Polymer Property : Tensile Strength at Break = 206 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength at Break 206 MPa
29900 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP RX05491 PA 66
LNP* Thermocomp* RX05491 is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: Heat Stabilized.
Tensile Strength at Break 206 MPa
29900 psi
ISO 527
SABIC Innovative Plastics LNP VERTON RV008ES PA 66
LNP* VERTON* RV008ES is a compound based on Nylon 66 resin containing 40% Long Glass Fiber. Added features of this material include: Easy Molding, Heat Stabilized, Structural.
Tensile Strength at Break 206 MPa
29900 psi
ISO 527
SABIC Innovative Plastics LNP VERTON RV008ES PA 66 (Asia Pacific)
LNP* Verton* RV008ES is a compound based on Nylon 66 resin containing Long Glass Fiber. Added features of this material include: Easy Molding, Heat Stabilized.
Tensile Strength at Break 206 MPa
29900 psi
ASTM D638
SABIC Innovative Plastics LNP VERTON RVL28 PA 66 (Asia Pacific)
LNP VERTON* RVL28 is a compound based on Nylon 66 resin containing Long Glass Fiber, PTFE. Added features of this material include: Easy Molding.
Tensile Strength at Break 206 MPa
29900 psi
ISO 527-2
Ascend Performance Materials VYDYNE® R533H Nylon, 33% Glass Reinforced, DAM
Vydyne® R533H is 33% glass-fiber reinforced, heat-stabilized PA66 resin. Available in natural, it is specifically designed to maximize the retention of physical properties when exposed to anti-free..
Tensile Strength at Break 206 MPa
29900 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP VERTON RX00327 PA 66
LNP* VERTON* RX00327 is a compound based on Nylon 66 resin containing proprietary fillers. Added feature of this material is: Structural.