Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 23.4 MPa | 3390 psi | Type IV, 51 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Wire & Cable W84592L Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne |
|||
Tensile Strength at Break | 23.4 MPa | 3400 psi | 2 in/min; ASTM D638 |
RheTech Products HP513-00 High Performance Polypropylene Copolymer, Non-UV Stabilized, Natural Applications: Interior trimI/P componentsCenter consolesInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 23.4 MPa | 3400 psi | 2 in/min; ASTM D638 |
RheTech Products M12P250-01 12% Mica Reinforced Polypropylene Copolymer, Black Applications: Filler panelsHVAC ductsFan shroudsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 23.4 MPa | 3400 psi | 2 in/min; ASTM D638 |
RheTech Products P252-00 Polypropylene Copolymer, Natural Applications: Interior trimUnderhood componentsElectrical housingsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 23.4 MPa | 3390 psi | Type I, 51 mm/min; ASTM D638 |
PolyOne Trilliant™ HC X THC 1101 Natural Copolyester Trilliant™ HC high performance blends offer outstanding strength, durability and chemical resistance through the combination of Eastman Tritan™ copolyester with other various polymeric resins. Tri.. |
|||
Tensile Strength at Break | 23.4 MPa | 3400 psi | chs 2 in/min; ASTM D638 |
Network Polymers NPP 50-4052 Description: High Density Polyethylene (HDPE)Information provided by Network Polymers Inc. |
|||
Tensile Strength at Break | 23.4 MPa | 3390 psi | Type I, 51 mm/min; ASTM D638 |
PolyOne Edgetek® XT X XT 1001 Natural Copolyester Edgetek™ XT high performance blends offer outstanding strength, durability and chemical resistance through the combination of Eastman Tritan™ copolyester with other various polymeric resins. Edget.. |
|||
Tensile Strength at Break | 23.4 MPa | 3390 psi | ASTM D638 |
Resirene Resirene® 2270 High Impact Polystyrene Features:Medium FlowGood GlossFDA Rating: 21 CFR 177.1640High ProductivityApplications:Extrusion/ ThermoformingInjectionDiskettesPen BarrelsInformation provided by US distributor Calsak Corporation... |
|||
Tensile Strength at Break | 23.4 MPa | 3400 psi | 2 in/min; ASTM D638 |
RheTech Products HP511-00 27% Talc Reinforced Polypropylene Copolymer, High Performance, Non-UV Stabilized, Natural Applications: Interior trimCenter consolesI/P componentsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 23.4 MPa | 3400 psi | 2 in/min; ASTM D638 |
RheTech Products HP512-00 High Performance Polypropylene Copolymer, Non-UV Stabilized, Natural Applications: Interior trimI/P componentsCenter consolesInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 23.4 MPa | 3400 psi | 2 in/min; ASTM D638 |
RheTech Products M12P256-01 12% Mica Reinforced Polypropylene Copolymer, Black Applications: Air damsAir ducts - distributionClose out panelsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 23.4 MPa | 3390 psi | ASTM D4894 |
3M Dyneon™ CC174-N PTFE, 15% Fiberglass/Moly Filled
(discontinued **) Product Form: Gray, non-pelletized powder. Applications include bearings, rider rings, and packings.Data provided by Dyneon. |
|||
Tensile Strength at Break | 23.4 MPa | 3400 psi | ASTM D4745 |
3M Dyneon™ CC174/N Custom Fluoropolymer Compound
(discontinued **) This compound consists of a mixture of 15% fiberglass & 5% natural molybdenum disulfide blended with PTFE.Information provided by Dyneon, A 3M Company |
|||
Tensile Strength at Break | 23.4 MPa | 3400 psi | ASTM D638 |
Ineos N00N-00 Polypropylene Impact Copolymer Grade N00N-00 is a fractional melt flow rate, high impact copolymer polypropylene specifically designed for non-pressure structured wall pipe but can also be used in other extrusion applications req.. |
|||
Tensile Strength at Break | 23.4 MPa | 3400 psi | ASTM D638 |
Teknor Apex APEX® 3601-95 Polyvinyl Chloride, Flexible Uses: Medical/Healthcare Applications Agency Ratings: NSF 61 Forms: Pellets Additional Information: Second Generation SeriesInformation Provided by Teknor Apex |
|||
Tensile Strength at Break | 23.4 MPa | 3400 psi | ASTM D638 |
Teknor Apex APEX® 3611-90 Polyvinyl Chloride, Flexible Uses: Medical/Healthcare Applications Agency Ratings: NSF 61 Forms: Pellets Additional Information: Second Generation SeriesInformation Provided by Teknor Apex |
|||
Tensile Strength at Break | 23.4 MPa | 3400 psi | ASTM D638 |
Teknor Apex APEX® 60001-L Polyvinyl Chloride, Flexible Notes: RoHS Compliant Uses: Wire and Cable Applications Forms: PelletsInformation Provided by Teknor Apex |
|||
Tensile Strength at Break | 23.4 MPa | 3400 psi | ASTM D412 |
Teknor Apex Monprene® MP-1885-L3 Thermoplastic Elastomer Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Fo.. |
|||
Tensile Strength at Break | 23.4 MPa | 3400 psi | ASTM D412 |
Teknor Apex Monprene® MP-1885UV Thermoplastic Elastomer Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Fo.. |
|||
Tensile Strength at Break | 23.4 MPa | 3400 psi | ASTM D638 |
Teknor Apex APEX® 80459 Polyvinyl Chloride, Flexible Notes: 105°C Jacket; RoHS Compliant Uses: Wire and Cable ApplicationsForms: PelletsInformation Provided by Teknor Apex |
|||
Tensile Strength at Break | 23.4 MPa | 3400 psi | ASTM D638 |
Plastics Group Polifil® C-40 40% Calcium Carbonate-Reinforced Polypropylene Polifil® C series compounds are homopolymer polypropylene resins reinforced with fine particle size calcium carbonate. They combine high impact with stiffness, heat aging, good colorability, resist.. |
|||
Tensile Strength at Break | 23.4 MPa | 3400 psi | ASTM D638 |
Chesterton ARC 855 Abrasion Control Liquid Description: An advanced ceramic composite formulated to protect equipment from aggressive chemical attack, corrosion, and erosion. The product is a low viscosity composite that is easily applied by.. |
|||
Tensile Strength at Break | 23.4 MPa | 3400 psi | ASTM D638 |
Chesterton ARC S1 General purpose coating Description: An advanced polymer composite formulated to protect metal surfaces from corrosion and chmical attack. It is normally applied at a thickness of 250 microns (10 mils) per coat. Non-shrink.. |
|||
Tensile Strength at Break | 23.4 MPa | 3390 psi | chs 2.0 in/min; ASTM D638 |
Diamond Polymers Centrex® 601 Profile Extrusion Grade AES Centrex 601 resin is a very high-impact, low-gloss AES (acrylonitrile-ethylene-propylene-styrene) resin with good resistance to weather aging. It has good melt strength for profile extrusion and can.. |
|||
Tensile Strength at Break | 23.4 MPa | 3390 psi | chs 0.2 in/min; ASTM D638 |
Diamond Polymers Centrex® 835 Sheet Extrusion Grade Centrex 835 resin is a low-gloss grade of ASA (acrylonitrile-styrene-acrylate) with good resistance to weather aging. It has good melt strength for extrusion and thermoforming applications. Centrex .. |
|||
Tensile Strength at Break | 23.4 MPa @Temperature 23.0 °C |
3390 psi @Temperature 73.4 °F |
ASTM D638, ISO 527-2 |
DuPont™ Surlyn® 6320 Magnesium Ionomer Surlyn® 6320 is a magnesium ionomer thermoplastic resin. It is available for use in conventional extrusion and injection equipment, to create various sheets or shapes. Surlyn® 6320 thermoplastic r.. |
|||
Tensile Strength at Break | 23.4 MPa | 3390 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Syncure™ S1075A Polyethylene, Crosslinked (XLPE) Moisture Crosslinkable Polyethylene Compound. Available as Base Resin component for PolyOne Syncure System.Tensile, Elongation, Deformation, Hot Creep, and Gel measured on a 95 phr S1074A / 5 phr S1.. |