Polymer Property : Tensile Strength at Break = 23.5 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	23.5 MPa	3410 psi	50 mm/min; ISO 527
Polimeri Europa Edistir ICE R 830D Polystyrene Environmental stress cracking resistant (ESCR) HIPS. ICE PD R 830D combines high impact strength with an improved chemical resistance to oils, fats and chemical agents, such as detergents for both i..
Tensile Strength at Break	23.5 MPa @Thickness 2.00 mm	3410 psi @Thickness 0.0787 in	50mm/min; ASTM D638
LG Chemical KEYFLEX BT 1033D Ester Type TPE Description: Injection Molding, TPC-ET, General Purpose, Low ModulusApplication: Automotive Interior, Soft Touch GripsCAS: 37282-12-5Information provided by LG Chemical
Tensile Strength at Break	23.5 MPa @Temperature 145 Â°C, Time 2100 sec	3410 psi @Temperature 293 Â°F, Time 0.583 hour	ASTM D412
LG Chemical SBR 1721 High Acrylonitrile Polymer Description: SBR 1721 is an oil extended cold polymerization SBR with 37.5 parts of highly aromatic oil and styrene-butadiene copolymer of 40% bound styrene. Raw materials for this product are car..
Tensile Strength at Break	23.5 MPa	3410 psi
JPJ Technologies 530B HDPE Blow Molding Information provided by JPJ Technologies
Tensile Strength at Break	>= 23.5 MPa	>= 3410 psi
Sibur Nitrilast-26M Nitrile-Butadiene Rubber (NBR) 2845 N 28.60. For production of oil-benzene resistant articles for the automobile, aviation and rubber technical industries. Rubbers on the base of Nitrilast possess good oil-benzene resistance. ..
Tensile Strength at Break	>= 23.5 MPa	>= 3410 psi
Sibur Nitrilast-33M Nitrile-Butadiene Rubber (NBR) BYLT M-50 DN 202. For production of oil-benzene resistant articles for the automobile, aviation and rubber technical industries. Rubbers on the base of Nitrilast possess good oil-benzene resistanc..
Tensile Strength at Break	23.5 MPa	3410 psi	ISO R 527
Stir SpA SL 48 D K (PVC) Application: Extrusion for mesh coverInformation provided by STIR SpA
Tensile Strength at Break	>= 23.5 MPa	>= 3410 psi
Sibur SKN-26ASME Nitrile-Butadiene Rubber (NBR) For production of rubber and asbestos technical articles which are used as sets for automobile, air planes, different machines and equipment, agricultural, drilling, and polygraph machinery, as well..
Tensile Strength at Break	>= 23.5 MPa	>= 3410 psi
Sibur SKS-30 ARKM-15 1st Group Oil-Filled Styrene-Butadiene Rubber SBR 1705. For use in the tire industry for production of tire thread and other parts for tires, in the rubber technical industry for production of a wide assortment of rubber technical articles, an..
Tensile Strength at Break	23.5 MPa	3410 psi	50 mm/min; ASTM D638
Supreme Petrochem SH 825 High Impact Polystyrene Characteristics Good flow properties Very good stiffness High heat grade Processing MoldingApplications Home appliances, lamp shades, wall clocks Gift sets, picnic boxes Air cooler, watch casesM..
Tensile Strength at Break	23.5 MPa	3410 psi	ASTM D638
3M Scotchkote™ 162PWX Epoxy Coating 3M Scotchkote Epoxy Coating 162PWX is a 100% solid two-part epoxy coating that has been specifically developed for the long term protection of drinking water pipelines, storage and process tanks or ..