. Characteristics of this grade are: Easy Release.This data was supplied by SABIC-IP for the Americas region.
Tensile Strength at Break 171 MPa
24800 psi
ASTM D 638
SABIC Innovative Plastics LNP Thermocomp QF008S PA 6/10
LNP* Thermocomp* QF008S is a compound based on Nylon 6/10 resin containing Glass Fiber. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP for the Americas ..
Tensile Strength at Break 171 MPa
24800 psi
ASTM D638
SABIC Innovative Plastics LNP VERTON RV008E PA 66
LNP* VERTON* RV008E is a compound based on Nylon 66 resin containing 40% Long Glass Fiber. Added features of this material include: Easy Molding, Structural.
Tensile Strength at Break 171 MPa
24800 psi
ASTM D638
SABIC Innovative Plastics LNP VERTON RV008E PA 66 (Asia Pacific)
LNP* VERTON* RV008E is a compound based on Nylon 66 resin containing Long Glass Fiber. Added features of this material include: Easy Molding.
Tensile Strength at Break 171 MPa
24800 psi
ASTM D638
Unitika RUN35-C25 Weather resistant PA6, Dry
Weather resistant, noncoating, external exposure-compatibleInformation provided by Unitika Ltd.
Tensile Strength at Break 171 MPa
24800 psi
Type I, 5.1 mm/min; ASTM D638
PolyOne Nymax™ GF 1800 43 Natural Nylon 612 with 43% Glass Fiber  (discontinued **)
Molded Test Bars: Dry as Molded
Tensile Strength at Break 171 MPa
24800 psi
ASTM D 638
SABIC Innovative Plastics LNP Thermocomp QF008S PA 6/10 (Asia Pacific)
LNP* Thermocomp* QF008S is a compound based on Nylon 6/10 resin containing Glass Fiber. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP for the Asia Paci..